Liquid binder composition for binding fibrous materials

Patent metadata

Field	Value
Publication number	US-9920197-B2
Application number	US-201313915651-A
Country	US
Kind code	B2
Filing date	Jun 12, 2013
Priority date	Dec 20, 2012
Publication date	Mar 20, 2018
Grant date	Mar 20, 2018

Abstract

A liquid binder composition for binding fibrous materials in the fabrication of resin-infusible preform is disclosed. The binder composition is an aqueous dispersion containing (a) one or more multifunctional epoxy resins, (b) at least one thermoplastic polymer, (c) one or more surfactants selected from anionic surfactants, nonionic surfactants, and combinations thereof, (d) water, and is essentially free of organic solvents. Also disclosed is an emulsification process for producing the liquid binder composition.

First claim

What is claimed is:

1. A liquid binder composition for binding fibrous materials comprising:
a) one or more multifunctional epoxy resins;
b) a polyarylsulphone comprising repeating units of -(PhSO 2 Ph)-, where Ph is phenylene;
c) at least one non-ionic surfactant selected from block copolymers comprising hydrophilic and hydrophobic blocks, wherein the hydrophilic blocks are derived from polyethyleneoxide or poly (ethylene-propylene oxide) or poly(ethylene-butylene oxide); and
d) water,
wherein said composition is an emulsion which is substantially free of organic solvents, and
wherein said polyarylsulphone is soluble in a thermoset matrix resin upon curing of the matrix resin.

2. The liquid binder composition of claim 1 , wherein said polyarylsulphone is soluble in one or more epoxy resins upon curing thereof.

3. The liquid binder composition of claim 1 , wherein said polyarylsulphone further comprises one or more reactive pendant or end groups selected from: OH, NH 2 , NHR′ or —SH, where R′ is a hydrocarbon group containing up to 8 carbon atoms, epoxy, (meth)acrylate, (iso)cyanate, isocyanate ester, acetylene, ethylene, maleimide, anhydride, and oxazoline.

4. The liquid binder composition of claim 3 , wherein the -(PhSO 2 Ph)- unit is present in the polyarylsulphone in such a proportion that on average at least two of said unit -(PhSO 2 Ph)- are in sequence in each polymer chain present.

5. The liquid binder composition of claim 1 , wherein the polyarylsulphone is a copolymer containing the following units:
X-PhSO 2 Ph-X-PhSO 2 Ph (“PES”) and  (I)

X-(Ph) a -X-PhSO 2 Ph (“PEES”)  (II)

wherein X is O or S and may differ from unit to unit, and a is 1-4.

6. The liquid binder composition of claim 1 , wherein said polyarylsulphone has a glass transition temperature (T g ) of greater than 150° C. as measured by Differential scanning calorimetry (DSC).

7. The liquid binder composition of claim 1 , further comprising
an anionic surfactant which is represented by the following formula:
A-R

wherein R is an alkyl, aryl, aryl-alkyl, or an alkylene chain having 4-50 carbon atoms (C 4 to C 50 ); and A is lithium, sodium, potassium, ammonium, quaternary ammonium amine salt of a carboxylic-, or sulfonic-, or phosphoric acid group.

8. The liquid binder composition of claim 1 , wherein the composition has a solid content of 0.1%-10%.

9. The liquid binder composition of claim 1 further comprising a crosslinker selected from aminoplasts, phenolics, azlactones, aziridines, and blocked isocyanates.

10. The liquid binder composition of claim 1 , wherein a combination of non-ionic surfactants is present and the non-ionic surfactants are (i) a block copolymer of Polyethyleneoxide (PEO) and Polypropylene oxide (PPO) with an average molecular weight in the range of 8000-18000 Da and (ii) an alkoxylated aliphatic diamine with an average molecular weight in the range of 18000-25000 Da.

11. The liquid binder composition of claim 7 , wherein a combination of non-ionic surfactants is present and the non-ionic surfactants are (i) a block copolymer of Polyethyleneoxide (PEO) and Polypropylene oxide (PPO) with an average molecular weight in the range of 8000-18000 Da and (ii) an alkoxylated aliphatic diamine with an average molecular weight in the range of 18000-25000 Da.

Assignees

• Cytec Tech Corp

Inventors

• Restuccia Carmelo Luca
• Hobisch Gerald
• Jacobs William
• Ponsolle Dominique

Classifications

• Y10T442/60

  Nonwoven fabric [i.e., nonwoven strand or fiber material] · CPC title

• Y10T442/2738

  Coating or impregnation intended to function as an adhesive to solid surfaces subsequently associated therewith · CPC title

• Y10T442/30

  Woven fabric [i.e., woven strand or strip material] · CPC title

• C08L63/00 Primary

  Compositions of epoxy resins; Compositions of derivatives of epoxy resins · CPC title

• D04H5/04

  strengthened or consolidated by applying or incorporating chemical or thermo-activatable bonding agents in solid or liquid form · CPC title