Method of preparing heat-resistant resin, heat-resistant resin and heat-resistant ABS resin composition

Patent metadata

Field	Value
Publication number	US-9845370-B2
Application number	US-201515022550-A
Country	US
Kind code	B2
Filing date	Oct 6, 2015
Priority date	Oct 7, 2014
Publication date	Dec 19, 2017
Grant date	Dec 19, 2017

Abstract

The present invention relates to a method of preparing a heat-resistant resin, a heat-resistant resin, and a heat-resistant ABS resin. According to the preparation method of the present invention, the heat-resistant resin can be prepared at a high polymerization conversion rate within a shortened polymerization time, and the amount of polymerized coagulum and the content of fine particles upon coagulation are decreased. Accordingly, a heat-resistant resin and a heat-resistant ABS resin composition with enhanced heat deflection temperature and processability are provided.

First claim

The invention claimed is:

1. A method of preparing a resin, the method comprising:
polymerizing a vinylcyan compound-based first part comprising 70 to 80 parts by weight of a first monomer and 30 to 20 parts by weight of a vinylcyan compound monomer and having a glass transition temperature of 140° C. or more, a number average particle diameter of 300 to 700 Å, and a weight-average molecular weight of 200,000 to 300,000 g/mol; and
polymerizing a vinylcyan compound-based second part, the second part enveloping the first part comprising the first monomer and the vinylcyan compound monomer,
wherein the resin comprises 30 to 80 parts by weight of the first part and 70 to 20 parts by weight of the second part, and has a glass transition temperature of 135 to 145° C. and a weight-average molecular weight of 100,000 to 150,000 g/mol.

2. The method according to claim 1 , wherein a total time taken for the polymerizing of the vinylcyan compound-based first part and the polymerizing of the vinylcyan compound-based second part is four hours or less, and a polymerization conversion rate of each of the polymerizing of the vinylcyan compound-based first part and the polymerizing of the vinylcyan compound-based second part is 98.5% or more.

3. The method according to claim 1 , wherein, in the 20 to 30 parts by weight of the vinylcyan compound monomer of the polymerizing of the first part, at least one selected from a (meth)acrylic acid alkyl ester monomer and an aromatic vinyl compound monomer (except for α-methylstyrene) is comprised in an amount of 2 to 5 parts by weight.

4. The method according to claim 1 , wherein the polymerizing of the vinylcyan compound-based first part comprises:
emulsion-polymerizing by feeding 70 to 80 parts by weight of the first monomer batchwise, 8 to 10 parts by weight of the vinylcyan compound monomer, and 0 to 2 parts by weight of at least one selected from a (meth)acrylic acid alkyl ester monomer and an aromatic vinyl compound monomer (except for α-methylstyrene), in a presence of a C 12 to C 18 saturated hydrocarbon-based emulsifier;
emulsion-polymerizing by continuously feeding 5 to 15 parts by weight of the vinylcyan compound monomer in a presence of the C 12 to C 18 saturated hydrocarbon-based emulsifier when a polymerization conversion rate is 83 to 88%; and
polymerizing by feeding 2 to 8 parts by weight of the vinylcyan compound monomer batchwise when a polymerization conversion rate is 92 to 96%.

5. The method according to claim 4 , wherein the emulsifier of the emulsion-polymerizing by feeding 70 to 80 parts by weight of the first monomer is comprised in an amount of 1.4 to 2.9 parts by weight based on 100 parts by weight of a total of the monomers of the polymerizing of the vinylcyan compound-based first part, and the emulsifier of the emulsion-polymerizing by continuously feeding 5 to 15 parts by weight of the vinylcyan compound monomer is comprised such that a total amount of this emulsifier and the emulsifier of the emulsion-polymerizing by feeding 70 to 80 parts by weight of the first monomer is 2.1 to 4.0 parts by weight.

6. The method according to claim 1 , wherein, in the polymerizing of the vinylcyan compound-based second part, the first monomer is comprised in an amount of 5 to 60 parts by weight, based on 100 parts by weight of the first part and a total of the monomers.

7. The method according to claim 1 , wherein, in the polymerizing of the vinylcyan compound-based second part, the vinylcyan compound monomer is comprised in an amount of 5 to 20 parts by weight based on 100 parts by weight of the first part and a total of the monomers.

