Catalytic cracking catalyst, process for producing the same, and method of catalytic cracking of hydrocarbon oil

Patent metadata

Field	Value
Publication number	US-9861966-B2
Application number	US-29359707-A
Country	US
Kind code	B2
Filing date	Mar 2, 2007
Priority date	Mar 22, 2006
Publication date	Jan 9, 2018
Grant date	Jan 9, 2018

Abstract

A catalytic cracking catalyst is provided which has high cracking activity and with which the production of FCC gasoline having a high octane number can efficiently proceed without lowering a gasoline yield. Also provided are a process for producing the catalyst and a method of the catalytic cracking of a hydrocarbon oil with the catalyst.
The catalyst for catalytic cracking of a hydrocarbon oil comprises a crystalline aluminosilicate, a binder, and a clay mineral in a certain proportion, wherein the content of sodium and potassium therein is 0.5% by mass or lower in terms of oxide (Na 2 O and K 2 O) amount, the content of at least one rare earth metal therein is 3.0% by mass or lower in terms of oxide (RE 2 O 3 , wherein RE is a rare earth element) amount, the [RE 2 O 3 +Na 2 O+K 2 O]/[crystalline aluminosilicate] ratio by mass is 0.1 or lower, and the catalyst has a xenon adsorption amount, as measured at an adsorption temperature of 25° C. and a partial xenon pressure of 650 torr, of 2.20×10 20 molecules or more per g of the catalyst. Also provided are a process for producing the catalyst and a method of catalytic cracking of a hydrocarbon oil with the catalyst.

First claim

The invention claimed is:

1. A catalyst for catalytic cracking of a hydrocarbon oil, which consists of 20-50 mass % of a crystalline aluminosilicate, 5-40 mass % of a binder, and 10-75 mass % of a clay mineral, wherein the content of sodium and potassium therein is 0.5% by mass or lower in terms of oxide (Na 2 O and K 2 O) amount, the content of at least one rare earth metal therein is 3.0% by mass or lower in terms of oxide (RE 2 O 3 , wherein RE is a rare earth element) amount, the [RE 2 O 3 +Na 2 O+K 2 O]/[crystalline aluminosilicate] mass ratio is 0.1 or lower, and the catalyst has a xenon adsorption amount, as measured at an adsorption temperature of 25° C. and a partial xenon pressure of 650 torr, of 2.20×10 20 molecules or more per g of the catalyst.

2. A process for producing the catalyst for catalytic cracking of a hydrocarbon oil according to claim 1 , characterized by spray-drying an aqueous slurry containing a crystalline aluminosilicate, a binder, and a clay mineral and then washing the resultant particles by ion exchange to remove sodium and potassium so that the content of sodium and potassium becomes 0.5% by mass or lower in terms of oxide (Na 2 O and K 2 O) amount.

3. A method of catalytic cracking of a hydrocarbon oil, characterized by catalytically cracking a hydrocarbon oil using the catalyst for catalytic cracking of a hydrocarbon oil according to claim 1 .

Assignees

• Watanabe Katsuya
• Cosmo Oil Co Ltd
• Petroleum Energy Center Found

Inventors

• Watanabe Katsuya

Classifications

• B01J35/70

  characterised by their crystalline properties, e.g. semi-crystalline (catalysts comprising carbon B01J21/18; molecular sieves B01J29/00) · CPC title

• B01J35/38

  Abrasion or attrition resistance · CPC title

• C10G2400/02

  Gasoline · CPC title

• C10G11/05

  Crystalline alumino-silicates, e.g. molecular sieves · CPC title

• B01J35/002

  Operations & Transport · mapped topic