Brazing concept

Patent metadata

Field	Value
Publication number	US-9849534-B2
Application number	US-201314387061-A
Country	US
Kind code	B2
Filing date	Mar 27, 2013
Priority date	Mar 28, 2012
Publication date	Dec 26, 2017
Grant date	Dec 26, 2017

Abstract

The present invention relates to a blend of at least one boron source and at least one silicon source, wherein the blend comprises boron and silicon in a weight ratio boron to silicon within a range from about 5:100 to about 2:1, wherein silicon and boron are present in the blend in at least 25 wt %, and wherein the at least one boron source and the at least one silicon source are oxygen free except for inevitable amounts of contaminating oxygen, and wherein the blend is a mechanical blend of powders, and wherein particles in the powders have an average particle size less than 250 μm. The present invention relates further to a composition comprising the blend a substrate applied with the blend, a method for providing a brazed product, and uses.

First claim

The invention claimed is:

1. A mechanical mixture of two or more components comprising at least one boron source and at least one silicon source, wherein the components have an average particle size less than 250 μm, and each component is either (i) of a silicon source selected from the group consisting of at least one of elemental silicon, ferro silicon, iron silicides, silicon carbides, and silicon borides or (ii) of a boron source selected from the group consisting of at least one of elemental boron, boron carbides, nickel borides, and silicon borides,
wherein the mechanical mixture comprises boron and silicon in a weight ratio boron to silicon within a range from about 5:100 to about 1:1,
wherein silicon and boron are together present in the mechanical mixture in at least 25 wt %, and
wherein the at least one boron source and the at least one silicon source are oxygen free except for inevitable amounts of contaminating oxygen, and wherein the inevitable amount of contaminating oxygen is less than 10 wt %.

2. A composition comprising the mixture according to claim 1 .

3. The composition according to claim 2 , wherein the composition further comprises powders of a parent material, wherein the parent material is present in an amount less than 75 wt % calculated on the total weight of silicon, boron and parent material.

4. The composition according to claim 2 , wherein the composition further comprises powders of a braze alloy.

5. The composition according to claim 2 , wherein the composition further comprises at least one binder selected from solvents, water, oils, gels, lacquers, varnish, polymers, wax or combinations thereof.

6. The composition according to claim 5 , wherein the mixture is dispersed in the at least one binder.

7. The composition according to claim 5 , wherein the at least one binder is selected from polyesters, polyethylenes, polypropylenes, acrylic polymers, (meth)acrylic polymers, polyvinyl alcohols, polyvinyl acetates, polystyrenes, waxes, or combinations thereof.

8. The composition according to claim 2 , wherein the composition is a paint, or the composition is a paste, or the composition is a dispersion.

9. A brazed product obtained by a method for providing a product having at least one brazed joint between contact areas between substrates, said method comprising the steps of:
applying the composition of claim 2 on at least one substrate;
assembling the at least one substrate with at least one additional substrate, such that the at least one silicon source and the at least one boron source are present between contact areas of the at least one substrate and the at least one additional substrate;
heating the assembled substrates to a brazing temperature below 1250° C., in a furnace in vacuum, in an inert gas, in a reducing atmosphere, or combinations thereof; and
cooling the assembled substrates to obtain the product having at least one brazed joint between contact areas of the at least one substrate and the at least one additional substrate.

10. A product comprising a substrate of a parent material and the composition according to claim 2 , said parent material having a solidus temperature above 1100° C.,
wherein at least a part of the surface of the substrate of the parent material has a coated layer of the composition.

11. The product according to claim 10 , wherein the average total amount of silicon and boron in the coated layer is less than 1 mg/mm 2 .

12. The product according to claim 10 , wherein the parent material is selected from the group consisting of iron based alloys, nickel based alloys, chromium based alloys, cobalt based alloys, and copper based alloys having a melting point of at least 1100° C.

13. The product according to claim 10 , wherein the parent material comprises from about 15 to about 22 wt % chromium, from about 8 to about 22 wt % nickel, from about 0 to about 3 wt % manganese, from about 0 to about 1.5 wt % silicon, from about 0 to about 8 wt % molybdenum, and balanced with iron.

14. The product according to claim 10 , wherein the parent material comprises at least 80 wt % Ni.

15. The product according to claim 10 , wherein the parent material comprises more than 50 wt % Fe, less than 13 wt % Cr, less than 1 wt % Mo, less than 1 wt % Ni and less than 3 wt % Mn.

16. The product according to claim 10 , wherein the parent material comprises more than 10 wt % Cr and more than 60 wt % Ni.

17. The product according to claim 10 , wherein the parent material comprises more than 15 wt % Cr, more than 10 wt % Mo, and more than 50 wt % Ni.

18. The product according to claim 10 , wherein the parent material comprises more than 10 wt % Fe, 0.1 to 30 wt % Mo, 0.1 to 30 wt % Ni, and more than 50 wt % Co.

19. The product according to claim 10 , wherein the substrate is selected from the group consisting of coils, plates, parts, and sheets.

20. The product according to claim 10 , wherein a braze alloy layered product is obtained by heating said coated layer of the composition and the substrate, and thereby the composition is alloying with elements of the substrate, and wherein the obtained braze alloy layer has a melting point lower than the melting point of the parent material.

21. The mixture according to claim 1 , wherein silicon and boron are together present in the mechanical mixture in at least 35 wt %.

22. A method for providing a product having at least one brazed joint between contact areas between substrates, said method comprising the steps of:
applying the composition of claim 2 on at least one substrate;
assembling the at least one substrate with at least one additional substrate, such that the at least one silicon source and the at least one boron source are present between contact areas of the at least one substrate and the at least one additional substrate;
heating the assembled substrates to a brazing temperature below 1250° C., in a furnace in vacuum, in an inert gas, in a reducing atmosphere, or combinations thereof; and
cooling the assembled substrates to obtain the product having at least one brazed joint between contact areas of the at least one substrate and the at least one additional substrate.

23. The method according to claim 22 , wherein silicon and boron are present in the mixture within the range 25 wt % to 100 wt %, and the mixture is a mechanical mixture of powders.

24. The method according to claim 22 , wherein the at least one silicon source and at the least one boron source is the same source.

25. The method according to claim 22 , wherein the applying step comprises applying the at least one boron source and at least one silicon source on at least a part of one surface on at least one substrate, the at least one boron source being selected from elemental boron, boron carbides, nickel borides, and silicon borides, and the at least one silicon source being selected from elemental silicon, ferro silicon, iron silicides, silicon carbides, and silicon borides.

26. The method according to claim 22 , wherein the heating step comprises heating the assembled substrates, obtaining a molten braze alloy on the substrate(s) and letting the molten braze alloy be transferred by capillary forces to the contact areas between the substrates.

27. The method according to claim 22 , wherein the heating step comprises heating the product to a temperature of at least 900° C.

28. The method according

Assignees

• Alfa Laval Corp Ab

Inventors

• Sjödin Per
• Walter Kristian

Classifications

• B22F1/10

  Metallic powder containing lubricating or binding agents; Metallic powder containing organic material · CPC title

• B23K35/004

  at least one of the workpieces being of a metal of the iron group · CPC title

• B23K35/36

  Selection of non-metallic compositions, e.g. coatings or fluxes (B23K35/34 takes precedence); Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest · CPC title

• B23K35/362

  Selection of compositions of fluxes (B23K35/365, B23K35/368 take precedence) · CPC title

• B23K35/30 Primary

  with the principal constituent melting at less than 1550°C · CPC title