8. The method according to claim 7 , wherein, in 5 to 20 parts by weight of the vinylcyan compound monomer, at least one selected from a (meth)acrylic acid alkyl ester monomer and an aromatic vinyl compound monomer (except for α-methylstyrene) is comprised in an amount of 1 to 5 parts by weight.

9. The method according to claim 1 , wherein the polymerizing of the second part comprises:
emulsion-polymerizing by feeding 30 to 80 parts by weight of the first part, 7 to 45 parts by weight of the first monomer, 3 to 10 parts by weight of the vinylcyan compound monomer, and 0 to 2 parts by weight of at least one selected from a (meth)acrylic acid alkyl ester and an aromatic vinyl compound (except for α-methylstyrene) to a mixture that comprises an emulsifier mixture comprising a C 12 to C 18 saturated hydrocarbon-based emulsifier and a monomer-type or polymer-type emulsifier with an unsaturated double bond, and a molecular weight controller mixture comprising a mercaptan-based C 6 to C 12 molecular weight controller and a dimer-based molecular weight controller;
emulsion-polymerizing by continuously feeding 3 to 10 parts by weight of the first monomer and 3 to 5 parts by weight of the vinylcyan compound monomer in a presence of a C 12 to C 18 saturated hydrocarbon-based emulsifier when a polymerization conversion rate is 83 to 88%; and
polymerizing by adding 1 to 5 parts by weight of the vinylcyan compound monomer batchwise when a polymerization conversion rate is 92 to 96%.

10. The method according to claim 9 , wherein, in the emulsion-polymerizing by feeding 30 to 80 parts by weight of the first part, the mercaptan-based C 6 to C 12 molecular weight controller and the dimer-based molecular weight controller are mixed in a ratio of 50:50 to 90:10 and comprised in an amount of 0.2 to 0.5 parts by weight based on 100 parts by weight of the first part and a total of the monomers.

11. The method according to claim 9 , wherein, in the emulsion-polymerizing by feeding 30 to 80 parts by weight of the first part, the C 12 to C 18 saturated hydrocarbon-based emulsifier and the low molecular weight emulsifier with an unsaturated double bond are mixed in a weight ratio of 50:50 to 90:10 and comprised in an amount of 0.5 to 1.0 parts by weight based on 100 parts by weight of the first part and a total of the monomers of the polymerizing of the vinylcyan compound-based second part.

12. The method according to claim 9 , wherein, in the emulsion polymerizing by continuously feeding 3 to 10 parts by weight of the first monomer, the C 12 to C 18 saturated hydrocarbon-based emulsifier is comprised in an amount of 0.2 to 0.5 parts by weight, based on 100 parts by weight of the first part and a total of the monomers of the polymerizing of the vinylcyan compound-based second part.

13. The method according to claim 1 , wherein, in the polymerizing of the vinylcyan compound-based second part, an amount of coagulum is 0.03% by weight or less.

14. A SAN resin, comprising:
a vinylcyan compound-based first part comprising 70 to 80 parts by weight of a first monomer and 30 to 20 parts by weight of a vinylcyan compound monomer and having a glass transition temperature of 140° C. or more, an average particle diameter of 300 to 700 Å, and a weight-average molecular weight of 200,000 to 300,000 g/mol; and
a second part enveloping the first part comprising the monomer and the vinylcyan compound monomer,
wherein the resin comprises 30 to 80 parts by weight of the first part and 70 to 20 parts by weight of the first part, and has a glass transition temperature of 135 to 145° C. and a weight-average molecular weight of 100,000 to 150,000 g/mol.

15. The SAN resin according to claim 14 , wherein the resin has a weight-average molecular weight of 100,000 to 150,000 g/mol and a glass transition temperature of 135 to 145° C.

16. An ABS resin composition, wherein the ABS resin composition comprises the SAN resin according to claim 14 and an ABS resin and has

Assignees

• Lg Chemical Ltd

Inventors

• Chai Joo Byung
• Park Eun Seon
• Jeon Tae Young
• Kim Young Min
• Kim Jong Beom
• Kim Chang Sull
• Jung Yu Sung

Classifications

• C08F265/08 Primary

  on to polymers of nitriles · CPC title

• C08F279/04

  Vinyl aromatic monomers and nitriles as the only monomers · CPC title

• C08F2/22

  Emulsion polymerisation · CPC title

• C08F2/38

  Polymerisation using regulators, e.g. chain terminating agents {, e.g. telomerisation} · CPC title

• C08F212/10 Primary

  with nitriles · CPC title