Enzymatic pretreatment of wood in a method for producing mechanical paper pulp

Patent metadata

Field	Value
Publication number	US-9834886-B2
Application number	US-201214347753-A
Country	US
Kind code	B2
Filing date	Sep 6, 2012
Priority date	Sep 30, 2011
Publication date	Dec 5, 2017
Grant date	Dec 5, 2017

Abstract

A method for producing mechanical paper pulp comprises: impregnating unprocessed wood, whereby unprocessed wood is exposed to an impregnating composition comprising at least a laccase enzyme and a formula mediator (I), wherein R 1 and R 2 are identical or different groups, chosen from among a hydrogen atom, a hydrocarbon chain, linear or branched, saturated or unsaturated, comprising 1 to 14 carbon atoms, wherein each hydrocarbon chain can be replaced by one or more functional groups chosen from among —OH, —SO 3 , benzyl, amino, mercapto, keto or carboxyl, wherein R 1 and R 2 in combination can form a cyclical structure, to achieve impregnation of the wood; and mechanically refining the impregnated wood, such that a mechanical paper pulp is obtained. The disclosure also relates to an impregnating composition used in this method and to the use thereof in a method for producing mechanical paper pulp, as well as to a method for producing paper.

First claim

The invention claimed is:

1. A method for producing mechanical paper pulp, comprising:
impregnating an untreated wood, comprising contacting the untreated wood with an impregnating composition comprising at least one laccase enzyme and a mediator of formula (I):

wherein R 1 and R 2 are identical or different C1 to C4 alkyl chains, to give an impregnated wood; and
mechanically refining the impregnated wood to obtain a mechanical paper pulp, wherein the mechanical paper pulp is a defibrator mechanical pulp (SGW), a pressure defibrator mechanical pulp (PGW), a refiner mechanical pulp (RMP), a thermomechanical pulp (TMP), a high-temperature thermomechanical pulp (HTMP), or a chemithermomechanical pulp (CTMP).

2. The method of claim 1 , wherein the mediator is diethyl hydroxylamine (DEHA).

3. The method of claim 1 , wherein the impregnating composition is produced using, and relative to its total weight:
0.01% to 10% by weight of a laccase solution containing 1000 LAMU/mL of said solution, and
0.1% to 10% by weight of mediator.

4. The method of claim 1 , wherein the impregnating composition is used at a rate of from 0.1 to 12 L/kg of the untreated wood for impregnation.

5. The method of claim 1 , wherein the untreated wood is selected from coniferous woods, deciduous woods and mixtures thereof.

6. The method of claim 1 , wherein the untreated wood is in the form of chips.

7. The method of claim 1 , wherein the contacting during the impregnating step is performed for a time of from 5 min to 240 min.

8. The method of claim 1 , wherein the impregnating step is performed at a temperature of from 35° C. to 80° C.

9. The method of claim 1 , wherein the impregnating step is performed at a pH of from 3 to 11.

10. The method of claim 1 , further comprising, before the impregnating step, steaming the untreated wood.

11. The method of claim 1 , further comprising, before the impregnating step, pressing the untreated wood.

12. The method of claim 1 , further comprising, at the end of the impregnating step, steaming the impregnated wood.

13. The method of claim 1 , further comprising, after the refining step, bleaching the mechanical paper pulp, comprising contacting the mechanical paper pulp with a bleaching composition.

14. The method of claim 13 , wherein the bleaching composition comprises a bleaching agent and at least one alkaline agent selected from: alkali metal and alkaline earth metal oxides, hydroxides, silicates, and carbonates, ammonia, aqueous ammonia, and mixtures thereof.

15. The method of claim 14 , wherein the bleaching step is carried out using:
from 0.5% to 10% by weight of bleaching agent, relative to the total weight of mechanical paper pulp;
from 0.5% to 10% by weight of alkaline agent, relative to the total weight of mechanical pulp.

16. The method of claim 1 , further comprising chelating the mechanical paper pulp by contacting the mechanical paper pulp with a chelating composition comprising a chelating agent.

