Cable with semiconductive layer made of polypropylene composition and improved long term thermal stability

Patent metadata

Field	Value
Publication number	US-9852826-B2
Application number	US-201113702425-A
Country	US
Kind code	B2
Filing date	May 31, 2011
Priority date	Jun 10, 2010
Publication date	Dec 26, 2017
Grant date	Dec 26, 2017

Abstract

Described herein is a cable that includes a conductor surrounded by at least one semiconductive layer, wherein the layer comprises a polymer composition comprising a polypropylene homopolymer or a polypropylene copolymer with one or more comonomers, a polyolefin functionalized with an anhydride of a mono- or polycarboxylic acid, wherein said anhydride of a mono- or polycarboxylic acid can be linear or cyclic, wherein the functionalized polyolefin is different from the polypropylene homopolymer or polypropylene copolymer or the second polymer, and wherein the amount of the functionalized polyolefin is up to 10 wt % based on the total amount of the polymer composition, a solid conductive filler and a LDPE homopolymer or a LDPE copolymer of ethylene with one or more comonomers having a melting temperature (Tm) less than the Tm of the polypropylene homopolymer or polypropylene copolymer. Also described herein is a process for producing the polymer composition.

First claim

The invention claimed is:

1. A cable comprising a conductor surrounded by at least one layer, wherein the layer comprises a polymer composition comprising
a) a polypropylene homopolymer or a polypropylene copolymer with one or more comonomers,
b) a polyolefin functionalized with an anhydride of a mono- or polycarboxylic acid, wherein said anhydride of a mono- or polycarboxylic acid can be linear or cyclic, wherein the functionalized polyolefin (b) is different from the polypropylene homopolymer or polypropylene copolymer (a) or the second polymer (d), and wherein the amount of the functionalized polyolefin is up to 10 wt % based on the total amount (100%) of the polymer composition,
c) a solid conductive filler and,
d) a LDPE homopolymer or a LDPE copolymer of ethylene with one or more comonomers having a melting temperature (Tm) less than the Tm of the polypropylene homopolymer or polypropylene copolymer (a).

2. The cable according to claim 1 , wherein the cable is
a cable comprising a conductor surrounded by at least a semiconductive layer comprising the polymer composition, or
a cable comprising a conductor surrounded by at least an inner semiconductive layer, an insulation layer and an outer semiconductive layer, in that order, wherein at least the inner semiconductive layer or the outer semiconductive layer comprises the polymer composition.

3. The cable according to claim 1 , wherein polymer composition comprises the polypropylene homopolymer or copolymer (a) in an amount of from 40 to 99.5 wt % based on the combined weight (100 wt %) of the polypropylene homopolymer or copolymer (a), the functionalized polyolefin (b) and the second polymer (d) present in the polymer composition.

4. The cable according to claim 1 , wherein the polymer composition comprises the second polymer (d) in an amount of from 0 to 65 wt % based on the combined weight (100 wt %) of the polypropylene homopolymer or copolymer (a), the functionalized polyolefin (b) and the second polymer (d) present in the polymer composition.

5. The cable according to claim 1 , wherein the polymer composition comprises the solid conductive filler (c) in an amount of up to 50 wt % on the total amount (100 wt %) of the polymer composition.

6. The cable according to claim 1 , wherein the polymer composition has an MFR (230° C., 5.0 kg) from 0.01 to 30.0 g/10 min.

7. The cable according to claim 1 , wherein the solid conductive filler (c) is carbon black.

8. The cable according to claim 1 , wherein the polymer composition present in one or more layers is non-crosslinked after producing the cable.

9. A process for producing the cable according to claim 1 , which comprises the steps of
(a) providing and mixing the polymer composition of claim 1 ,
(b) applying a meltmix of the polymer composition obtained from step (a) on a conductor to form at least one layer of the cable.

10. The process of claim 9 for producing a power cable comprising a conductor surrounded by an inner semiconductive layer, an insulation layer, and an outer semiconductive layer, in that order, wherein the process comprises the steps of
(a)
providing and mixing a first semiconductive composition comprising a polymer, a conductive filler and further component(s) for the inner semiconductive layer,
providing and mixing a polymer composition for the insulation layer,
providing and mixing a second semiconductive composition comprising a polymer, a conductive filler and further component(s) for the outer semiconductive layer,

(b)
applying on a conductor,
a meltmix of the first semiconductive composition obtained from step (a) to form the inner semiconductive layer,
a meltmix of polymer composition obtained from step (a) to form the insulation layer, and
a meltmix of the second semiconductive composition obtained from step (a) to form the outer semiconductive layer, wherein at least one of the first semiconductive composition or the second semiconductive composition comprises the polymer composition of claim 1 .

11. The cable according to claim 1 , wherein the anhydride is maleic anhydride.

12. The cable according to claim 1 , wherein the polyolefin in component (b) is polypropylene or polyethylene.

13. The cable according to claim 1 , wherein the polyolefin in component (b) is a homopolymer of propylene, random copolymer of propylene, or a heterophasic copolymer of propylene.

14. The cable according to claim 1 , wherein the functionalized polyolefin (b) comprises a polypropylene grafted with maleic anhydride.

15. The cable according to claim 1 , wherein the polypropylene homopolymer or copolymer (a) comprises a heterophasic propylene copolymer composition comprising a polypropylene homopolymer or random copolymer matrix (1) and dispersed therein a second propylene copolymer (2).

16. The cable according to claim 1 , wherein the polymer composition comprises the functionalized polyolefin (b) in an amount of from 0.1 to 4.0 wt % based on the total amount (100 wt %) of the polymer composition.

Assignees

• Steffl Thomas
• Svanberg Christer
• Borealis Ag

Inventors

• Steffl Thomas
• Svanberg Christer

Classifications

• H01B7/17

  Protection against damage caused by external factors, e.g. sheaths or armouring · CPC title

• C08L23/14

  Copolymers of propene (C08L23/16 takes precedence) · CPC title

• H01B1/24

  the conductive material comprising carbon-silicon compounds, carbon or silicon · CPC title

• C08K3/04

  Carbon · CPC title

• C08L23/0815

  with aliphatic 1-olefins containing one carbon-to-carbon double bond · CPC title