Bearing component and its manufacturing method

Patent metadata

Field	Value
Publication number	US-9878396-B2
Application number	US-201414783446-A
Country	US
Kind code	B2
Filing date	Apr 7, 2014
Priority date	Apr 9, 2013
Publication date	Jan 30, 2018
Grant date	Jan 30, 2018

Abstract

A bearing component and a method to form a bearing component. The bearing component comprises a first and a second metallic material wherein the first material presents a first carbon content and the second material presents a second carbon content, wherein the first material and the second material have been joined by a diffusion welding process. The diffusion welding process has resulted in a transition zone with a varying carbon content between the first material and the second material. The varying carbon content in the transition zone is essentially within an interval, wherein the interval end points are defined by the carbon content of the first material and the second material.

First claim

The invention claimed is:

1. A method to form a bearing component, comprising:
a first metallic material and a second metallic material, wherein the first metallic material presents a first carbon content and the second metallic material presents a second carbon content,
wherein the first metallic material and the second metallic material have been joined by a diffusion welding process, wherein the diffusion welding process has resulted in a transition zone with a varying carbon content between the first metallic material and the second metallic material, and
wherein the varying carbon content in the transition zone is essentially within an interval, and
wherein the interval end points are defined by the carbon contents of the first metallic material and the second metallic material, the forming method comprising steps of:
heating the first metallic material and the second metallic material and pressing them against each other under a specific pressure and for a period of time thereby allowing the materials to diffuse into each other at a joining temperature,
wherein the first material having a first carbon activity that increases linearly as the first carbon content increases due to the step of heating, the second material having a second carbon activity that is constant during the step of heating as the second carbon content increases, the first metallic material presents a first carbon activity essentially similar to a second carbon activity of the second metallic material at the joining temperature such that there are no carbon gradients in the first material and no carbon gradients in the second material.

2. The method to form the bearing component according to claim 1 , wherein the the carbon content changes at a depth of twenty millimeters from a surface of the bearing component.

3. The method to form the bearing component according to claim 1 , wherein carbon has not formed cementites or iron carbides that are larger relative to a surrounding structure in the bearing component.

4. The method to form the bearing component according to claim 1 , wherein the forming method is done by a hot isostatic pressing.

5. The method to form the bearing component according to claim 1 , wherein the temperature is 1000-1300 degrees C.

6. The method to form the bearing component according to claim 1 , wherein the temperature is 1100-1200 degrees C.

7. The method to form the bearing component according to claim 1 , wherein the temperature is 1140-1160 degrees C.

8. The method to form the bearing component according to claim 1 , wherein the pressure is 80-310 MPa.

9. The method to form the bearing component according to claim 1 , wherein at least one of the first metallic material and the second metallic material is in powder form before heating.

10. The method to form the bearing component according to claim 1 , wherein the bearing component is subsequently cut into at least two pieces creating at least two bearing components.

11. The method to form the bearing component according to claim 1 , wherein the bearing component is one of:
an inner ring of a bearing, or
an outer ring of a bearing, or
a roller of a roller bearing.

12. The method to form the bearing component according to claim 1 , wherein the temperature is 1150 degrees C.

Assignees

• Strandell Ingemar
• Skf Ab

Inventors

• Strandell Ingemar

Classifications

• B23K2203/04

  Operations & Transport · mapped topic

• B23K20/227 Primary

  with ferrous layer · CPC title

• B23K20/02

  by means of a press {; Diffusion bonding} · CPC title

• F16C2226/36

  by welding · CPC title

• B23K20/023

  Thermo-compression bonding · CPC title