Manufacturing method of catalyst ink, manufacturing method of fuel cell, and fuel cell

Patent metadata

Field	Value
Publication number	US-9865885-B2
Application number	US-201214241238-A
Country	US
Kind code	B2
Filing date	May 14, 2012
Priority date	Aug 31, 2011
Publication date	Jan 9, 2018
Grant date	Jan 9, 2018

Abstract

A catalyst ink for improving the performance of catalyst electrodes in a fuel cell is produced by the following procedure. A catalyst dispersion is prepared by dispersing catalyst-supported particles as conductive particles with a catalyst supported thereon in a solvent. A gel material having viscoelasticity is prepared by mixing an ionomer with a volatile solvent. A catalyst ink having a desired viscosity is produced by stirring and mixing the catalyst dispersion with the gel material.

First claim

The invention claimed is:

1. A manufacturing method of a catalyst ink used for formation of a catalyst electrode, the manufacturing method comprising steps of:
(a) dispersing catalyst-supported particles as conductive particles with a catalyst supported thereon in a solvent to prepare a catalyst dispersion;
(b) mixing an ionomer with a volatile solvent to prepare a gel material; and
(c) stirring and mixing the catalyst dispersion with the gel material to produce a catalyst ink,
wherein a storage modulus G1 of the gel material prepared in the step (b) satisfies: about 150 Pa≦G1≦about 400 Pa at a strain amount of 1% under application of vibration having a frequency of 1 Hz.

2. The manufacturing method according to claim 1 , wherein
the step (a) comprises a step of adding a surface active agent to improve dispersibility of the catalyst-supported particles, and
the surface active agent is an ionomer that has a same structure as that of the ionomer used in the step (b) or has a different structure but has an equivalent ion conductivity and an equivalent EW value to the ionomer used in the step (b).

3. The manufacturing method according to claim 2 , wherein
a ratio Wp of weight of the ionomer added to the catalyst dispersion in the step (a) to weight of the ionomer contained in the catalyst ink produced in the step (c) satisfies about 5%≦Wp≦about 25%.

4. The manufacturing method according to claim 1 , wherein
the step (b) comprises a step of thickening the gel material by heating.

5. The manufacturing method according to claim 1 , wherein
the step (b) comprises a step of thickening the gel material by applying a shear force.

6. The manufacturing method according to claim 1 , wherein
the volatile solvent is an alcohol solution, and
the step (b) comprises a step of regulating concentration of an alcohol in the alcohol solution, so as to adjust viscoelasticity of the gel material.

7. The manufacturing method according claim 1 , wherein
a storage modulus G1 of the gel material prepared in the step (b) satisfies: about 125 Pa≦G1≦about 425 Pa at a strain amount of 1% under application of vibration having a frequency of 1 Hz.

8. The manufacturing method according to claim 1 , wherein
the step (c) comprises steps of:
supplying the catalyst dispersion and the gel material into a vessel; and
applying a force toward a side face direction of the vessel to a mixed fluid of the catalyst dispersion and the gel material by utilizing a centrifugal force generated by a rotor rotating in the vessel, and stirring the mixed fluid in a state that the mixed fluid adheres in a film-like state on the side face, so as to adjust viscosity of the catalyst ink.

9. The manufacturing method according to claim 1 , wherein
the step (c) includes multiple stirring operations to apply different shear forces to a mixture of the catalyst dispersion and the gel material.

10. The manufacturing method according to claim 9 , wherein
the multiple stirring operations include a first stirring operation to apply a low shear force and a second stirring operation performed subsequent to the first stirring operation to apply a high shear force, wherein
a storage modulus G2 of the mixture after the first stirring operation satisfies: about 0 Pa≦G2≦about 10 Pa at a strain amount of 1% under application of vibration having a frequency of 1 Hz.

11. The manufacturing method according to claim 10 , wherein
a storage modulus G1 of the gel material prepared in the step (b) satisfies: about 150 Pa≦G1≦about 300 Pa at a strain amount of 1% under application of vibration having a frequency of 1 Hz.

12. The manufacturing method according to claim 2 , wherein
the step (c) mixes the catalyst dispersion with the gel material, such that a ratio Wri of weight of the ionomer included in the gel material to weight of the ionomer included in the catalyst dispersion satisfies Wri≧about 9.

13. The manufacturing method according to claim 1 , wherein
a storage modulus Gi of the catalyst ink produced in the step (c) satisfies: about 5 Pa≦Gi≦about 30 Pa at a strain amount of 1% under application of vibration having a frequency of 1 Hz.

14. A manufacturing method of a fuel cell, comprising:
applying the catalyst ink produced by the manufacturing method according to claim 1 by die-coat method to form a catalyst electrode.

15. A fuel cell, comprising:
a catalyst electrode formed by using the catalyst ink produced by the manufacturing method according to claim 1 .

16. The manufacturing method according to claim 1 , wherein a storage modulus G1 of the gel material prepared in the step (b) satisfies: about 150 Pa≦G1≦about 300 Pa at a strain amount of 1% under application of vibration having a frequency of 1 Hz.

Assignees

• Hori Yoshihiro
• Endou Yoshito
• Ohashi Sozaburo
• Ishihara Noriaki
• Okumura Masao
• Toyota Motor Co Ltd

Inventors

• Hori Yoshihiro
• Endou Yoshito
• Ohashi Sozaburo
• Ishihara Noriaki
• Okumura Masao

Classifications

• H01M4/8668 Primary

  Binders · CPC title

• H01M4/925

  supported on carriers, e.g. powder carriers · CPC title

• H01M4/8828

  Coating with slurry or ink · CPC title

• H01M4/926 Primary

  on carbon or graphite · CPC title

• H01M2008/1095

  Fuel cells with polymeric electrolytes · CPC title