Silicon-containing particle, negative-electrode material for use in non-aqueous electrolyte secondary battery, and non-aqueous electrolyte secondary battery

Patent metadata

Field	Value
Publication number	US-9837658-B2
Application number	US-201715642901-A
Country	US
Kind code	B2
Filing date	Jul 6, 2017
Priority date	Mar 5, 2013
Publication date	Dec 5, 2017
Grant date	Dec 5, 2017

Abstract

The present invention is directed to a silicon-containing particle for use as a negative-electrode active material of a non-aqueous electrolyte secondary battery, wherein a crystal grain size is 300 nm or less, the crystal grain size being obtained by a Scherrer method from a full width at half maximum of a diffraction line attributable to Si (111) and near 2θ=28.4° in an x-ray diffraction pattern analysis, and a true density is more than 2.320 g/cm 3 and less than 3.500 g/cm 3 . The invention provides silicon-containing particles for use as a negative-electrode active material of a non-aqueous electrolyte secondary battery that enable manufacture of a non-aqueous electrolyte secondary battery having an excellent cycle characteristics and a higher capacity compared with graphite types.

First claim

The invention claimed is:

1. A method for manufacturing a silicon-containing particle for use as a negative-electrode active material of a non-aqueous electrolyte secondary battery, the method comprising:
depositing a silicon lump or a silicon alloy lump on a substrate by vacuum deposition; and
pulverizing the silicon lump or the silicon alloy lump to produce the silicon-containing particle,
wherein:
the silicon-containing particle has (i) a crystal grain size that is 300 nm or less, the crystal grain size being obtained by a Scherrer method from a full width at half maximum of a diffraction line attributable to Si (111) and near 2θ=28.4° in an x-ray diffraction pattern analysis, and (ii) a true density that is equal to or more than 2.3719 g/cm 3 and less than 3.500 g/cm 3 .

2. The method for manufacturing a silicon-containing particle according to claim 1 , wherein the silicon-containing particle has a volume median diameter D 50 of a particle size ranging from 1 μm to 20 μm.

3. The method for manufacturing a silicon-containing particle according to claim 2 , wherein the step of depositing includes depositing the silicon alloy lump by vacuum deposition, and the silicon alloy lump contains one or more elements selected from the group consisting of boron, aluminum, phosphorus, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, arsenic, germanium, tin, antimony, indium, tantalum, tungsten, and gallium.

4. A method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery, the method comprising forming the negative-electrode material from silicon-containing particles manufactured using the method according to claim 3 , the silicon-containing particles acting as a negative-electrode active material of the non-aqueous electrolyte secondary battery.

5. The method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery according to claim 4 , wherein the negative-electrode material is further formed from graphite, the graphite acting as a conductive agent.

6. A method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery, the method comprising forming the negative-electrode material from silicon-containing particles manufactured using the method according to claim 2 , the silicon-containing particles acting as a negative-electrode active material of the non-aqueous electrolyte secondary battery.

7. The method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery according to claim 6 , wherein the negative-electrode material is further formed from graphite, the graphite acting as a conductive agent.

8. The method for manufacturing silicon-containing particle according to claim 1 , wherein the silicon-containing particle has a quotient of a volume median diameter D 50 of a particle size divided by the crystal grain size ranging from 1 to 5000.

9. The method for manufacturing a silicon-containing particle according to claim 8 , wherein the step of depositing includes depositing the silicon alloy lump by vacuum deposition, and the silicon alloy lump contains one or more elements selected from the group consisting of boron, aluminum, phosphorus, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, arsenic, germanium, tin, antimony, indium, tantalum, tungsten, and gallium.

10. A method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery, the method comprising forming the negative-electrode material from silicon-containing particles manufactured using the method according to claim 9 , the silicon-containing particles acting as a negative-electrode active material of the non-aqueous electrolyte secondary battery.

11. The method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery according to claim 10 , wherein the negative-electrode material is further formed from graphite, the graphite acting as a conductive agent.

12. A method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery, the method comprising forming the negative-electrode material from silicon-containing particles manufactured using the method according to claim 8 , the silicon-containing particles acting as a negative-electrode active material of the non-aqueous electrolyte secondary battery.

13. The method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery according to claim 12 , wherein the negative-electrode material is further formed from graphite, the graphite acting as a conductive agent.

14. The method for manufacturing a silicon-containing particle according to claim 1 , wherein the step of depositing includes depositing the silicon alloy lump by vacuum deposition, and the silicon alloy lump contains one or more elements selected from the group consisting of boron, aluminum, phosphorus, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, arsenic, germanium, tin, antimony, indium, tantalum, tungsten, and gallium.

15. A method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery, the method comprising forming the negative-electrode material from silicon-containing particles manufactured using the method according to claim 14 , the silicon-containing particles acting as a negative-electrode active material of the non-aqueous electrolyte secondary battery.

16. The method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery according to claim 15 , wherein the negative-electrode material is further formed from graphite, the graphite acting as a conductive agent.

17. A method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery, the method comprising forming the negative-electrode material from silicon-containing particles manufactured using the method according to claim 1 , the silicon-containing particles acting as a negative-electrode active material of the non-aqueous electrolyte secondary battery.

18. The method for manufacturing a negative-electrode material for use in a non-aqueous electrolyte secondary battery according to claim 17 , wherein the negative-electrode material is further formed from graphite, the graphite acting as a conductive agent.

19. A method for manufacturing a non-aqueous electrolyte secondary battery, the method comprising:
forming a negative-electrode molded body from the negative-electrode material manufactured using the method according to claim 17 ;
providing a positive-electrode molded body;
providing a separator configured to separate the negative-electrode molded body from the positive-electrode molded body; and
providing a non-aqueous electrolyte.

20. The method for manufacturing a non-aqueous electrolyte secondary battery according to claim 19 , wherein a material containing lithium ions is used as the non-aqueous electrolyte.

Assignees

• Shinetsu Chemical Co

Inventors

• Nakanishi Tetsuo
• Taniguchi Kazuyuki
• Yamada Yoshiyasu

Classifications

• C22C19/03

  based on nickel · CPC title

• C22C9/00

  Alloys based on copper · CPC title

• H01M4/625

  Carbon or graphite · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M10/052

  Li-accumulators · CPC title