Semi-solid electrolytes for batteries

Patent metadata

Field	Value
Publication number	US-9911984-B2
Application number	US-201514740356-A
Country	US
Kind code	B2
Filing date	Jun 16, 2015
Priority date	Jun 17, 2014
Publication date	Mar 6, 2018
Grant date	Mar 6, 2018

Abstract

Semi-solid electrolyte compositions are disclosed. The semi-solid electrolyte compositions contain a glyme or mixture of glymes, a lithium salt(s), and a polymeric complexing agent(s).

First claim

We claim:

1. A electrolyte composition comprising:
a glyme or a mixture of glymes, wherein the glyme is tetraethylene glycol dimethyl ether (TEGDME), bis(2-methoxyethyl) ether (Diglyme), triethylene glycol dimethyl ether (Triglyme), poly(ethylene glycol) (mw: 200-2000), polyglycol methyl ether (mw: 200-2000), ethylene glycol dibutyl ether, or combinations of any of them wherein the glyme is present in an amount of from 34 to 54 percent by weight based on the total weight of the glyme and lithium salt combined;
a lithium salt, wherein the lithium salt is present in an amount of from 40 to 66 percent by weight based on the total weight of the glyme and lithium salt combined; and
a polymeric complexing agent present in an amount of from 5 to 30 percent by weight, based on the total weight of the electrolyte composition, wherein the electrolyte composition has a storage modulus (1 Hz, 37° C.) of from 10 1 to 1×10 6 Pa and has an ionic conductivity of at least 1×10 −4 S/cm at 37° C.

2. The electrolyte composition of claim 1 wherein the polymeric complexing agent is PEO.

3. The electrolyte composition of claim 1 wherein the lithium salt is lithium bis(trifluoromethylsulfonyl) imide (LiTFSI), lithium bis(pentafluoroethylsulfonyl) imide (LiBETI), lithium tris(trifluorosulfonyl) methide, lithium perchlorate (LiCIO4), lithium tetrafluoroborate (LiBF4), lithium hexafluoroarsenate (LiAsF6), lithium hexafluorophosphate (LiPF6) or combinations of any of them.

4. The electrolyte composition of claim 1 wherein the polymeric complexing agent is PEO, copolymers of ethylene oxide with silicone, urethane, styrene, alkyl methacrylate monomers, ethylene oxide grafted onto main chains of phosphazene, silicone polymers, polyacrylonitrile, polyimide, poly methyl methacrylate, poly acrylic acid, or poly lithium acrylate.

5. An electrolyte comprising:
a glyme or mixture of glymes present in an amount of from 40 to 65 mole percent, the mole percent based on the total moles of glyme or mixture of glymes and lithium salt, wherein the glyme is tetraethylene glycol dimethyl ether (TEGDME), bis(2-methoxyethyl) ether (Diglyme), triethylene glycol dimethyl ether (Triglyme), poly(ethylene glycol) (mw: 200-2000), polyglycol methyl ether (mw: 200-2000), ethylene glycol dibutyl ether, or combinations of any of them;
a lithium salt present in an amount of 35 to 60 mole percent, the mole percent based on the total moles of glyme or mixture of glymes and lithium salt; and
a polymeric complexing agent present in an amount of from 5 to 30 percent by weight, based on the total weight of the electrolyte composition, wherein the electrolyte composition has a storage modulus (1 Hz, 37° C.) of from 10 1 to 1×10 6 Pa and has an ionic conductivity of at least 1×10 −4 S/cm at 37° C.

6. The electrolyte composition of claim 5 wherein the polymeric complexing agent is PEO.

7. The electrolyte composition of claim 5 wherein the lithium salt is lithium bis(trifluoromethylsulfonyl) imide (LiTFSI), lithium bis(pentafluoroethylsulfonyl) imide (LiBETI), lithium tris(trifluorosulfonyl) methide, lithium perchlorate (LiCIO4), lithium tetrafluoroborate (LiBF4), lithium hexafluoroarsenate (LiAsF6), lithium hexafluorophosphate (LiPF6) or combinations of any of them.

8. The electrolyte composition of claim 5 wherein the polymeric complexing agent is PEO, copolymers of ethylene oxide with silicone, urethane, styrene, alkyl methacrylate monomers, ethylene oxide grafted onto main chains of phosphazene, silicone polymers, polyacrylonitrile, polyimide, poly methyl methacrylate, poly acrylic acid, or poly lithium acrylate.

9. An electrolyte composition consisting essentially of:
a glyme or a mixture of glymes them wherein the glyme is present in an amount of from 34 to 54 percent by weight based on the total weight of the glyme and lithium salt combined;
a lithium salt, wherein the lithium salt is present in an amount of from 40 to 66 percent by weight based on the total weight of the glyme and lithium salt combined; and
a polymeric complexing agent present in an amount of from 5 to 30 percent by weight, based on the total weight of the electrolyte composition, wherein the electrolyte composition has a storage modulus (1 Hz, 37° C.) of from 10 1 to 1×10 6 Pa and has an ionic conductivity of at least 1×10 −4 S/cm at 37° C.

10. The electrolyte composition of claim 9 wherein the polymeric complexing agent is PEO.

11. An electrochemical cell comprising:
a casing;
an anode within the casing;
a cathode within the casing; and
an electrolyte of claim 1 .

12. The electrochemical cell of claim 11 wherein the anode contains a material selected from lithium metal, lithium alloys, graphitic carbon, petroleum coke, lithium titanate or combinations of any of them.

13. The electrochemical cell of claim 11 wherein the cathode contains a material selected from silver vanadium oxide, carbon monofluoride, manganese oxide, LiCoO 2 , LiMn 2 O 4 , LiNi 1/3 Mn 1/3 Co 1/3 O 2 , LiNiO 2 , S, or lithium sulfide.

14. The electrochemical cell of claim 11 wherein the casing is a coin cell, laminated foil pack, an adhesive bonded metal case, or a crimped metal case.

15. The electrochemical cell of claim 11 , wherein the casing is hermetic.

16. The electrochemical cell of claim 11 , wherein the electrochemical cell is a primary battery.

Assignees

• Medtronic Inc

Inventors

• Tamirisa Prabhakar A
• Klaassen Jody J
• Ye Hui

Classifications

• H01M4/525

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M2300/0085

  Immobilising or gelification of electrolyte · CPC title

• H01M10/0568

  characterised by the solutes · CPC title

• H01M2300/0025

  Organic electrolyte · CPC title

• H01M10/0569

  characterised by the solvents · CPC title