17. The method of claim 1 , wherein the impregnating composition is used at a rate of from 1 to 10 L/kg of the untreated wood for impregnation.

18. The method of claim 5 , wherein the untreated wood is selected from a spruce wood, a poplar wood, a eucalyptus wood, and mixtures thereof.

19. The method of claim 1 , wherein the contacting during the impregnating step is performed for a time of from 25 min to 180 min.

20. The method of claim 1 , wherein the impregnating step is performed at a temperature of from 40° C. to 70° C.

21. The method of claim 1 , wherein the impregnating step is performed at a pH of from 4 to 7.

22. The method of claim 10 , wherein steaming the untreated wood comprising steaming for 5 min to 30 min.

23. The method of claim 10 , further comprising pressing the untreated wood after steaming the untreated wood and before the impregnating step.

24. The method of claim 12 , wherein steaming the impregnated wood comprising steaming the impregnated wood for 1 min to 10 min.

25. The method of claim 13 , wherein the bleaching composition comprising a bleaching agent and at least one alkaline agent selected from potassium hydroxide, sodium hydroxide, magnesium hydroxide, calcium hydroxide, sodium silicate, sodium carbonate, magnesium carbonate, and mixtures thereof.

26. The method of claim 14 , wherein the bleaching step is carried out using:
from 1% to 8% by weight of bleaching agent, relative to the total weight of mechanical paper pulp; and
from 1% to 6% by weight of alkaline agent, relative to the total weight of mechanical pulp.

27. The method of claim 13 , further comprising a chelating step between the refining step and the step of bleaching the mechanical paper pulp, comprising contacting the mechanical pulp with a chelating composition comprising a chelating agent selected from ethylene diamine tetraacetic acid, its sodium salts, diethylene triamine pentaacetic acid, and its sodium salts.

28. The method of claim 1 , wherein the mechanical paper pulp is a thermomechanical pulp (TMP), or a chemithermomechanical pulp (CTMP).

29. A method for producing a mechanical paper pulp, comprising:
optionally steaming an untreated wood,
optionally pressing the untreated wood,
at least one step of impregnating the untreated wood with an impregnating composition comprising at least one laccase enzyme and a mediator of formula (I):

wherein R 1 and R 2 are identical or different C 1 to C 4 alkyl chains, to give an impregnated wood,
to give an impregnated wood,
optionally an operation of steaming the impregnated wood,
at least one step of mechanically refining the impregnated wood, to give a mechanical paper pulp,
optionally chelating the mechanical paper pulp, and optionally bleaching the mechanical paper pulp.

30. A mechanical pulp and papermaking process comprising:
impregnating an untreated wood, comprising contacting the untreated wood,
with an impregnating composition comprising at least one laccase enzyme and a mediator of formula (I):

wherein R 1 and R 2 are identical or different C 1 to C 4 alkyl chains groups,
give an impregnated wood; and
mechanically refining the impregnated wood to obtain a mechanical paper pulp, wherein the mechanical paper pulp is a defibrator mechanical pulp (SGW), a pressure defibrator mechanical pulp (PGW), a refiner mechanical pulp (RMP), a thermomechanical pulp (TMP), a high-temperature thermomechanical pulp (HTMP), or a chemithermomechanical pulp (CTMP); manufacturing paper with the mechanical paper pulp.

Assignees

• Blanc Jérôme
• Calais Christophe
• Meyer Valérie
• Petit-Conil Michel
• Arkema France

Inventors

• Blanc Jérôme
• Calais Christophe
• Meyer Valérie
• Petit-Conil Michel

Classifications

• D21C9/163

  with peroxides · CPC title

• D21C5/005

  Treatment of cellulose-containing material with microorganisms or enzymes · CPC title

• D21C9/10

  Bleaching {; Apparatus therefor} · CPC title

• D21B1/02

  Pretreatment of the raw materials by chemical or physical means (removal of bark B27L) · CPC title

• D21B1/021 Primary

  by chemical means · CPC title