Water expandable polymer beads containing latex particles

Patent metadata

Field	Value
Publication number	US-9850361-B2
Application number	US-201515531925-A
Country	US
Kind code	B2
Filing date	Nov 30, 2015
Priority date	Dec 2, 2014
Publication date	Dec 26, 2017
Grant date	Dec 26, 2017

Abstract

An emulsifier-free process for the preparation of water expandable polymer beads, including: a) providing an emulsifier-free starting composition comprising styrene, b) prepolymerizing the starting composition to obtain a prepolymer composition, c) mixing an aqueous blowing agent with the prepolymer composition at an elevated temperature to obtain an inverse emulsion of water droplets in the prepolymer composition, wherein the aqueous blowing agent comprises water and a water soluble initiator dissolved in the water and the water droplets comprise spheres of a styrene polymer, wherein the water soluble initiator partly decomposes due to the elevated temperature leading to the formation of the inverse emulsion of water droplets in the prepolymer composition, d) suspending the inverse emulsion in an aqueous medium to yield an aqueous suspension of suspended droplets and e) polymerizing monomers in the droplets of the suspension obtained by step d) to obtain the water expandable polymer beads.

First claim

The invention claimed is:

1. An emulsifier-free process for the preparation of water expandable polymer beads, which process comprises the steps of:
a) providing an emulsifier-free starting composition comprising styrene,
b) prepolymerizing the starting composition to obtain a prepolymer composition,
c) mixing an aqueous blowing agent with the prepolymer composition at an elevated temperature to obtain an inverse emulsion of water droplets in the prepolymer composition, wherein the aqueous blowing agent comprises water and a water soluble initiator dissolved in the water and the water droplets comprise spheres of a styrene polymer, wherein the water soluble initiator partly decomposes due to the elevated temperature leading to the formation of the inverse emulsion of water droplets in the prepolymer composition,
d) suspending the inverse emulsion in an aqueous medium to yield an aqueous suspension of suspended droplets and
e) polymerizing monomers in the droplets of the suspension obtained by step d) to obtain the water expandable polymer beads.

2. The process of claim 1 , wherein the water soluble initiator is a persulfate.

3. The process of claim 2 , wherein the water soluble initiator is selected from the group consisting of sodium Na 2 SO 5 , KHSO 5 , K 2 S 2 O 8 , Na 2 S 2 O 8 and (NH 4 ) 2 S 2 O 8 .

4. The process of claim 1 , wherein the aqueous blowing agent further comprises a modifier-free nanoclay dispersed in the water.

5. The process according to claim 4 , wherein the modifier-free nanoclay is an unmodified sodium montmorillonite nanoclay.

6. The process according to claim 4 , wherein the amount of the nanoclay is 0.1-10 wt % of the total weight of the monomers in the starting composition.

7. The process of claim 1 , wherein the aqueous blowing agent further comprises a water soluble polar comonomer containing a carbon-to-carbon double bond.

8. The process of claim 7 , wherein the water soluble polar comonomer is selected from the group consisting of (meth)acrylic acid, styrene sulfonate, vinyl benzene boronic acid and salts thereof.

9. The process claim 1 , wherein the starting composition further comprises a polyphenylene ether resin.

10. The process according to claim 1 , wherein step b) comprises heating the starting composition at a temperature of 85-91° C. for a period of 30-120 minutes.

11. The process according to claim 1 , wherein step c) comprises stirring the mixture at a temperature of 85-95° C.

12. The process according to claim 1 , wherein step e) comprises heating the suspension obtained by step d) at a temperature of 90-135° C. for a period of 180-300 minutes.

13. Water expandable polymer beads obtained by the process according to claim 1 .

14. Expanded polymer beads obtained by expanding the water expandable polymer beads according to claim 13 .

15. The process according to claim 4 , wherein:
the amount of the nanoclay is 0.1-5 wt % of the total weight of the monomers in the starting composition,
step b) comprises heating the starting composition for a period of 70-90 minutes, and
step e) comprises heating the suspension obtained by step d) for a period of from 200-280 minutes.

16. The process according to claim 1 , wherein:
the water soluble initiator is a persulfate, and
the aqueous blowing agent further comprises a modifier-free nanoclay dispersed in the water, and a water soluble polar comonomer containing a carbon-to-carbon double bond.

17. The process according to claim 1 , wherein:
the starting composition further comprises a polyphenylene ether resin,
the nanoclay is an unmodified sodium montmorillonite nanoclay,
the amount of the nanoclay is 0.1-10 wt % of of the total weight of the monomers in the starting composition.

18. The process according to claim 17 , wherein
the water soluble initiator is selected from the group consisting of sodium Na 2 SO 5 , KHSO 5 , K 2 S 2 O 8 , Na 2 S 2 O 8 and (NH 4 ) 2 S 2 O 8 , and
the water soluble polar comonomer is selected from the group consisting of (meth)acrylic acid, styrene sulfonate, vinyl benzene boronic acid and salts thereof.

19. Water expandable polymer beads obtained by the process according to claim 16 .

20. Expanded polymer beads obtained by expanding the water expandable polymer beads according to claim 19 .

Assignees

• Sabic Global Technologies Bv

Inventors

• Ghurmallah Ghamdi
• Sciarone Timotheus Johannes Jacobus
• Leblanc Thierry
• Bus Tom

Classifications

• C08J2313/02

  Latex · CPC title

• C08J2319/02

  Latex · CPC title

• C08J9/0071

  Nanosized fillers, i.e. having at least one dimension below 100 nanometers · CPC title

• C08J2325/06

  Polystyrene · CPC title

• C08J9/20 Primary

  by suspension polymerisation in the presence of the blowing agent · CPC title