Construction chemical composition for tile mortar

Patent metadata

Field	Value
Publication number	US-9926233-B2
Application number	US-201515529329-A
Country	US
Kind code	B2
Filing date	Dec 17, 2015
Priority date	Dec 18, 2014
Publication date	Mar 27, 2018
Grant date	Mar 27, 2018

Abstract

The present invention relates to a construction chemical composition comprising Portland cement, a water retention agent, a dispersing agent, and a hardening accelerator comprising calcium-silicate-hydrate, as well as a mortar composition containing said construction chemical composition. Although the composition is based on Portland cement it has a pull-off strength after 6 h meeting the DIN requirements and can therefore be used as a fast setting tile mortar.

First claim

The invention claimed is:

1. A construction chemical composition comprising
a) 10 to 60% by weight, based on the total weight of the construction chemical composition, of Portland cement;
b) 0.01 to 3% by weight, based on the total weight of the construction chemical composition, of a water retention agent selected from at least one cellulose ether;
c) 0.1 to 10% by weight, based on the total weight of the construction chemical composition, of a redispersable polymer powder selected from at least one latex powder with a molecular weight of at least 500,000 g/mol; and
d) 0.2 to 3% by weight, based on the total weight of the construction chemical composition, of a hardening accelerator which comprises calcium-silicate-hydrate; and
e) sand.

2. The construction chemical composition according to claim 1 , wherein the hardening accelerator comprises calcium-silicate-hydrate and at least one calcium salt having a solubility in water of ≥1 g/l at 23° C.

3. The construction chemical composition according to claim 2 , wherein the calcium salt is selected from calcium nitrate, calcium acetate, calcium chloride, calcium hydroxide or calcium formate, or a mixture of two or more of these salts.

4. The construction chemical composition according to claim 2 , wherein the amount of calcium salt is in a range of from 0.1 to 2.5% by weight, based on the total weight of the composition.

5. The construction chemical composition according to claim 1 , wherein calcium-silicate-hydrate is obtained by the reaction of a watersoluble calcium compound with a watersoluble silicate compound in presence of a watersoluble dispersant.

6. The construction chemical composition according to claim 1 , wherein an aluminate fast-hardening cement, optionally selected from calcium aluminate cement and calcium sulphoaluminate cement, is contained in an amount of less than 10% by weight, based on the amount of Portland cement.

7. The construction chemical composition according to claim 1 , comprising anionic starch ether in an amount of less than 0.5% by weight, based on the total weight of the composition.

8. The construction chemical composition according claim 1 , wherein the cellulose ether is selected from the group comprising carboxymethyl cellulose, methyl cellulose, methyl hydroxypropyl cellulose, methyl hydroxyethyl cellulose or mixtures of two or more thereof.

9. The construction chemical composition according claim 1 , wherein the latex powder is selected from the group comprising styrene acrylate copolymer, polyvinyl acetate, styrene butadiene copolymer or mixtures of two or more thereof.

10. The construction chemical composition according to claim 1 , wherein the amount of cellulose ether is in a range of from 0.05 to 2% by weight, based on the total weight of the composition.

11. The construction chemical composition according to claim 1 , wherein the amount of latex powder is in a range of from 0.5 to 10% by weight, based on the total weight of the composition.

12. The construction chemical composition according to claim 1 , wherein the amount of the calcium-silicate-hydrate is in a range of from 0.05 to 2% by weight, based on the total weight of the composition.

13. The construction chemical composition according to claim 1 , additionally containing at least one rheology modifier.

14. The construction chemical composition according to claim 1 , additionally containing at least one cationic polymer.

15. A mortar composition containing the construction chemical composition of claim 1 .

16. A method comprising providing the mortar composition according to claim 15 as cementitious tile adhesive or grout mortar for a floor and/or a wall application.

Assignees

• Basf Se

Inventors

• Assmann Alexander
• Biro Christian
• Hesse Christoph

Classifications

• C04B2111/00637

  as glue or binder for uniting building or structural materials · CPC title

• C04B28/04 Primary

  Portland cements · CPC title

• C04B2111/00672

  Pointing or jointing materials · CPC title

• C04B2103/14

  Hardening accelerators · CPC title

• C04B14/06

  Quartz; Sand · CPC title