Abstract

A method for preparation of a dual phase filler for elastomers for manufacturing technical rubber items, including such for microwave protection. The method involves the following stages: first stage—1/10 of the silicasol impregnating solution obtained by its dilution in distilled water at a 1:10 ratio is pulverized over the carbon black at constant stirring; second stage—the carbon black pulverized with the silicasol impregnating solution is let stay in air at room temperature for 24 hours; third stage: a two-step thermal activation in a drying cabinet is carried out—at first at 80° C. for 2 hours, and then at 250° C. for 2 hours; fourth stage—9/10 of the impregnating solution that remained from the first stage is pulverized successively over the already impregnated carbon black at constant stirring. It again is let stay for 24 in air at room temperature; fifth stage: a three-step thermal activation in a drying cabinet is carried out—at first at 80° C. for 2 hours, then at 150° C. for 4 hours and finally at 250° C. for 4 hours. The dual phase filler includes SiO 2 in amounts 1 to 10% and carbon black 90 to 99%. It has the following parameters: specific surface area /BET/−20-50 m 2 /g, Iodine adsorption number—15-30 mg/g, Oil absorption number—50-90 ml/100 g, mesopore volume—0.05-0.20 cm 3 (STP)/g, mesopore diameter—10-20 nm. According to the invention the advantages ensured by the method are in the implementation of a multistage thermal activation at not very high temperature; in yielding improved texture of the dual phase filler obtained and in better insulation of the carbon black aggregates by the silica phase.

First claim

The invention claimed is:

1. A method for preparing an elastomer reinforcing dual phase filler based on carbon black with introduced silica, wherein the carbon black is pulverized with an impregnating silicasol solution according to a thin layer chromatography technique, said method comprising:
(1) pulverizing the silicasol over carbon black with constant stirring, wherein said impregnating solution is obtained by spraying carbon black with silicasol in a thin layer chromatography method with constant stirring, wherein the obtained impregnated carbon black is then diluted in distilled water at a 1:10 ratio;
(2) resting the carbon black pulverized with the silicasol impregnating solution obtained in (1) in air at room temperature for 24 hours;
(3) performing a two-step thermal activation in a drying cabinet, with a first step being performed at 80° C. for 2 hours, and then a second step being performed at 250° C. for 2 hours;
(4) successively pulverizing impregnating solution over the already impregnated carbon black with constant stirring;
(5) resting the carbon black pulverized with the silicasol impregnating solution obtained in (4) for 24 hours in air at room temperature; and
(6) performing a three-step thermal activation in a drying cabinet, with a first step being performed at 80° C. for 2 hours, a second step being performed at 150° C. for 4 hours and a third step being performed at 250° C. for 4 hours.

2. The method for preparation of a dual phase filler according to claim 1 , wherein an amount of silicasol needed for the carbon black impregnation is 1.0-20.0 ml/100 g carbon black.

3. The method for preparation of a dual phase filler according to claim 1 , wherein said silicasol comprises SiO 2 in an amount of 40% based upon the total amount of silicasol, wherein said silicasol has a pH of 9 and a density of 1.3 g/cm 3 .

Assignees

• Univ King Abdulaziz

Inventors

• Al-Ghamdi Ahmed A
• Al-Hartomy Omar A
• Al-Solamy Falleh R
• DISHOVSKY Nikolay Todorov
• Lakov Lako Panov
• MALINOVA Petrunka Atanasova

Classifications

• C01P2006/16

  Pore diameter · CPC title

• C09C1/48 Primary

  Carbon black · CPC title

• C01P2006/12

  Surface area · CPC title

• C01P2004/04

  obtained by TEM, STEM, STM or AFM · CPC title

• C01P2006/14

  Pore volume · CPC title