Aluminum alloy brazing sheet

Patent metadata

Field	Value
Publication number	US-9914185-B2
Application number	US-201314398889-A
Country	US
Kind code	B2
Filing date	May 2, 2013
Priority date	May 7, 2012
Publication date	Mar 13, 2018
Grant date	Mar 13, 2018

Abstract

An aluminum alloy brazing sheet makes it possible to inexpensively braze aluminum in a nitrogen gas furnace without using flux and a toxic element. The aluminum alloy brazing sheet is used for brazing aluminum in an inert gas atmosphere without using flux, and includes a core material and a filler metal, one side or each side of the core material being clad with the filler metal, the core material being formed of an aluminum alloy that includes 0.2 to 1.3 mass % of Mg, and the filler metal including 6 to 13 mass % of Si and 0.004 to 0.1 mass % of Li, with the balance being aluminum and unavoidable impurities.

First claim

The invention claimed is:

1. An aluminum alloy brazing sheet for brazing aluminum in an inert gas atmosphere without using flux, the brazing sheet comprising a core material, an intermediate material, and a filler metal, one side or each side of the core material being clad with the filler metal through the intermediate material, the core material being formed of an aluminum alloy, the intermediate material being formed of an aluminum alloy that includes 0.2 to 1.3 mass % of Mg, with the balance being aluminum and unavoidable impurities and the filler metal including 6 to 13 mass % of Si and 0.004 to 0.1 mass % of Li, with the balance being aluminum and unavoidable impurities, wherein the aluminum alloy that forms the intermediate material includes 0.2 to 1.3 mass % of Mg, and further includes one or more of 0.05 to 1.8 mass % of Mn, 1.0 mass % or less of Si, 1.0 mass % or less of Fe, 0.9 mass % or less of Cu, 6.5 mass % or less of Zn, 0.2 mass % or less of Ti, and 0.5 mass % or less of Zr, with the balance being aluminum and unavoidable impurities.

2. The aluminum alloy brazing sheet according to claim 1 , wherein the aluminum alloy that forms the core material includes 0.05 to 1.8 mass % of Mn, and one or more of 1.0 mass % or less of Si, 1.0 mass % or less of Fe, 0.9 mass % or less of Cu, 6.5 mass % or less of Zn, 0.2 mass % or less of Ti, and 0.5 mass % or less of Zr, with the balance being aluminum and unavoidable impurities.

3. The aluminum alloy brazing sheet according to claim 1 , wherein the aluminum alloy that forms the core material includes0.05 to 1.8 mass % of Mn, and one or more of 1.0 mass % or less of Si, 1.0 mass % or less of Fe, 0.9 mass % or less of Cu, 6.5 mass % or less of Zn, 0.2 mass % or less of Ti, and 0.5 mass % or less of Zr, with the balance being aluminum and unavoidable impurities.

4. The aluminum alloy brazing sheet according to claim 1 , wherein the filler metal further includes one or more of 0.004 to 0.2 mass % of Bi, 0.05 to 0.4 mass % of Mg, 0.002 to 0.05 mass % of Sr and 0.003 to 0.07 mass % of Sb, 0.05 to 0.8 mass % of Fe, 0.05 to 0.2mass % of Mn, and 0.01 to 0.15 mass % of Ti.

5. An aluminum alloy brazing sheet for brazing aluminum in an inert gas atmosphere without using flux, the brazing sheet comprising a core material, an intermediate material, a filler metal and a sacrificial anode material, wherein one side of the core material being clad with the filler metal through the intermediate material, and the other side of the core material is clad with a sacrificial anode material, the core material being formed of an aluminum alloy, the intermediate material being formed of an aluminum alloy that includes 0.2 to 1.3 mass % of Mg, with the balance being aluminum and unavoidable impurities, the filler metal including 6 to 13 mass % of Si and 0.004 to 0.1 mass % of Li, with the balance being aluminum and unavoidable impurities, and the sacrificial anode material including 0.9 to 6 mass % of Zn, with the balance being aluminum and unavoidable impurities, wherein the aluminum alloy that forms the intermediate material includes 0.2 to 1.3 mass % of Mg, and further includes one or more of 0.05 to 1.8 mass % of Mn, 1.0 mass % or less of Si, 1.0 mass % or less of Fe, 0.9 mass % or less of Cu, 6.5 mass % or less of Zn, 0.2 mass % or less of Ti, and 0.5 mass % or less of Zr, with the balance being aluminum and unavoidable impurities.

6. The aluminum alloy brazing sheet according to claim 5 , wherein the aluminum alloy that forms the core material includes 0.05 to 1.8 mass % of Mn, and one or more of 1.0 mass % or less of Si, 1.0 mass % or less of Fe, 0.9 mass % or less of Cu, 6.5 mass % or less of Zn, 0.2 mass % or less of Ti, and 0.5 mass % or less of Zr, with the balance being aluminum and unavoidable impurities.

7. The aluminum alloy brazing sheet according to claim 5 , wherein the aluminum alloy that forms the core material includes 0.05 to 1.8 mass % of Mn, and one or more of 1.0 mass % or less of Si, 1.0 mass % or less of Fe, 0.9 mass % or less of Cu, 6.5 mass % or less of Zn, 0.2 mass % or less of Ti, and 0.5 mass % or less of Zr, with the balance being aluminum and unavoidable impurities.

8. The aluminum alloy brazing sheet according to claim 5 , wherein the filler metal further includes one or more of 0.004 to 0.2 mass % of Bi, 0.05 to 0.4 mass % of Mg, 0.002 to 0.05 mass % of Sr and 0.003 to 0.07 mass % of Sb, 0.05 to 0.8 mass % of Fe, 0.05 to 0.2 mass % of Mn, and 0.01 to 0.15 mass % of Ti.

Assignees

• Uacj Corp

Inventors

• Itoh Yasunaga
• YAMAYOSHI Tomoki

Classifications

• C22C21/10

  with zinc as the next major constituent · CPC title

• B23K1/012

  Soldering with the use of hot gas · CPC title

• C22C21/02

  with silicon as the next major constituent · CPC title

• B23K35/286

  Al as the principal constituent · CPC title

• C22C21/04

  Modified aluminium-silicon alloys · CPC title