Water-repellant transparent coating-substrate assembly and process for producing the same

Patent metadata

Field	Value
Publication number	US-9856407-B2
Application number	US-201314758354-A
Country	US
Kind code	B2
Filing date	Dec 24, 2013
Priority date	Dec 27, 2012
Publication date	Jan 2, 2018
Grant date	Jan 2, 2018

Abstract

A water-repellent transparent coating-substrate assembly includes a substrate and a water-repellent transparent coating disposed on a surface of the substrate, the transparent coating including an inorganic oxide fine particle layer containing inorganic oxide fine particles, and an overcoating layer disposed on the inorganic oxide fine particle layer, the surface of the water-repellent transparent coating having irregularities including depressions and protrusions in which the protrusions have an average height (T F ) in the range of 30 to 500 nm and an average protrusion interval (pitch width) (W F ) in the range of 50 to 1000 nm, the water-repellent transparent coating having a water contact angle in the range of 130 to 180°.

First claim

The invention claimed is:

1. A water-repellent transparent coating-substrate assembly comprising:
a substrate; and
the water-repellent transparent coating disposed on a surface of the substrate and having depressions and protrusions on a surface thereof,
wherein an average height of the protrusions (T F ) is 30 to 500 nm and an average interval (pitch width) of the protrusions (W F ) is 50 to 1000 nm,
wherein the protrusions have finer depressions and finer protrusions on a surface thereof,
wherein an average interval of the finer protrusions (W FF ) is smaller than the average interval of the protrusions (W F ),
wherein an average height of the finer protrusions (T FF ) is 3 to 50 nm and an average interval of the finer protrusions (W FF ) is 3 to 50 nm,
wherein the water-repellent transparent coating includes an inorganic oxide fine particle layer and an overcoating layer disposed on the inorganic oxide fine particle layer, and
wherein the water-repellent transparent coating has a water contact angle of 130 to 180°.

2. The water-repellent transparent coating-substrate assembly according to claim 1 , wherein a ratio of (T F )/(W F ) is 0.1 to 10.

3. The water-repellent transparent coating-substrate assembly according to claim 1 , wherein the inorganic oxide fine particle layer contains inorganic oxide fine particles and a binder.

4. The water-repellent transparent coating-substrate assembly according to claim 3 , wherein the content of the binder in terms of oxide is 1 to 200 parts by weight when the content of said inorganic oxide fine particles in terms of oxide is 100 parts by weight.

5. The water-repellent transparent coating-substrate assembly according to claim 1 , further comprising a primer layer between the substrate and the inorganic oxide fine particle layer.

6. The water-repellent transparent coating-substrate assembly according to claim 1 , wherein the inorganic oxide fine particles have one or more kinds of shapes selected from plate shapes, fiber shapes, chain shapes, warty shapes, cluster shapes and sunflower shapes.

7. The water-repellent transparent coating-substrate assembly according to claim 6 , wherein
the plate-shaped inorganic oxide fine particles have an average particle diameter (D P ) of 10 to 300 nm, an average thickness (T P ) of 1 to 60 nm, and a ratio of the average particle diameter (D P ) to the average thickness (T P ) , (D P ) /(T P ) , of 1.5to 50,
the fiber-shaped inorganic oxide fine particles have an average length (L F ) of 10 to 500 nm, an average particle width (W FS ) of 1 to 100 nm, and a ratio of the average length (L F ) to the average particle width (W FS ), (L F )/(W FS ), of 1.5 to 50,
the chain-shaped inorganic oxide fine particles are chains each composed of 2 to 100 primary fine particles having an average particle diameter (D C ) of 3 to 50 nm, and have an average length (L C ) of 6 to 500 nm, and a ratio of the average length (L C ) to the average particle diameter (D C ), (L C )/(D C ), of 2 to 50,
the warty particles are inorganic oxide particles having wart-like projections on the surface of the inorganic oxide particles, and have an average particle diameter (D A ) measured by an image analysis method of 10 to 150 nm,
the cluster-shaped particles are aggregated particles (secondary particles) composed of inorganic oxide primary particles having an average particle diameter (D B1 ) of 10 to 150 nm, the secondary particles having an average particle diameter (D B2 ) of 20 to 500 nm, and
the sunflower-shaped particles are inorganic oxide particles that include inorganic oxide base particles (A) and inorganic oxide top fine particles (B) covering the surface of the base particles, the inorganic oxide base particles (A) being spherical particles with an average particle diameter (D A ) of 40 to 600 nm, the inorganic oxide top fine particles (B) having an average particle diameter (D B ) of 4 to 60 nm.

