Water-emulsifiable isocyanates for coatings having an improved gloss

Patent metadata

Field	Value
Publication number	US-9902871-B2
Application number	US-201414888283-A
Country	US
Kind code	B2
Filing date	Apr 22, 2014
Priority date	May 2, 2013
Publication date	Feb 27, 2018
Grant date	Feb 27, 2018

Abstract

The invention relates to new, water-emulsifiable isocyanates, to a process for preparing water-emulsifiable isocyanates, and to the use thereof.

First claim

The invention claimed is:

1. A water-emulsifiable polyisocyanate composition, comprising:
(A) a polyisocyanate comprising at least one (cyclo)aliphatic diisocyanate,
(B) a compound (B) comprising at least two isocyanate-reactive groups, and at least one group selected from the group consisting of a thioether group (—S—), a selanyl group (—Se—), a sulfoxide group (—S(═O)—), and a sulfone group (—S(═O) 2 —),
(C) a compound comprising an isocyanate-reactive group and a dispersive group, and
(D) optionally a solvent,

wherein
a ratio of NCO groups in (A) to isocyanate-reactive groups in (B) and (C) is from 5:1 to 100:1,
an ethylene oxide group content, calculated as 44 g/mol, based on a sum of (A), (B), and (C), is at least 12 wt. %,
an amount of component (C) is at least 5 and up to 25 wt. %, and
the composition has a viscosity at 23° C. of from 2500 mPas to 12 000 mPas.

2. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the at least one (cyclo)aliphatic diisocyanate is selected from the group consisting of hexamethylene diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, isophorone diisocyanate, 4,4′-di(isocyanatocyclohexyl)methane, and 2,4′-di(isocyanatocyclohexyl)methane.

3. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the polyisocyanate is an isocyanurate of 1,6-hexamethylene diisocyanate.

4. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the component (B) is selected from the group consisting of a compound of (B1), a compound of (B2), a compound of (B3), and a compound of (B4):

where
R 4 and R 5 independently are each C 1 -C 18 alkylene, or—optionally interrupted by one or more oxygen atoms and/or sulfur atoms, —C 2 -C 18 alkylene, C 6 -C 12 arylene, or C 5 -C 12 cycloalkyl, each of which is optionally substituted by a functional group, aryl, alkyl, aryloxy, alkyloxy, halogen, a heteroatom and/or a heterocycle.

5. The water-emulsifiable polyisocyanate composition according to claim 4 , wherein R 4 and R 5 independently are selected from the group consisting of 1,2-ethylene, 1,2-propylene, 1,3-propylene, 1,4-butylene, 1,5-pentylene, 1,6-hexylene, 2-methyl-1,3-propylene, 2-ethyl-1,3-propylene, 2,2-dimethyl-1,3-propylene, 2,2-dimethyl-1,4-butylene, 3-oxa-1,5-pentylene, 3,6-dioxa-1,8-octylene, 3,6,9-trioxa-1,11-undecylene, 1,1-, 1,2-, 1,3- or 1,4-cyclohexylene, 1,2- or 1,3-cyclopentylene, 1,2-, 1,3-, or 1,4-phenylene, and 4,4′-biphenylene.

6. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the component (B) is selected from the group consisting of 3-thiapentane-1,5-diol (thiodiglycol), 1,5-dimethyl-3-thiapentane-1,5-diol, 1-methyl-3-thiahexane-1,6-diol, 4-thiaheptane-1,7-diol, and 4,4′-dihydroxydiphenyl sulfide.

7. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the compound (C) comprises a monoalcohol comprising at least 7 ethylene oxide groups.

8. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the compound (C) comprises a compound of formula
R 1 —O—[—X i ] k —H

where
R 1 is C 1 -C 18 alkyl, or—optionally interrupted by one or more oxygen atoms and/or sulfur atoms, —C 2 -C 18 alkyl, C 6 -C 12 aryl, C 5 -C 12 cycloalkyl, or a five- to six-membered heterocycle comprising oxygen, nitrogen and/or sulfur atoms,
k is an integer of from 7 to 30, and
each X i , for i=1 to k, independently of one another, is —CH 2 —CH 2 —O—.

9. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the compound (C) comprises one compound of formula
RG-R 6 -DG

where
RG is at least one isocyanate-reactive group,
DG is at least one dispersive group selected from the group consisting of —COOH, —SO 3 H, —OPO 3 H, and —PO 3 H, and also an anionic form thereof, which optionally is associated with any desired counterion, and
R 6 is an aliphatic, cycloaliphatic, or aromatic radical comprising 1 to 20 carbon atoms.

10. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the compound (C) is selected from the group consisting of mercaptoacetic acid, mercaptopropionic acid, thiolactic acid, mercaptosuccinic acid, glycine, iminodiacetic acid, sarcosine, alanine, β-alanine, leucine, isoleucine, aminobutyric acid, hydroxyacetic acid, hydroxypivalic acid, lactic acid, hydroxysuccinic acid, hydroxydecanoic acid, dimethylolpropionic acid, dimethylolbutyric acid, ethylenediaminetriacetic acid, hydroxydodecanoic acid, hydroxyhexadecanoic acid, 12-hydroxystearic acid, aminobenzenesulfonic acids substituted on the ring by alkyl, aminonaphthalenecarboxylic acid, hydroxyethanesulfonic acid, hydroxypropanesulfonic acid, mercaptoethanesulfonic acid, mercaptopropanesulfonic acid, aminomethanesulfonic acid, taurine, aminopropanesulfonic acid, N-alkyl-, -cycloalkyl-, or -aryl-substituted aminomethanesulfonic acid or aminopropanesulfonic acid, and an alkali metal, an alkaline earth metal, or an ammonium salt thereof.

11. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the compound (C) is a phosphoric ester of formulae (Ia) or (Ib) or a mixture thereof

where
R 10 and R 11 independently are alkyl, cycloalkyl, aryl, or aralkyl.

12. A method for making a coating material, the method comprising:
incorporating the water-emulsifiable polyisocyanate composition according to claim 1 into the coating material,
wherein the coating material is suitable for wood, wood veneer, paper, board, card, textile, leather, nonwoven, plastics surface, glass, ceramic, mineral building material, metal, or coated metal.

13. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein the compound (C) is a phosphoric ester of formulae (Ia) or (Ib) or a mixture thereof

where
R 10 and R 11 have formula (II)
R 12 —O—[—X i —] n —  (II)

where
R 12 is C 1 to C 20 alkyl,
n is 0 or a positive integer from 1 to 20, and
each X i , for i=1 to n, is independently selected from the group consisting of —CH_—CH 2 —O—, —CH 2 —CH(CH 3 )—O—, and —CH(CH 3 )—CH 2 —O—.

14. The water-emulsifiable polyisocyanate composition according to claim 1 , wherein when the composition is applied to a substrate and cured to form a coating, the coating has a gloss determined at an angle of 20° of 54.6 to 71.8.

15. The water-emulsifiable polyisocyanate composition according to claim 1 , which comprises 0.5 to 15 wt. %, based on the sum of (A), (B) and (C).

16. The water-emulsifiable polyisocyanate composition according to claim 1 , which comprises 1 to 10 wt. %, based on the sum of (A), (B) and (C).

17. A water-emulsifiable polyisocyanate composition, comprising in at least partially reacted form:
(A) a polyisocyanate comprising at least one (cyclo)aliphatic diisocyanate,
(B) a compound (B) comprising at least two isocyanate-reactive groups, and at least one group selected from the group consisting of a thioether group (—S—), a selanyl group (—Se—), a sulfoxide group (—S(═O)—), and a sulfone group (—S(═O) 2 —), and
(C) a compound comprising an isocyanate-reactive group and a dispersive group, wherein
a ratio of NCO groups in (A) to isocyanate-reactive groups in (B

Assignees

• Basf Se

Inventors

• Steinbrecher Angelika Maria
• Haeberle Karl
• Lucas Frederic

Classifications

• C08G18/585

  having sulfur · CPC title

• C08G18/283

  Compounds containing ether groups, e.g. oxyalkylated monohydroxy compounds · CPC title

• C08K5/29

  Compounds containing {one or more} carbon-to-nitrogen double bonds · CPC title

• C08G18/52 Primary

  Polythioethers · CPC title

• C08G18/0819

  containing anionic or anionogenic groups · CPC title