Method for electric resistance welded steel tube

Patent metadata

Field	Value
Publication number	US-9862014-B2
Application number	US-201213711942-A
Country	US
Kind code	B2
Filing date	Dec 12, 2012
Priority date	Feb 26, 2007
Publication date	Jan 9, 2018
Grant date	Jan 9, 2018

Abstract

A method for manufacturing an electric resistance welded steel tube including: forming a steel tube material into an almost cylindrical open pipe, the steel tube material being a steel sheet wherein Ti and N satisfy (N/14)<(Ti/47.9); forming an electric resistance welded steel tube by bonding ends of the open pipe to each other by induction resistance welding with heat input controlled so that the bond width is 30 to 65 μm; heating the electric resistance welded steel tube to a temperature equal to or higher than the Ac 3 transformation temperature; and diameter-reducing rolling the heated electric resistance welded steel tube with rolling reduction expressed by an outer diameter ratio greater than (1−25/the bond width before diameter-reducing rolling (μm))×100% such that the bond width is 25 μm or less.

First claim

What is claimed is:

1. A method for manufacturing an electric resistance welded steel tube for heat treatment, comprising:
forming a steel sheet into an almost cylindrical open pipe, the steel tube material being a steel sheet having a composition constituted by, in mass percent:

C: 0.15 to 0.40%
Si: 0.05 to 0.50%

Mn: 0.30 to 2.00%
Al: 0.01 to 0.10%

Ti: 0.001 to 0.04%
B: 0.0005 to 0.0050%, and

N: 0.0010 to 0.0100%

with Ti and N satisfying (N/14)<(Ti/47.9) as well as Fe and unavoidable impurities as the balance;
forming an electric resistance welded steel tube by bonding lengthwise ends of the open pipe to each other by electric resistance welding with heat input controlled so that the bond width will fall within the range of 30 to 65 μm;
heating the electric resistance welded steel tube to a temperature equal to or higher than the Ac 3 transformation temperature; and
diameter-reducing rolling the heated electric resistance welded steel tube with rolling reduction expressed by an outer diameter ratio being (1−25/the bond width before diameter-reducing rolling (μm))×100% or greater such that the bond width will be 25 μm or less.

2. The method according to claim 1 , wherein the composition further comprises one or more selected from, in mass percent, Cr: 1.0% or less, Mo: 1.0% or less, W: 1.0% or less, Ni: 1.0% or less, and Cu: 1.0% or less.

3. The method according to claim 2 , wherein the composition further contains either or both of, in mass percent, Nb: 0.2% or less and V: 0.2% or less.

4. The method according to claim 1 , wherein the composition further contains either or both of, in mass percent, Nb: 0.2% or less and V: 0.2% or less.

Assignees

• Jfe Steel Corp

Inventors

• Kawabata Yoshikazu
• Sakaguchi Masayuki
• Sakata Kei

Classifications

• C22C38/04

  containing manganese · CPC title

• B23K2201/06

  Operations & Transport · mapped topic

• C21D9/50

  for welded joints · CPC title

• Y10T428/1241

  Nonplanar uniform thickness or nonlinear uniform diameter [e.g., L-shape] · CPC title

• C22C38/001

  containing N · CPC title