8. The water-repellent transparent coating-substrate assembly according to claim 6 , wherein the plate-shaped inorganic oxide fine particles are plate-shaped alumina fine particles or plate-shaped alumina-silica fine particles.

9. The water-repellent transparent coating-substrate assembly according to claim 6 , wherein the fiber-shaped inorganic oxide fine particles are fiber-shaped alumina fine particles or fiber-shaped alumina-silica fine particles.

10. The water-repellent transparent coating-substrate assembly according to claim 6 , wherein the chain-shaped inorganic oxide fine particles are chain-shaped silica fine particles.

11. The water-repellent transparent coating-substrate assembly according to claim 7 , wherein
the warty particles and the cluster-shaped particles are each at least one selected from SiO 2 , ZrO 2 , CeO 2 , WO 3 , TiO 2 , and composite oxides and mixtures of these oxides, and
the sunflower-shaped particles are at least one selected from SiO 2 , Al 2 O 3 , Sb 2 O 5 , ZrO 2 , TiO 2 , Fe 2 O 3 , CeO 2 , and composite oxides or mixtures of these oxides (wherein the inorganic oxide base particles (A) and the inorganic oxide top fine particles (B) of the sunflower-shaped particles may be the same as each other).

12. The water-repellent transparent coating-substrate assembly according to claim 11 , wherein the warty particles, the cluster-shaped particles and the sunflower-shaped particles are each silica.

13. The water-repellent transparent coating-substrate assembly according to claim 5 , wherein the primer layer includes a silica.

14. The water-repellent transparent coating-substrate assembly according to claim 1 , wherein the inorganic oxide fine particles are surface-treated with a hydrolyzable organosilicon compound represented by Formula (1) below:
SiX 4   (1)

(in the formula, X is an alkoxy group having 1 to 4 carbon atoms, a hydroxyl group, a halogen or hydrogen).

15. The water-repellent transparent coating-substrate assembly according to claim 3 , wherein the binder is a silica and is a hydrolyzate polycondensate of a hydrolyzable organo silicon compound represented by Formula (2) below:
R n —SiX 4 −n   (2)

(in the formula, R is a non-substituted or substituted hydrocarbon group having 1 to 10 carbon atoms; X is an alkoxy group having 1 to 4 carbon atoms, a hydroxyl group, a halogen or hydrogen; and n is an integer of 0 to 1).

16. The water-repellent transparent coating-substrate assembly according to claim 1 , wherein the content of the overcoating layer in terms of oxide (solid) is 1 to 100 parts by weight when the content of said inorganic oxide fine particles in terms of oxide is 100 parts by weight.

17. The water-repellent transparent coating-substrate assembly according to claim 1 , wherein the overcoating layer is a fluorine-containing silica layer and the fluorine-containing silica layer includes a hydrolyzate polycondensate of a hydrolyzable organosilicon compound represented by Formula (3) below:
R n —SiX 4−n   (3)

(in the formula, R is a fluorine-substituted hydrocarbon group having 1 to 10 carbon atoms, and may be the same or different; X is an alkoxy group having 1 to 4 carbon atoms, a hydroxyl group, a halogen or hydrogen; and n is an integer of 1 to 3).

18. The water-repellent transparent coating-substrate assembly according to claim 17 , wherein the fluorine-containing silica layer further includes a hydrolyzate polycondensate of a hydrolyzable organosilicon compound represented by Formula (4) below:
SiX 4   (4)

(in the formula, X is an alkoxy group having 1 to 4 carbon atoms, a hydroxyl group, a halogen or hydrogen).

Assignees

• Jgc Catalysts & Chemicals Ltd

Inventors

• Hakoshima Yuhko
• Matsuda Masayuki
• Muraguchi Ryo
• Egami Kazutaka
• Koyanagi Tsuguo
• Kumazawa Mitsuaki
• Yoshida Satoshi
• Tawarasako Yuji

Classifications

• B32B2307/412

  Transparent · CPC title

• B32B9/00 Primary

  Layered products comprising a {layer of a} particular substance not covered by groups B32B11/00 - B32B29/00 · CPC title

• C03C17/3411

  with at least two coatings of inorganic materials (C03C17/36, C03C17/42 take precedence) · CPC title

• B32B2307/73

  Hydrophobic · CPC title

• C09K3/18 Primary

  for application to surfaces to minimize adherence of ice, mist or water thereto (rendering particulate materials free flowing, in general, e.g. making them hydrophobic B01J2/30); Thawing or antifreeze materials for application to surfaces (used in liquids for heat-transfer, heat-exchange or heat-storage or for the production of heat or cold other than by combustion, e.g. radiator liquids, C09K5/00) · CPC title