Multilayer resin material for dental milling and machining

Patent metadata

Field	Value
Publication number	US-9839498-B2
Application number	US-201615362867-A
Country	US
Kind code	B2
Filing date	Nov 29, 2016
Priority date	Nov 30, 2015
Publication date	Dec 12, 2017
Grant date	Dec 12, 2017

Abstract

To provide a multilayer resin material for dental milling and machining, comprising an inorganic filler in a content of 40% by weight or more and a plurality of layers different in transparency and color tone from each other, wherein the thickness of the uppermost layer (U) and the thickness of the lowermost layer (L) are each 1 mm or more, the contrast ratios (uppermost layer: C U , lowermost layer: C L ) as indices for the transparency of the uppermost layer (U) and the transparency of the lowermost layer (L) satisfy the following relations:

0.30≦C U ≦0.60

0.55≦C L ≦0.90

C U <C L

and the chromaticities (uppermost layer: L U ·a U ·b U , lowermost layer: L U ·a U ·b L ) based on the L*a*b* colorimetric system as the indices of the color tones in the uppermost layer (U) and the lowermost layer (L) satisfy the following relations:

60≦ L U ·L L ≦80

−3≦ a U ·a L ≦2

0≦ b U ·b L ≦30

First claim

What is claimed is:

1. A multilayer resin material for dental milling and machining, comprising an inorganic filler in a content of 40% by weight or more and a plurality of layers different in transparency and color tone from each other, wherein the thickness of the uppermost layer (U) and the thickness of the lowermost layer (L) are each 1 mm or more,
the contrast ratios (uppermost layer: C U , lowermost layer: C L ) as indices for the transparency of the uppermost layer (U) and the transparency of the lowermost layer (L) satisfy the following relations:
0.30≦C U ≦0.60

0.55≦C L ≦0.90

C U ≦C L

and the chromaticities (uppermost layer: L U ·a U ·b U , lowermost layer: L L ·a L ·b L ) based on the L*a*b* colorimetric system as the indices of the color tones in the uppermost layer (U) and the lowermost layer (L) satisfy the following relations:
60 ≦L U ·L L ≦80

−3 ≦a U ·a L ≦2

0 ≦b U ·b L ≦30.

2. The multilayer resin material for dental milling and machining according to claim 1 , wherein the volume ratio between the uppermost layer (U) and the lowermost layer (L) is 1:3 to 1:1.

3. The multilayer resin material for dental milling and machining according to claim 1 ,
wherein the thickness of a middle layer (M) positioned between the uppermost layer (U) and the lowermost layer (L) is 0.5 mm or more; and
the contrast ratio (C M ) as an index for the transparency in the middle layer (M) satisfies the following relations:
0.45≦C M ≦0.65

C U <C M <C L

and the chromaticity (middle layer: L M ·a M ·b M ) based on the L*a*b* colorimetric system as the index for the color tone in the middle layer (M) satisfies the following relations:
60≦L M ≦80

−3 a M ≦2

0≦b M ≦30.

4. The multilayer resin material for dental milling and machining according to 3 , wherein at least one of the volume ratio between the uppermost layer (U) and the middle layer (M), the volume ratio between the middle layer (M) and the lowermost layer (L) and the volume ratio between the uppermost layer (U) and the lowermost layer (L) is 1:3 to 1:1.

5. The multilayer resin material for dental milling and machining according to claim 3 , wherein the contrast ratio difference (|C U −C L |) between the uppermost layer (U) and the lowermost layer (L) is 0.03 to 0.15.

6. The multilayer resin material for dental milling and machining according to claim 3 , wherein the color difference ΔE UL between the uppermost layer (U) and the lowermost layer (L) is 0.1 to 15.0.

7. The multilayer resin material for dental milling and machining according to claim 3 , wherein the contrast ratio difference (|C U −C M |) between the uppermost layer (U) and the middle layer (M) is 0.03 to 0.15, and the contrast ratio difference (|C M −C L |) between the middle layer (M) and the lowermost layer (L) is 0.03 to 0.15.

8. The multilayer resin material for dental milling and machining according to claim 7 , wherein the color difference ΔE UL between the uppermost layer (U) and the lowermost layer (L) is 0.1 to 15.0.

9. The multilayer resin material for dental milling and machining according to claim 7 , wherein the color difference ΔE UM between the uppermost layer (U) and the middle layer (M) and the color difference ΔE ML between the middle layer (M) and the lowermost layer (L) are 0.1 to 15.0.

10. The multilayer resin material for dental milling and machining according to 4 , wherein at least one of the volume ratio between the uppermost layer (U) and the middle layer (M), the volume ratio between the middle layer (M) and the lowermost layer (L) and the volume ratio between the uppermost layer (U) and the lowermost layer (L) is 1:3 to 1:1.

11. The multilayer resin material for dental milling and machining according to claim 3 , wherein the color difference ΔE UM between the uppermost layer (U) and the middle layer (M) and the color difference ΔE ML between the middle layer (M) and the lowermost layer (L) are 0.1 to 15.0.

12. The multilayer resin material for dental milling and machining according to 11 , wherein at least one of the volume ratio between the uppermost layer (U) and the middle layer (M), the volume ratio between the middle layer (M) and the lowermost layer (L) and the volume ratio between the uppermost layer (U) and the lowermost layer (L) is 1:3 to 1:1.

13. The multilayer resin material for dental milling and machining according to claim 1 , wherein the contrast ratio difference (|C U −C L |) between the uppermost layer (U) and the lowermost layer (L) is 0.03 to 0.15.

14. The multilayer resin material for dental milling and machining according to claim 13 , wherein the color difference ΔE UL between the uppermost layer (U) and the lowermost layer (L) is 0.1 to 15.0.

15. The multilayer resin material for dental milling and machining according to claim 13 , wherein the volume ratio between the uppermost layer (U) and the lowermost layer (L) is 1:3 to 1:1.

16. The multilayer resin material for dental milling and machining according to claim 1 , wherein the color difference ΔE UL between the uppermost layer (U) and the lowermost layer (L) is 0.1 to 15.0.

17. The multilayer resin material for dental milling and machining according to claim 16 , wherein the volume ratio between the uppermost later (U) and the lowermost layer (L) is 1:3 to 1:1.

18. A method for producing the multilayer resin material for dental milling and machining according to claim 1 , produced by stacking uncured paste-like substances in layers and sequentially polymerizing and curing the stacked substances, wherein the difference or differences in the linear polymerization shrinkage rate between the respective layers are 1.0% or less, and/or the difference or differences in the heat generated by polymerization between the respective layers are 50 J/g or less.

Assignees

• Shofu Inc

Inventors

• Goto Masanori
• Kitamura Toshio
• Teramae Mitsuji

Classifications

• A61C5/77

  Methods or devices for making crowns · CPC title

• A61C13/082

  Cosmetic aspects, e.g. inlays; Determination of the colour (A61C19/10 takes precedence) · CPC title

• A61C5/30

  Securing inlays, onlays or crowns · CPC title

• C08F222/22 Primary

  Esters containing nitrogen · CPC title

• A61C13/09

  {Composite teeth, e.g. front and back section (A61C13/0835, A61C13/1023 take precedence)}; Multilayer teeth · CPC title