Resin particles and process for producing same, antiglare film, light-diffusing resin composition, and external preparation

Patent metadata

Field	Value
Publication number	US-9890223-B2
Application number	US-201113819867-A
Country	US
Kind code	B2
Filing date	Sep 28, 2011
Priority date	Sep 28, 2010
Publication date	Feb 13, 2018
Grant date	Feb 13, 2018

Abstract

A process for producing resin particles includes a step in which a polymerizable mixture including a polymerizable monomer including at least one of a styrene-based monomer and a (meth)acrylic-based monomer, and a polymerization initiator is absorbed into seed particles in an aqueous medium, without using a dispersant, in the presence of an anionic surfactant not having a polyoxyethylene chain but having an alkyl group; and a step in which the polymerizable monomer is polymerized in an aqueous medium, without using a dispersant, in the presence of an anionic surfactant having a polyoxyethylene chain to thereby obtain resin particles. The resin particles include a resin derived from a polymerizable monomer including at least one of a styrene-based monomer and a (meth)acrylic-based monomer. The proportion by number of particles having a particle diameter in the range of from 80 to 120% of the volume-average particle diameter is 85% or more.

First claim

The invention claimed is:

1. Resin particles that:
are obtained by the process comprising
absorbing a polymerizable mixture comprising a polymerizable monomer comprising at least one of a monofunctional styrene-based monomer and a monofunctional (meth)acrylic-based monomer, and a polymerization initiator into seed particles in an aqueous medium, without using a dispersant, in the presence of an anionic surfactant not having a polyoxyethylene chain but having an alkyl group; and
polymerizing the polymerizable monomer in an aqueous medium, without using a dispersant, in the presence of an anionic surfactant having a polyoxyethylene chain to thereby obtain resin particles; wherein
the anionic surfactant having a polyoxyethylene chain is added at the time of the polymerization,
the resin particles comprises a resin derived from a polymerizable monomer comprising at least one of a monofunctional styrene-based monomer and a monofunctional (meth)acrylic-based monomer, and
the resin particles exhibit a b* value in the range of from −1.0 to +2.0, as measured with a color and color-difference meter, when subjected to a heat treatment for 2 hours at 150° C. in a thermostatic chamber.

2. Resin particles comprising a resin derived from a polymerizable monomer comprising at least one of a monofunctional styrene-based monomer and a monofunctional (meth)acrylic-based monomer, wherein
the proportion by number of particles having a particle diameter in the range of from 80 to 120% of the volume-average particle diameter is 83% or more, and
the resin particles exhibit a b* value in the range of from −1.0 to +1.0, as measured with a color and color-difference meter, when subjected to a heat treatment for 2 hours at 150° C. in a thermostatic chamber.

3. The resin particles according to claim 2 , wherein a magnesium content is 10 ppm or less.

4. The resin particles according to claim 2 , wherein the polymerizable monomer further comprises at least one of a multifunctional styrene-based monomer and a multifunctional (meth)acrylic-based monomer.

5. The resin particles according to claim 4 , wherein the multifunctional (meth)acrylic-based monomer is in a range of from 5 to 30% by weight of the polymerizable monomer.

6. The resin particles according to claim 2 , wherein the polymerizable monomer comprises a monofunctional (meth)acrylic-based monomer wherein the monofunctional (meth)acrylic-based monomer is an alkyl (meth)acrylate, and wherein the number of carbons of the alkyl is from 2 to 12.

7. The resin particles according to claim 2 , produced by a seed polymerization method.

8. An anti-glare film obtained by coating a coating composition comprising the resin particles according to claim 2 onto a transparent base film.

9. An external preparation comprising the resin particles according to claim 2 .

10. A coating composition comprising the resin particles according to claim 2 .

11. A light-diffusing resin composition comprising the resin particles according to claim 2 .

12. A light-diffusing resin molded article obtained by molding the light-diffusing resin composition according to claim 11 .

13. An external preparation comprising the resin particles according to claim 4 .

14. A coating composition comprising the resin particles according to claim 4 .

15. An anti-glare film obtained by coating the coating composition according to claim 14 onto a transparent base film.

16. A light-diffusing resin composition comprising the resin particles according to claim 4 .

17. A light-diffusing resin molded article obtained by molding the light-diffusing resin composition according to claim 16 .

18. A process for producing the resin particles according to claim 2 , the process comprising:
absorbing a polymerizable mixture comprising a polymerizable monomer comprising at least one of a monofunctional styrene-based monomer and a monofunctional (meth)acrylic-based monomer, and a polymerization initiator into seed particles in an aqueous medium, without using a dispersant, in the presence of an anionic surfactant not having a polyoxyethylene chain but having an alkyl group; and
polymerizing the polymerizable monomer in an aqueous medium, without using a dispersant, in the presence of an anionic surfactant having a polyoxyethylene chain to thereby obtain resin particles; wherein
the anionic surfactant having a polyoxyethylene chain is added at the time of the polymerization,
the proportion by number of the resin particles having a particle diameter in the range of from 80 to 120% of the volume-average particle diameter is 83% or more, and
the resin particles exhibit a b* value in the range of from −1.0 to +1.0, as measured with a color and color-difference meter, when subjected to a heat treatment for 2 hours at 150° C. in a thermostatic chamber.

19. The process for producing resin particles according to claim 1 , wherein
the anionic surfactant not having a polyoxyethylene chain but having an alkyl group is at least one compound selected from the group consisting of alkyl sulfosuccinates, alkyl sulfonates, and alkyl sulfoacetates, and
the anionic surfactant having a polyoxyethylene chain is at least one compound selected from the group consisting of polyoxyethylene aryl ether phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl ether sulfates, polyoxyethylene aryl ether sulfates, and polyoxyethylene alkyl sulfosuccinates.

20. The process for producing resin particles according to claim 1 , wherein
the anionic surfactant not having a polyoxyethylene chain but having an alkyl group is a dialkyl sulfo succinate, and
the anionic surfactant having a polyoxyethylene chain is at least one of a polyoxyethylene alkyl ether phosphate and a polyoxyethylene aryl ether sulfate.

21. The process for producing resin particles according to claim 1 , wherein
the polymerizable monomer comprises a monofunctional (meth)acrylic-based monomer, and
30 to 500 parts by weight of the polymerizable mixture based on 1 part by weight of seed articles is absorbed.

Assignees

• Nakamura Masaaki
• Harada Ryosuke
• Okamoto Koichiro
• Sekisui Plastics

Inventors

• Nakamura Masaaki
• Harada Ryosuke
• Okamoto Koichiro

Classifications

• C08F2/14 Primary

  Organic medium · CPC title

• G02B5/0242

  by means of dispersed particles · CPC title

• B32B5/16

  characterised by features of a layer formed of particles, e.g. chips, powder {or granules (layer formed of natural mineral particles B32B19/00; layer being formed of wood fibres, chips or particles B32B21/02)} · CPC title

• C08F2/26 Primary

  anionic · CPC title

• G02B1/04

  made of organic materials, e.g. plastics (G02B1/08 takes precedence) · CPC title