Process for unitary graphene layer or graphene single crystal

Patent metadata

Field	Value
Publication number	US-9890469-B2
Application number	US-201615354706-A
Country	US
Kind code	B2
Filing date	Nov 17, 2016
Priority date	Nov 26, 2012
Publication date	Feb 13, 2018
Grant date	Feb 13, 2018

Abstract

A unitary graphene layer or graphene single crystal containing closely packed and chemically bonded parallel graphene planes having an inter-graphene plane spacing of 0.335 to 0.40 nm and an oxygen content of 0.01% to 10% by weight, which unitary graphene layer or graphene single crystal is obtained from heat-treating a graphene oxide gel at a temperature higher than 100° C., wherein the average mis-orientation angle between two graphene planes is less than 10 degrees, more typically less than 5 degrees. The molecules in the graphene oxide gel, upon drying and heat-treating, are chemically interconnected and integrated into a unitary graphene entity containing no discrete graphite flake or graphene platelet. This graphene monolith exhibits a combination of exceptional thermal conductivity, electrical conductivity, mechanical strength, surface smoothness, surface hardness, and scratch resistance unmatched by any thin-film material of comparable thickness range.

First claim

We claim:

1. A process for producing a unitary graphene layer or graphene single crystal containing closely packed and chemically bonded parallel graphene oxide planes having an inter plane spacing of 0.335 to 0.40 nm, a thickness greater than 10 nm, an electrical conductivity greater than 1,500 S/cm, a thermal conductivity greater than 600 W/mK, a physical density greater than 1.8 g/cm3, an oxygen content of 0.01% to 10% by weight, and an average mis-orientation angle between two graphene oxide planes is less than 10 degrees, said process comprising:
a. preparing a graphene oxide gel having graphene oxide molecules dispersed in a fluid medium, wherein the graphene oxide gel is optically transparent or translucent;
b. depositing a layer of said graphene oxide gel onto a surface of a supporting substrate to form a deposited graphene oxide gel thereon;
c. partially or completely removing said fluid medium from the deposited graphene oxide gel layer to form a graphene oxide layer; and
d. heat-treating the graphene oxide layer to form said unitary graphene layer or graphene single crystal at a temperature higher than 500° C.

2. The process of claim 1 , wherein said graphene oxide gel is prepared by immersing a graphitic material in a powder or fibrous form in an oxidizing liquid to form an optically opaque suspension in a reaction vessel at a reaction temperature for a length of time sufficient to obtain a graphene oxide gel that is optically transparent or translucent, wherein said graphene oxide gel is composed of graphene oxide molecules dispersed in an acidic medium having a pH value of no higher than 5 and said graphene oxide molecules have an oxygen content no less than 20% by weight.

3. The process of claim 1 , wherein said graphene oxide gel is prepared by immersing a graphitic material in an oxidizing agent to form an optically opaque suspension and allowing an oxidizing reaction to proceed until an optically transparent or translucent solution is formed, and wherein said graphitic material is selected from natural graphite, artificial graphite, meso-phase carbon, meso-phase pitch, meso-carbon micro-bead, soft carbon, hard carbon, coke, carbon fiber, carbon nano-fiber, carbon nano-tube, or a combination thereof.

4. The process of claim 1 , further comprising a step of compressing said graphene oxide layer.

5. The process of claim 4 , further comprising a step of further heat treatment after said step of compressing.

6. The process of claim 1 , wherein said steps (b) and (c) include feeding a sheet of a solid substrate material from a roller to a deposition zone, depositing a layer of graphene oxide gel onto a surface of said sheet of solid substrate material to form a graphene oxide gel layer thereon, drying said graphene oxide gel to form a dried graphene oxide layer deposited on said substrate surface, and collecting graphene oxide layer-deposited substrate sheet on a collector roller.

7. The process of claim 1 , wherein said fluid medium of said graphene oxide gel is selected from the group consisting of water, polar solvents including alcohol, a mixture of water and acid, and combinations thereof.

8. The process of claim 1 , wherein said fluid medium is removed using a vacuum oven.

9. The process of claim 1 , wherein said graphene oxide molecules in said graphene oxide gel have an average molecular weight less than 43,000 g/mole.

10. The process of claim 1 , wherein said graphene oxide molecules in said graphene oxide gel have an average molecular weight less than 4,000 g/mole.

11. The process of claim 1 , wherein said graphene oxide molecules in said graphene oxide gel have an average molecular weight between 200 g/mole and 4,000 g/mole.

12. The process of claim 1 , wherein said graphene oxide molecules form covalent bonds primarily in an edge to edge manner.

13. The process of claim 1 , wherein said heat-treatment temperature is higher than 1000° C.

14. The process of claim 1 , wherein said heat-treatment temperature is higher than 1500° C.

15. The process of claim 1 , wherein said heat-treatment temperature is higher than 2200° C.

16. The process of claim 1 , wherein said deposited graphene oxide gel has a thickness of less than 10 mm prior to drying.

17. The process of claim 1 , wherein said deposited graphene oxide gel has a thickness of less than 1 mm prior to drying.

18. The process of claim 1 , wherein said deposited graphene oxide gel has a thickness of less than 500 μm prior to drying.

19. The process of claim 1 , wherein said unitary graphene layer or graphene single crystal has a thickness greater than 1 nm and less than 200 μm.

20. The process of claim 1 , wherein said unitary graphene layer or graphene single crystal has a thickness greater than 1 μm and less than 100 μm.

21. The process of claim 1 , wherein said graphene single crystal has a lateral size greater than 100 μm.

22. The process of claim 1 , wherein said graphene single crystal has a lateral size greater than 1 mm.

23. The process of claim 1 , wherein said an oxygen content is between 0.01% and 2% by weight.

Assignees

• Zhamu Aruna
• Xiong Wei
• Jang Bor Z
• Nanotek Instruments Inc

Inventors

• Zhamu Aruna
• Xiong Wei
• Jang Bor Z

Classifications

• B82Y30/00

  Nanotechnology for materials or surface science, e.g. nanocomposites · CPC title

• C01P2006/80

  Compositional purity · CPC title

• C01B32/198

  Graphene oxide · CPC title

• C30B29/02

  Elements · CPC title

• C01B32/192

  starting from graphitic oxides · CPC title