Thin strip component, method for manufacturing same, and motor using thin strip component
US-10862354-B2 · Dec 8, 2020 · US
US9863015B2 · US · B2
| Field | Value |
|---|---|
| Publication number | US-9863015-B2 |
| Application number | US-201314371053-A |
| Country | US |
| Kind code | B2 |
| Filing date | Feb 18, 2013 |
| Priority date | Mar 14, 2012 |
| Publication date | Jan 9, 2018 |
| Grant date | Jan 9, 2018 |
A practical reading order for non-experts. Skip the full description unless you need deep technical detail.
What the patent document calls the invention.
A short plain-language summary of the technical disclosure.
Who owns or filed the patent and who is credited as inventor.
Filing, priority, publication, and grant dates set the timeline.
The legal scope of protection — read this for what is actually claimed.
Technology tags used to group this patent with similar filings.
Prior art links and similar publications in this corpus.
Official abstract text for this publication.
A manufacturing method for strip casting 550 MPa-grade high strength atmospheric corrosion-resistant steel strip, comprising the following steps: 1) smelting, where the chemical composition of a molten steel is that: C is between 0.03-0.08%, Si≦0.4%, Mn is between 0.6-1.5%, P is between 0.07-0.22%, S≦0.01%, N≦0.012%, Cu is between 0.25-0.8%, Cr is between 0.3-0.8%, and Ni is between 0.12-0.4%, additionally, also comprised is at least one micro-alloying element among Nb, V, Ti, and Mo, where Nb is between 0.01-0.08%, V is between 0.01-0.08%, Ti is between 0.01-0.08%, and Mo is between 0.1-0.4%, and where the remainder is Fe and unavoidable impurities; 2) strip casting, where a 1-5 mm-thick cast strip is casted directly; 3) cooling the strip, where the cooling rate is greater than 20° C./s; 4) online hot rolling the cast strip, where the hot rolling temperature is between 1050-1250° C., where the reduction rate is between 20-50%, and where the deformation rate is >20 s −1 ; austenite online recrystallizing after hot rolling, where the thickness of the hot rolled strip is between 0.5-3.0 mm; and, 5) cooling and winding, where the cooling rate is between 10-80° C./s, and where the winding temperature is between 570-720° C. The microscopic structure of a steel strip acquired is primarily constituted by fine polygonal ferrite and pearlite.
Opening claim text (preview).
The invention claimed is: 1. A manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade, the method sequentially comprising the following steps: 1) smelting, wherein the molten steel has a chemical composition by weight percentage as follows: C 0.03˜0.08%, Si≦0.4%, Mn 0.6˜1.5%, P 0.07˜0.22%, 0<S≦0.01%, 0<N≦0.012%, Cu 0.25˜0.8%, Cr 0.3˜0.8% and Ni 0.12˜0.4%, and at least one microalloy element selected from Nb, V, Ti, and Mo having a content of Nb 0.01˜0.08%, V 0.01˜0.08%, Ti 0.01˜0.08% and Mo 0.1˜0.4%, and balance being Fe and inevitable impurities; 2) continuous strip casting, wherein the molten steel is introduced into a molten pool formed by a pair of relatively rotating and internally water-cooled casting rollers and side dams, and is directly cast into a cast strip having a thickness of 1˜5 mm through rapid solidification; 3) cooling the cast strip after the continuous strip casting, wherein after being continuously cast and coming out of the casting rollers, the cast strip goes through an airtight chamber for cooling, the cooling rate is 21° C./sec. to 38° C./sec.; 4) online hot rolling the cast strip after cooling the cast strip under a hot rolling temperature of 1,050˜1,250° C., a reduction rate of 20˜50%, and a deformation rate of >20 s −1 , wherein the thickness of the steel strip after hot rolling is 0.5˜3.0 mm, and online austenite recrystallization occurs upon the hot rolling of the cast strip; 5) cooling and coiling after the online hot rolling the cast strip, wherein the cooling rate of the hot-rolled strip is controlled to be 16° C./sec. to 74° C./sec., and the coiling temperature of the hot-rolled strip is controlled to be 570˜720° C.; and wherein the final resulting steel strip has a microstructure substantially consisting of fine polygonal ferrite and pearlite conferring a strength property and an elongation property to the steel strip. 2. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, in step 1), the content of each of Nb, V and Ti is 0.01˜0.05% by weight percentage, and the content of Mo is 0.1˜0.25% by weight percentage. 3. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, in step 4), the hot rolling temperature is in the range of 1,100˜1,250° C. 4. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, in step 4), the hot rolling temperature is in the range of 1,150˜1,250° C. 5. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 or claim 3 , wherein, in step 4), the reduction rate of the hot rolling is 30˜50%. 6. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 or claim 3 , wherein, in step 4), the deformation rate of hot rolling is >30 s −1 . 7. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 5 , wherein, in step 4), the deformation rate of hot rolling is 22 s −1 to 47 s −1 . 8. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, in step 5), the cooling rate is in the range of 18° C./sec to 62° C./sec. 9. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 or claim 8 , wherein, in step 5), the coiling temperature is in the range of 620˜720° C. 10. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, the thickness of said steel strip is less than 3 mm. 11. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, the thickness of said steel strip is less than 2 mm. 12. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 , wherein, the thickness of said steel strip is less than 1 mm. 13. The manufacturing method of a continuous strip cast atmospheric corrosion-resistant steel strip having a high-strength of 550 MPa-grade according to claim 1 or claim 10 , wherein, said steel strip has a yield strength of 550 MPa or above, a tensile strength of 650 MPa or above, and an elongation of 22% or above.
Rapid solidification; Thin strip casting · CPC title
Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment (hardening articles or materials formed by forging or rolling with no further heating beyond that required for the formation C21D1/02) · CPC title
with molybdenum or tungsten · CPC title
with niobium or tantalum · CPC title
Pearlite · CPC title