Heat-shrinkable multilayer film and heat shrinkable label

Patent metadata

Field	Value
Publication number	US-9827746-B2
Application number	US-201214241339-A
Country	US
Kind code	B2
Filing date	Sep 4, 2012
Priority date	Sep 5, 2011
Publication date	Nov 28, 2017
Grant date	Nov 28, 2017

Abstract

The present invention provides a heat shrinkable multilayer film that has excellent adhesiveness between front and back layers and an interlayer, effectively prevents delamination, and is less likely to have white creases on folds. The present invention also provides a heat shrinkable label formed from the heat shrinkable multilayer film. The present invention relates to a heat shrinkable multilayer film, including: front and back layers each containing a polyester resin; an interlayer containing a polystyrene resin; and adhesive layers, wherein the front and back layers and the interlayer are stacked with the adhesive layers interposed therebetween, and the adhesive layers each contain 50 to 95% by weight of a polystyrene resin and 5 to 50% by weight of a polyester elastomer.

First claim

The invention claimed is:

1. A heat shrinkable multilayer film, comprising:
front and back layers each comprising a polyester resin;
an interlayer comprising a polystyrene resin; and
adhesive layers,
wherein the front and back layers and the interlayer are stacked with the adhesive layers interposed therebetween,
each of the adhesive layers consists of from 55 to 85% by weight of a polystyrene resin and from 15 to 45% by weight of a polyester elastomer,
the polyester resin is obtained by polycondensation of a dicarboxylic acid component and a diol component,
the diol component comprises a component derived from 1, 4-cyclohexane dimethanol,
the polystyrene resin of the adhesive layer is different from the polystyrene resin of the interlayer,
the polystyrene resin of the interlayer is a styrene-butadiene copolymer having a styrene content of 78 to 90% by weight and a butadiene content of 10 to 22% by weight,
the polystyrene resin of the adhesive layer is a styrene-butadiene copolymer having a styrene content of 50 to 76% by weight and a butadiene content of 24 to 50% by weight, and
the polyester elastomer is a block copolymer consisting of a polyester and a polyalkylene ether glycol, the block copolymer comprising a polyalkylene ether glycol segment in an amount from 55 to 90% by weight, wherein the film does not form crease-whitening when the film is treated by being folded and pressed twice with a rubber roller at a load of 2 kg and a speed of 2 sec/100 mm in parallel to a machine direction of the film, and wherein the film has an adhesive strength in the machine direction of 100 to 200 g/cm, the adhesive strength being measured via separation at an angle of 180° and a tensile speed of 200 mm/min.

2. The heat shrinkable multilayer film according to claim 1 ,
wherein the polyester elastomer forming the adhesive layers has a melting point from 120° C. to 200° C.

3. The heat shrinkable multilayer film according to claim 1 ,
wherein the polyester elastomer forming the adhesive layers has a specific gravity from 0.95 to 1.20.

4. A heat shrinkable label formed of the heat shrinkable multilayer film according to claim 1 .

5. The heat shrinkable multilayer film according to claim 1 ,
wherein the polyester forming the block copolymer in the polyester elastomer is an aromatic polyester.

6. The heat shrinkable multilayer film according to claim 1 ,
wherein in the polyester elastomer, the polyester of the block copolymer forms a hard segment and the polyalkylene ether glycol of the block copolymer forms a soft segment.

7. The heat shrinkable multilayer film according to claim 1 , wherein
the polyester resin comprises a component derived from terephthalic acid as the dicarboxylic acid component, and
the adhesive layer has a thickness in a range from 0.3 μm to 3.0 μm.

Assignees

• Ishikawa Kiyoyasu
• Maruichi Naoyuki
• Gunze Kk

Inventors

• Ishikawa Kiyoyasu
• Maruichi Naoyuki

Classifications

• G09F2003/0255

  laminated · CPC title

• B32B2367/00

  Polyesters, e.g. PET, i.e. polyethylene terephthalate · CPC title

• B32B37/12

  characterised by using adhesives · CPC title

• B32B27/308

  comprising acrylic (co)polymers · CPC title

• B32B2307/736

  Shrinkable · CPC title