Method for manufacturing optical film

Patent metadata

Field	Value
Publication number	US-9931797-B2
Application number	US-201415108158-A
Country	US
Kind code	B2
Filing date	Dec 22, 2014
Priority date	Dec 24, 2013
Publication date	Apr 3, 2018
Grant date	Apr 3, 2018

Abstract

A method for manufacturing an optical film includes molding a sheet-shaped rubber-containing thermoplastic resin composition discharged in a molten state from a die outlet of an extruder by inserting the composition between a pair of smoothing rollers including an elastic roller, wherein a melt viscosity η of the rubber-containing thermoplastic resin composition as measured at a temperature of the rubber-containing thermoplastic resin composition during the discharge from a die and a shear velocity of 122 sec −1 is 600 Pa·sec or more but 2000 Pa·sec or less; a surface temperature of the elastic roller is Tg−70° C. or higher but Tg−20° C. or lower; and η×V/P is 5000 or less, wherein V represents a line velocity (m/min) and P represents a pressure applied by the elastic roller (kgf/cm).

First claim

The invention claimed is:

1. A method for manufacturing an optical film, the method comprising:
molding a sheet-shaped rubber-containing thermoplastic resin composition discharged in a molten state from a die outlet of an extruder by inserting the composition between a pair of smoothing rollers comprising an elastic roller and a cast roller, wherein
a melt viscosity η of the rubber-containing thermoplastic resin composition as measured at a temperature of the rubber-containing thermoplastic resin composition during the discharge from a die and a shear velocity of 122 sec −1 is 600 Pa·sec or more but 2000 Pa·sec or less;
a surface temperature of the elastic roller is Tg−70° C. or higher but Tg−20° C. or lower, wherein Tg represents a glass transition temperature (° C.) of the rubber-containing thermoplastic resin composition; and
η×V/P is 5000 or less, wherein V represents a line velocity (m/min) and P represents a pressure applied by the elastic roller (kgf/cm).

2. The method for manufacturing an optical film according to claim 1 , wherein a direction of flow of the sheet-shaped rubber-containing thermoplastic resin composition is inclined toward a side of the cast roller with respect to a direction of discharge from the die outlet so that an angle which the direction of flow of the sheet-shaped rubber-containing thermoplastic resin composition forms with the direction of discharge from the die outlet is in a range of 0.1 degrees or more but 20 degrees or less.

3. The method for manufacturing an optical film according to claim 1 , wherein the optical film has a thickness of 30 μm or more but less than 80 μm.

4. The method for manufacturing an optical film according to claim 1 , wherein the melt viscosity of the rubber-containing thermoplastic resin composition as measured at 250° C. and a shear velocity of 122 sec −1 is 700 Pa·sec or more but 1250 Pa·sec or less.

5. The method for manufacturing an optical film according to claim 1 , wherein the rubber-containing thermoplastic resin composition contains an acrylic resin and acrylic rubber particles.

6. The method for manufacturing an optical film according to claim 1 , wherein the rubber-containing thermoplastic resin composition contains at least one selected from the group consisting of an acrylic resin copolymerized with an N-substituted maleimide compound as a copolymerization component, a glutaric anhydride acrylic resin, an acrylic resin having a lactone ring structure, a glutarimide acrylic resin, a hydroxyl group- and/or carboxyl group-containing acrylic resin, an aromatic vinyl-containing acrylic polymer obtained by polymerization of an aromatic vinyl monomer and another monomer copolymerizable therewith or a hydrogenated aromatic vinyl-containing acrylic polymer obtained by partial or complete hydrogenation of aromatic rings thereof, and an acrylic polymer containing a cyclic acid anhydride repeating unit.

Assignees

• Kaneka Corp

Inventors

• Kamikariya Naoya

Classifications

• C08J2451/00

  Characterised by the use of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Derivatives of such polymers · CPC title

• B29C2948/922

  Viscosity; Melt flow index [MFI]; Molecular weight · CPC title

• B29C48/92

  Measuring, controlling or regulating · CPC title

• B29C48/022

  characterised by the choice of material · CPC title

• B29K2101/12

  Thermoplastic materials · CPC title