Ballistic resistant article and process to manufacture said article

Patent metadata

Field	Value
Publication number	US-9869534-B2
Application number	US-201414767371-A
Country	US
Kind code	B2
Filing date	Mar 21, 2014
Priority date	Mar 26, 2013
Publication date	Jan 16, 2018
Grant date	Jan 16, 2018

Abstract

A ballistic resistant article is provided along with a process to manufacture the article. The ballistic resistant articles includes at least one consolidated composite, wherein the at least one consolidated composite includes at least two layers, each layer includes a network of fibers, the fibers have a strength of at least 800 mN/tex (1100 MPa) according to ASTM D 7269-07, the fibers in each layer are impregnated with a matrix material, and each consolidated composite has a front surface and a rear surface. In the ballistic article, at least the front surface of each consolidated composite is powder coated with partly molten and solidified powder particles to form a powder coated surface.

First claim

The invention claimed is:

1. A ballistic resistant article comprising at least one consolidated composite, wherein
the at least one consolidated composite comprises at least two layers,
each layer comprises a network of fibers,
the fibers have a strength of at least 800 mN/tex (1100 MPa) according to ASTM D 7269-07,
the fibers in each layer are impregnated with a matrix material, and
each consolidated composite has a front surface and a rear surface,
wherein
at least the front surface of each consolidated composite is powder coated with partly molten and solidified powder particles to form a powder coated surface.

2. The ballistic resistant article according to claim 1 , wherein the article comprises 2 to 100 consolidated composites.

3. The ballistic resistant article according to claim 1 , wherein each consolidated composite comprises 2 to 10 layers.

4. The ballistic resistant article according to claim 1 , wherein the network of fibers comprised by each layer is a woven fabric or a non-woven fabric.

5. The ballistic resistant article according to claim 4 , wherein the non-woven fabric is a unidirectional aligned fiber layer.

6. The ballistic resistant article according to claim 1 , wherein the fibers are aramid fibers.

7. The ballistic resistant article according to claim 1 , wherein the matrix material comprises an organic polymer and the polymer is a styrene isoprene styrene block copolymer, a styrene butadiene random copolymer, a self-crosslinking acrylic polymer and/or a crosslinkable acrylic polymer or a polychloroprene polymer.

8. The ballistic resistant article according to claim 1 , wherein a matrix material content in each layer and in each consolidated composite ranges from 5 wt. -% to 30 wt. -% with respect to the weight of the fibers without moisture, and an areal density of each consolidated composite ranges from 50 g/m 2 to 500 g/m 2 .

9. The ballistic resistant article according to claim 1 , wherein the powder particles consist of a thermoplastic polymer, wherein the thermo-plastic polymer is a member selected from one of the groups consisting of low-density polyethylenes (LDPE), linear low-density polyethylenes (LLDPE), high-density polyethylenes (HDPE) and polyvinyl chlorides (PVC).

10. The ballistic resistant article according to claim 1 , wherein an areal density of the partly molten and solidified powder particles on a powder coated surface ranges from 0.1 g/m 2 to 50 g/m 2 .

11. Process to manufacture a ballistic resistant article according to claim 1 , wherein the process comprises the following steps:
a) manufacturing at least one consolidated composite which comprises at least two layers, each layer comprises a network of fibers, the fibers have a strength of at least 800 mN/tex (1100 MPa) according to ASTM D 7269-07, and the fibers in each layer have been impregnated with a matrix material,
b) powder coating at least one surface of the consolidated composite resulting from step a) with powder particles by
(1) distributing the powder particles on the surface,
(2) partly melting the distributed particles resulting from step b(1) on the surface, and
(3) solidifying the partly molten particles resulting from step b(2) on the surface, and, if two or more composites have been manufactured in steps a) and b),
c) stacking the two or more powder coated consolidated composites obtained in step b) and fixating the consolidated composites with one another by stitching them.

12. Process according to claim 11 , wherein the operations (1), (2) and (3) have to be performed in a manner that ensures that an island in the sea coating pattern is obtained on the powder coated surface.

13. The ballistic resistant article according to claim 1 , wherein the partly molten and solidified powder particles form an island in the sea coating pattern on the powder coated surface.

14. The ballistic resistant article according to claim 13 , wherein the islands in the island-in-the-sea coating pattern do not contact one another, and, if looked from above, exhibit a spherical and/or elliptical shape.

15. The ballistic resistant article according to claim 14 , wherein the spherical shaped islands have an arithmetically averaged diameter d s and the elliptical shaped island have an arithmetically averaged diameter d e obtained from arithmetically averaging the lengths of the long axes and of the short axes of the ellipses, so that the islands,
when looked from above, exhibit an average diameter d i =(d s +d e )/2, and d i ranges from 10 to 10000 μm, and
when looked from the side, exhibit an arithmetically averaged height h, and h ranges from 0.5 to 1000 μm.

16. The ballistic resistant article according to claim 13 , wherein the islands cover a fraction of the powder coated surface defined by a cover factor f c ={(A covered /(A uncovered +A covered )) }·100 [%], wherein A uncovered denotes the uncovered area of the powder coated surface and A covered denotes the covered area of the powder coated surface, and f c ranges from 1% to 95%.

Assignees

• Teijin Aramid Bv
• Barrday Inc

Inventors

• De Haas Marc-Jan
• Van Norel Alex
• Van Bommel Vincent
• Poulopoulos Nektarios
• Williams Alicia

Classifications

• B32B5/024

  Woven fabric · CPC title

• B32B5/022 Primary

  Non-woven fabric · CPC title

• B32B2260/046

  Synthetic resin · CPC title

• B32B2264/0257

  Polyolefin particles, e.g. polyethylene or polypropylene homopolymers or ethylene-propylene copolymers · CPC title

• B32B5/26

  another layer {next to it} also being fibrous or filamentary {(relative arrangement of fibres or filaments of different layers B32B5/12)} · CPC title