Abstract

A colored cementitious composition is provided that is composed of hydraulic cement and a liquid coloring suspension. The liquid coloring suspension for cementitious compositions contains polycarboxylate dispersant, pigment, and a polysaccharide thixotropic additive. The liquid coloring suspension has improved viscosity consistency, improved shelf-life, anti-settling and anti-sludging properties, and decreased polycarboxylate dispersant requirements.

First claim

We claim:

1. A liquid coloring suspension for cementitious compositions comprising:
a) liquid;
b) polycarboxylate dispersant;
c) pigment; and,
d) at least one microbially derived polysaccharide thixotropic additive selected from diutan gum, welan gum or combinations thereof; wherein the viscosity of the liquid coloring suspension is stable over time.

2. The liquid coloring suspension of claim 1 , wherein the polysaccharide is diutan gum.

3. The liquid coloring suspension of claim 1 , wherein the amount of polycarboxylate dispersant solids are from about 0.5% to about 3%, pigment solids are from about 50% to about 75%, and the polysaccharide thixotropic additive is from about 0.025% to about 1%, based on the total weight of the liquid coloring suspension.

4. The liquid coloring suspension of claim 1 , wherein the amount of polycarboxylate dispersant solids are from about 1% to about 2.5%, pigment solids are from about 53% to about 70%, and thixotropic additive is from about 0.1% to about 0.7%, based on the total weight of the liquid coloring suspension.

5. The liquid coloring suspension of claim 1 , wherein the liquid comprises water.

6. The liquid coloring suspension of claim 1 , wherein the pigment comprises an inorganic pigment.

7. The liquid coloring suspension of claim 6 , wherein the inorganic pigment comprises carbon black or a metal containing pigment that comprises at least one of iron oxide, chromium oxide, aluminum oxide, lead chromate, titanium oxide, zinc white, zinc oxide, zinc sulfide, lead white, iron manganese black, cobalt green, manganese blue, manganese violet, cadmium sulfoselenide, chromium orange, nickel titanium yellow, chromium titanium yellow, cadmium sulfide, zinc yellow, cobalt blue, ultramarine blue, or mixtures thereof.

8. The liquid coloring suspension of a claim 1 , wherein the pigment comprises an organic pigment.

9. The liquid coloring suspension of claim 8 wherein the organic pigment comprises phthalocyanine.

10. The liquid coloring suspension of claim 1 , further comprising at least one of additional dispersant, water reducer, fungicidal admixture, insecticidal admixture, or germicidal admixture.

11. A colored cementitious composition comprising hydraulic cement to which a liquid coloring suspension has been added, the liquid coloring suspension comprising:
a) liquid;
b) polycarboxylate dispersant;
c) pigment; and,
d) at least one microbially derived polysaccharide thixotropic additive selected from diutan gum, welan gum or combinations thereof; wherein the liquid coloring suspension improves the color in the cementitious composition without increasing the water demand.

12. The liquid coloring suspension of claim 11 , wherein the polysaccharide is diutan gum.

13. The colored cementitious composition of claim 11 , wherein the liquid comprises water.

14. The colored cementitious composition of claim 11 , wherein the pigment comprises an inorganic pigment.

15. The colored cementitious composition of claim 14 wherein the inorganic pigment comprises carbon black or a metal containing pigment that comprises at least one of iron oxide, chromium oxide, aluminum oxide, lead chromate, titanium oxide, zinc white, zinc oxide, zinc sulfide, lead white, iron manganese black, cobalt green, manganese blue, manganese violet, cadmium sulfoselenide, chromium orange, nickel titanium yellow, chromium titanium yellow, cadmium sulfide, zinc yellow, cobalt blue, ultramarine blue, or mixtures thereof.

16. The colored cementitious composition of claim 11 , wherein the pigment comprises an organic pigment.

17. The colored cementitious composition of claim 16 wherein the organic pigment comprises phthalocyanine.

18. The colored cementitious composition of claim 11 , wherein the amount of polycarboxylate dispersant solids are from about 0.0008% to about 0.51%, pigment solids are from about 0.1% to about 10%, and thixotropic additive is from about 0.00008% to about 0.17%, by total dry weight of cementitious binder.

19. The colored cementitious composition of claim 11 , wherein the amount of polycarboxylate dispersant solids are from about 0.004% to about 0.25%, pigment solids are from about 0.25% to about 6%, and thixotropic additive is from about 0.0004% to about 0.07%, by total dry weight of cementitious binder.

20. The colored cementitious composition of claim 11 , having a water to cement ratio of about 0.25 to about 0.7.

21. The colored cementitious composition of claim 11 , wherein the cement comprises at least one of portland cement, modified portland cement, masonry cement, or mixtures thereof.

22. The colored cementitious composition of claim 11 , further comprising a cement admixture or additive, other than the liquid coloring suspension, that comprises at least one of air entrainer, set accelerator, set retarder, air detraining agent, foaming agent, corrosion inhibitor, shrinkage reducing admixture, crack reducing admixture, additional dispersant, water reducer, fiber, pozzolan, strength enhancing agents, rheology modifying agent, water repellent, wetting agent, water soluble polymer, dampproofing admixture, gas former, permeability reducer, pumping aid, fungicidal admixture, germicidal admixture, insecticidal admixture, aggregate, alkali-reaction reducer, bonding admixture, polymeric microspheres, or mixtures thereof.

23. The colored cementitious composition of claim 22 , wherein the aggregate comprises at least one of silica, quartz, crushed marble, glass spheres, granite, limestone, calcite, feldspar, alluvial sands, or sand.

24. The colored cementitious composition of claim 22 , wherein the pozzolan comprises at least one of natural pozzolan, metakaolin, fly ash, silica fume, calcined clay, or blast furnace slag.

Assignees

• Construction Research & Technology Gmbh

Inventors

• Smith James Curtis
• Hevener Eric

Classifications

• C04B40/0039

  Premixtures of ingredients · CPC title

• C04B2103/54

  Pigments; Dyes · CPC title

• C04B2111/82

  Coloured materials · CPC title

• C04B14/308

  Iron oxide · CPC title

• C04B28/04 Primary

  Portland cements · CPC title