Abstract

A method of treating an acid effluent including phosphoric acid in accordance with various embodiments may include: providing an acid effluent including phosphoric acid; adding a base and silicon particles from a further effluent to the acid effluent including phosphoric acid so that a mixture is obtained and a solid content is formed; separating from the mixture a solid content including silicon and a salt resulting from a reaction of the base with the acid, so that a clarified effluent can be rejected in the environment and a filter press cake can be obtained and further used as additive for concrete.

First claim

What is claimed is:

1. A method of treating an acid effluent comprising phosphoric acid, the method comprising:
providing an acid effluent comprising phosphoric acid;
generating a mixture by adding to the acid effluent a base and silicon particles; and
separating from the mixture a solid content comprising silicon and a salt resulting from a reaction of the base with the acid.

2. The method of treating an acid effluent according to claim 1 , wherein the base is added before the silicon particles.

3. The method of treating an acid effluent according to claim 1 , wherein the base and the silicon particles are pre-mixed and added to the acid effluent together.

4. The method of treating an acid effluent according to claim 1 , wherein the base is selected from the group consisting of calcium hydroxide, calcium oxide, barium hydroxide, barium oxide, magnesium hydroxide and combinations thereof.

5. The method of treating an acid effluent according to claim 1 , wherein the base is one or more of calcium hydroxide and calcium oxide.

6. The method of treating an acid effluent according to claim 1 , wherein the silicon particles are from a further effluent.

7. The method of treating an acid effluent according to claim 1 , wherein the silicon particles are added in the form of a sediment obtained by adding a base to the further effluent containing silicon.

8. The method of treating an acid effluent according to claim 1 , wherein the solid content is separated by using a filter press.

9. The method of treating an acid effluent according to claim 1 , wherein the acid effluent originates from a processing of one or more wafers.

10. The method of treating an acid effluent according to claim 1 , wherein the acid effluent originates from an etching processing of one or more wafers.

11. The method of treating an acid effluent according to claim 1 , wherein the acid effluent comprises the phosphoric acid in an amount of about 1 to about 3 mol/l.

12. The method of treating an acid effluent according to claim 1 , wherein the amount of base added is such that the pH value of the resulting mixture is from 7 to 8.

13. The method of treating an acid effluent according to claim 1 , wherein the amount of silicon particles added is such to obtain a mass concentration from about 10 g/l to about 100 g/l in the mixture.

14. The method of treating an acid effluent according to claim 1 , wherein the acid effluent is agitated at least during the addition of the base.

15. A method of producing an additive for concrete, the method comprising:
providing an acid effluent comprising phosphoric acid;
generating a mixture by adding to the acid effluent a base and silicon particles; and
feeding the mixture into a filter press so as to obtain a filter press cake comprising silicon and a salt resulting from a reaction of the base with the acid.

16. The method of producing an additive for concrete according to claim 15 , wherein the base is selected from the group consisting of calcium hydroxide, calcium oxide, barium hydroxide, barium oxide, magnesium hydroxide and combinations thereof.

17. The method of producing an additive for concrete according to claim 15 , wherein the base is calcium hydroxide and/or calcium oxide.

18. The method of producing an additive for concrete according to claim 15 , wherein the silicon particles are from a further effluent.

19. An additive for concrete obtained by the method of claim 15 , having a pressed form and comprising silicon and a salt resulting from a reaction of the base with the acid.

20. The additive for concrete according to claim 19 , wherein a solution resulting from a dissolution of at least part of the additive in water is pH neutral.

Assignees

• Infineon Technologies Ag

Inventors

• Kroener Friedrich

Classifications

• C04B18/0418

  Wet materials, e.g. slurries · CPC title

• C04B28/02

  containing hydraulic cements other than calcium sulfates · CPC title

• C02F1/66

  by neutralisation; pH adjustment (for degassing C02F1/20; using ion-exchange C02F1/42; for flocculation or precipitation of suspended impurities C02F1/52; for removing dissolved compounds C02F1/58) · CPC title

• C04B20/023

  Chemical treatment · CPC title

• C04B18/0481 Primary

  Other specific industrial waste materials not provided for elsewhere in C04B18/00 · CPC title