Thickening polymer

Patent metadata

Field	Value
Publication number	US-9850454-B2
Application number	US-201214126021-A
Country	US
Kind code	B2
Filing date	Jun 15, 2012
Priority date	Jun 27, 2011
Publication date	Dec 26, 2017
Grant date	Dec 26, 2017

Abstract

Polymer obtainable by radical emulsion polymerization of (A) at least one acidic vinyl monomer or salt thereof; (B) at least one nonionic vinyl monomer, particularly preferably a hydrophobic nonionic vinyl monomer; (C) at least one monomer containing an unsaturated end group and a polyoxyalkylene part; (D) at least one crosslinking monomer; and (E) optionally, a protective colloid, characterized in that the polymerization is controlled such that (F) the gel effect occurs, at least at times, achieved by adding monomers of type (A), (B), and (C) (dosing time) during 120 minutes; and such that (G) the crosslinking monomer (D) is added, at the very earliest, 10 minutes after the first addition of the monomers (A), (B), and (C).

First claim

What is claimed is:

1. A polymer, wherein the polymer is obtainable by radical emulsion polymerization of
(A) at least one acidic vinyl monomer or salt thereof,
(B) at least one nonionic vinyl monomer,
(C) at least one monomer containing an unsaturated end group and a polyoxyalkylene moiety,
(D) at least one crosslinking monomer,
(E) optionally, a protective colloid,

the polymerization being controlled such that
(F) at least at times the gel effect occurs, achieved by adding monomers (A), (B) and (C) within 120 minutes, and
(G) the crosslinking monomer (D) is added at the earliest 10 minutes after a first addition of monomers (A), (B) and (C).

2. The polymer of claim 1 , wherein (B) comprises a hydrophobic nonionic vinyl monomer.

3. The polymer of claim 1 , wherein no associative monomers are present.

4. The polymer of claim 1 , wherein (A) comprises at least one of methacrylic acid, an alkali metal salt thereof, an alkaline earth metal salt thereof, an ammonium salt thereof, and an alkylammonium salt thereof.

5. The polymer of claim 1 , wherein (B) comprises at least one monomer selected from C1-C22-alkyl acrylates and C1-C22-alkyl methacrylates.

6. The polymer of claim 1 , wherein (C) comprises at least one monomer selected from vinylpolyalkylene glycols and polymerizable surfactants.

7. The polymer of claim 1 , wherein (C) comprises at least one monomer selected from ethoxylated and propoxylated 1,4-butanediol vinyl ether having 30 ethyleneoxy and propyleneoxy units, allylpolyethylene glycol ethers having 30 ethyleneoxy units, allylpolyethylene glycol ethers having 20 ethyleneoxy units, vinylpolyethylene glycol ethers having 20 ethyleneoxy units, CH 2 ═CHCH 2 O[(CH 2 CH 2 O) n (CH 2 (CH 3 )CHO)] m CH 3 where m+n=5 to 100 and n/m=1, and polyalkylene glycol allyl butyl ethers having 25 ethyleneoxy and 8 propyleneoxy units.

8. The polymer of claim 1 , wherein (D) comprises at least one monomer selected from polyol (meth)acrylates having at least two (meth)acrylate groups and mixed esters of polyols with acrylic acid and/or methacrylic acid.

9. The polymer of claim 1 , wherein the polymer comprises from 10% to 75% of (A), from 10% to 90% of (B), from 0.5% to 40% of (C), and up to 1% of (D).

10. The polymer of claim 1 , wherein the polymer comprises from 20% to 60% of (A), from 40% to 80% of (B), from 1% to 10% of (C), and from 0.05% to 0.5% of (D).

11. The polymer of claim 1 , wherein a mass ratio (A):(B) is from 1:2.2 to 1.5:1.

12. A polymer, wherein the polymer is obtainable by radical emulsion polymerization of
(A) at least one acidic vinyl monomer or salt thereof,
(B) at least one nonionic vinyl monomer,
(C) at least one monomer containing an unsaturated end group and a polyoxyalkylene moiety,
(D) at least one crosslinking monomer,
(E) optionally, a protective colloid,

the polymerization being controlled such that
(F) at least at times the gel effect occurs, achieved by adding monomers (A), (B) and (C) within 60 minutes and
(G) the crosslinking monomer (D) is added at the earliest 15 minutes after a first addition of monomers (A), (B) and (C),

and wherein (A) comprises at least one of methacrylic acid, an alkali metal salt thereof, an alkaline earth metal salt thereof, an ammonium salt thereof, and an alkylammonium salt thereof, (B) comprises at least one monomer selected from C1-C22-alkyl acrylates and C1-C22-alkyl methacrylates, (C) comprises at least one monomer selected from ethoxylated and propoxylated 1,4-butanediol vinyl ether having 30 ethyleneoxy and propyleneoxy units, allylpolyethylene glycol ethers having 30 ethyleneoxy units, allylpolyethylene glycol ethers having 20 ethyleneoxy units, vinylpolyethylene glycol ethers having 20 ethyleneoxy units, CH 2 ═CHCH 2 O[(CH 2 CH 2 O) n (CH 2 (CH 3 )CHO)] m CH 3 where m+n=5 to 100 and n/m=1, and polyalkylene glycol allyl butyl ethers having 25 ethyleneoxy and 8 propyleneoxy units, and (D) comprises at least one monomer selected from polyol (meth)acrylates having at least two (meth)acrylate groups and mixed esters of polyols with acrylic acid and/or methacrylic acid.

13. The polymer of claim 12 , wherein the polymer comprises from 28% to 52% of (A), from 40% to 62% of (B), from 2% to 6% of (C), and from 0.1% to 0.3% of (D).

14. A thickened preparation, wherein the preparation comprises the polymer of claim 1 .

15. The preparation of claim 14 , wherein the preparation is aqueous and comprises from 0.5% to 5% of the polymer.

16. The preparation of claim 1 , wherein (A) consists of methacrylic acid, (B) consists of ethylacrylate and (C) consists of allylpolyalkylene glycol ether having 20 ethyleneoxy units and 20 propyleneoxy units.

17. The preparation of claim 16 , wherein D consists of trimethylolpropane triacrylate.

18. The polymer of claim 17 , wherein the polymer comprises from 28% to 52% of (A), from 40% to 62% of (B), from 2% to 6% of (C), and from 0.1% to 0.3% of (D).

19. The preparation of claim 1 , wherein monomers (A), (B) and (C) are added within 60 minutes.

20. The preparation of claim 1 , wherein monomer (D) is added at the earliest 15 minutes after the first addition of monomers (A), (B) and (C).

Assignees

• Mertens Sascha
• Beiersdorf Ag

Inventors

• Mertens Sascha

Classifications

• A61K2800/262

  Transparent; Translucent · CPC title

• A61K2800/548

  Associative polymers · CPC title

• C08F220/26

  Esters containing oxygen in addition to the carboxy oxygen · CPC title

• C08F2/26

  anionic · CPC title

• A61Q19/10

  Washing or bathing preparations · CPC title