Cross-linkable masses based on organyl-oxysilane-terminated polymers

Patent metadata

Field	Value
Publication number	US-9920229-B2
Application number	US-201414904876-A
Country	US
Kind code	B2
Filing date	Aug 5, 2014
Priority date	Aug 23, 2013
Publication date	Mar 20, 2018
Grant date	Mar 20, 2018

Abstract

Moisture curable compositions having a low modulus and a high resilience are prepared by curing a composition containing a first polymer which predominately contains two moisture-curable silyl groups, and a second polymer which is terminated by an alkoxy group and contains but a single moisture-curable silyl group, or a hydroxyl group.

First claim

The invention claimed is:

1. A moisture-curable composition comprising:
(A) 100 parts by weight of at least one silane-crosslinking polymer of the formula
(HO) x —Y—[O—CO—NH—(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] 2-x   (I)

where
Y is a divalent polymer radical,
R each, independently, is the same or different and is a monovalent, optionally substituted hydrocarbyl radical,
R 1 each, independently, is the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
R 2 each, independently, is may be the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
x is 0 or 1,
a each, independently, is the same or different and is 0, 1 or 2
and
b each, independently, is the same or different and is an integer from 1 to 10,
with the proviso that component (A) includes less than 15 mol % of polymers of the formula (I) with x=1,
(B) 5 to 500 parts by weight of at least one silane-crosslinking polymer of the formula
R 6 —O—Z—[O—CO—NH—(CR 4 2 ) d —SiR 3 c (OR 5 ) 3-c ] 1-y [OH] y   (II)

where

Z is a divalent polymer radical having no hydroxyl group,
R 3 each, independently, is the same or different and is a monovalent, optionally substituted hydrocarbyl radical,
R 4 each, independently, is the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
R 5 each, independently, is the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
R 6 each, independently, is monovalent, optionally substituted hydrocarbyl radical,
y is 0 or 1,
c each, independently, is the same or different and is 0, 1 or 2
and
d may be the same or different and is an integer from 1 to 10,
with the proviso that component (B) includes less than 15 mol % of polymers of the formula (II) with y=1, and,
(I) from 0.01 to 100 parts by weight of at least one non-reactive plasticizer, wherein the moisture-curable composition has a resilience of at least 70%, and a 100% modulus of from 0.1 to 0.5 Mpa, following cure.

2. A moisture-curable composition comprising:
(A) 100 parts by weight of at least one silane-crosslinking polymer of the formula
(HO) x —Y—[O—CO—NH—(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] 2-x   (I)

where
Y is a divalent polymer radical,
R each, independently, is the same or different and is a monovalent, optionally substituted hydrocarbyl radical,
R 1 each, independently, is the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
R 2 each, independently, is may be the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
x is 0 or 1,
a each, independently, is the same or different and is 0, 1 or 2
and
b each, independently, is the same or different and is an integer from 1 to 10,
with the proviso that component (A) includes less than 15 mol % of polymers of the formula (I) with x=1,
(B) 5 to 500 parts by weight of at least one silane-crosslinking polymer of the formula
R 6 —O—Z—[O—CO—NH—(CR 4 2 ) d —SiR 3 c (OR 5 ) 3-c ] 1-y [OH] y   (II)

where

Z is a divalent polymer radical having no hydroxyl group,
R 3 each, independently, is the same or different and is a monovalent, optionally substituted hydrocarbyl radical,
R 4 each, independently, is the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
R 5 each, independently, is the same or different and is a hydrogen atom or a monovalent, optionally substituted hydrocarbyl radical,
R 6 each, independently, is monovalent, optionally substituted hydrocarbyl radical,
y is 0 or 1,
c each, independently, is the same or different and is 0, 1 or 2
and
d may be the same or different and is an integer from 1 to 10,
with the proviso that component (B) includes less than 15 mol % of polymers of the formula (II) with y=1, and
(I) from 0.01 to 100 parts by weight of at least one non-reactive plasticizer

wherein at least 70 mol percent of component (A) polymers, b=3, R 1 =H, and a=0, and in the remaining polymers of component (A), b=1, R 1 =H, and wherein at least 70 mol percent of component (B) polymers, d=1, R 4 =H, and c=1, wherein the moisture-curable composition has a resilience of at least 70%, and a 100% modulus of from 0.1 to 0.5 Mpa, following cure.

3. The composition of claim 1 , wherein component (A) includes less than 5 mol % of polymers of the formula (I) with x=1.

4. The composition of claim 2 , wherein component (A) includes less than 5 mol % of polymers of the formula (I) with x=1.

5. The composition of claim 1 , wherein component (B) includes less than 5 mol % of polymers of the formula (II) with y=1.

6. The composition of claim 2 , wherein component (B) includes less than 5 mol % of polymers of the formula (II) with y=1.

7. The composition of any of claim 1 , wherein the composition contains 10 to 100 parts by weight of polymer (B).

8. The composition of any of claim 2 , wherein the composition contains 10 to 100 parts by weight of polymer (B).

9. The composition of claim 1 , further comprising at least one organosilicon compound (C) having nitrogen atoms which are not bonded directly to a carbonyl group.

10. The composition of claim 2 , further comprising at least one organosilicon compound (C) having nitrogen atoms which are not bonded directly to a carbonyl group.

11. The composition of claim 9 , wherein the organosilicon compounds (C) are compounds containing units of the formula
D e Si(OR 7 ) f R 8 g O (4-e-f-g)/2   (III)

where
R 7 each, independently, is the same or different and is a hydrogen atom or optionally substituted hydrocarbyl radicals,
D each, independently, are the same or different and are monovalent, SiC-bonded radicals having nitrogen atoms which are not a bonded directly to carbonyl group,
R 8 each, independently, are the same or different and are a monovalent, optionally substituted, SiC-bonded, nitrogen-free organic radicals,
e is 0, 1, 2, 3 or 4,
f is 0, 1, 2 or 3 and
g is 0, 1, 2 or 3,
with the proviso that the sum total of e+f+g is less than or equal to 4 and at least one D radical is present per molecule.

12. The composition of claim 10 , wherein the organosilicon compounds (C) are compounds containing units of the formula
D e Si(OR 7 ) f R 8 g O (4-e-f-g)/2   (III)

where
R 7 each, independently, is the same or different and is a hydrogen atom or optionally substituted hydrocarbyl radicals,
D each, independently, are the same or different and are monovalent, SiC-bonded radicals having nitrogen atoms which are not a bonded directly to carbonyl group,
R 8 each, independently, are the same or different and are a monovalent, optionally substituted, SiC-bonded, nitrogen-free organic radicals,
e is 0, 1, 2, 3 or 4,
f is 0, 1, 2 or 3 and
g is 0, 1, 2 or 3,
with the proviso that the sum total of e+f+g is less than or equal to 4 and at least one D radical is present per molecule.

13. The composition of claim 1 , comprising:
(A) 100 parts by weight of polymer(s) (A),
(B) 5 to 500 parts of polymer(s) (B),
(C) 0.1 to 10 parts by weight of organosilicon compounds not having nitrogen atoms bonded directly to carbonyl groups,
(D) 50 to 500 parts by weight of fillers,
(E) optionally, silicone resins,
(F) opt

Assignees

• Wacker Chemie Ag

Inventors

• Stanjek Volker
• Zander Lars

Classifications

• C08G65/336 Primary

  containing silicon · CPC title

• C09K2003/1056

  Moisture-curable materials · CPC title

• C09J2471/00

  Presence of polyether · CPC title

• C08L71/02

  Polyalkylene oxides · CPC title

• C09J171/02

  Polyalkylene oxides · CPC title