Polysiloxane composition, hardened material and optical device

Patent metadata

Field	Value
Publication number	US-9822248-B2
Application number	US-201113700622-A
Country	US
Kind code	B2
Filing date	May 23, 2011
Priority date	May 28, 2010
Publication date	Nov 21, 2017
Grant date	Nov 21, 2017

Abstract

The present invention aims to provide a polysiloxane composition which exhibits high heat and light resistance, and excellent gas-barrier properties. The polysiloxane composition of the present invention includes: (A) a modified polyhedral polysiloxane which is obtained by modifying (a) an alkenyl group-containing polyhedral polysiloxane compound with (b) a hydrosilyl group-containing compound; and (B) an organopolysiloxane containing at least two alkenyl groups in a molecule, wherein the polysiloxane composition after curing has a water vapor permeability of not more than 30 g/m 2 /24 h, and the polysiloxane composition includes (B1) an aryl group-containing organopolysiloxane as the organopolysiloxane (B), and/or (C) a component which is (C1) an organosilicon compound that contains one alkenyl or hydrosilyl group in a molecule, or (C2) a cyclic olefin compound that contains one carbon-carbon double bond in a molecule.

First claim

The invention claimed is:

1. A polysiloxane composition, comprising:
(A) a modified polyhedral polysiloxane which is obtained by modifying (a) an alkenyl group-containing polyhedral polysiloxane compound with (b) a hydrosilyl group-containing compound; and
(B) an organopolysiloxane that contains at least two alkenyl groups in a molecule,
wherein the organopolysiloxane (B) contains an aryl group and has a weight-average molecular weight of 200 to 1000 and
wherein the polysiloxane composition after curing has a water vapor permeability of not more than 20 g/m 2 /24 h, and
wherein a cured article obtained by using the polysiloxane composition has a storage elastic modulus at 50° C. of 10 MPa or lower.

2. The polysiloxane composition according to claim 1 ,
wherein the modified polyhedral polysiloxane (A) is in a liquid form at 20° C.

3. The polysiloxane composition according to claim 1 ,
wherein the hydrosilyl group-containing compound (b) is a hydrosilyl group-containing cyclic siloxane.

4. The polysiloxane composition according to claim 1 ,
wherein the hydrosilyl group-containing compound (b) is a hydrosilyl group-terminated straight-chain siloxane.

5. The polysiloxane composition according claim 1 ,
wherein the alkenyl group-containing polyhedral polysiloxane compound (a) comprises a siloxane unit represented by the following formula:
[AR 1 2 SiO—SiO 3/2 ] a [R 2 3 SiO—SiO 3/2 ] b

wherein a+b is an integer of 6 to 24, provided that a represents an integer of 1 or more, and b represents an integer of 0 or 1 or more; A represents an alkenyl group; R 1 represents an alkyl group or an aryl group; and R 2 represents a hydrogen atom, an alkyl group, an aryl group, or a group bonded to another polyhedral polysiloxane.

6. The polysiloxane composition according to claim 1 ,
wherein the modified polyhedral polysiloxane (A) is obtained by adding to the alkenyl group-containing polyhedral polysiloxane compound (a) an excessive amount of the hydrosilyl group-containing compound (b) such that the number of hydrogen atoms directly bonded to Si atoms of the compound (b) is 2.5 to 20 per alkenyl group of the polyhedral polysiloxane compound (a), to carry out the modification, and then evaporating an unreacted portion of the hydrosilyl group-containing compound (b).

7. The polysiloxane composition according to claim 1 ,
wherein the modified polyhedral polysiloxane (A) contains at least three hydrosilyl groups in a molecule.

8. The polysiloxane composition according to claim 1 ,
wherein the modified polyhedral polysiloxane (A) comprises a structural unit represented by the following formula:
[XR 3 2 SiO—SiO 3/2 ] a [R 4 3 SiO—SiO 3/2 ] b

wherein a+b is an integer of 6 to 24, provided that a represents an integer of 1 or more, and b represents an integer of 0 or 1 or more; R 3 represents an alkyl group or an aryl group; R 4 represents an alkenyl group, a hydrogen atom, an alkyl group, an aryl group, or a group bonded to another polyhedral polysiloxane; and X has a structure represented by the following formula (1) or (2), and in the case where multiple Xs are present, the structures of the Xs may be the same as or different from one another:

wherein l represents an integer of 2 or more; m represents an integer of 0 or more; n represents an integer of 2 or more; Y represents a hydrogen atom, an alkenyl group, an alkyl group, an aryl group, or a moiety bonded to a polyhedral polysiloxane via an alkylene chain, and Ys may be the same as or different from one another; Z represents a hydrogen atom, an alkenyl group, an alkyl group, an aryl group, or a moiety bonded to a polyhedral polysiloxane via an alkylene chain, and Zs may be the same as or different from one another, provided that at least one of Y and Z is a hydrogen atom.

9. The polysiloxane composition according to claim 1 , comprising a hydrosilylation catalyst.

10. The polysiloxane composition according to claim 1 , comprising a curing retardant.

11. The polysiloxane composition according to claim 1 , comprising an adhesion promoter.

12. The polysiloxane composition according to claim 1 , comprising an inorganic filler.

13. A cured article, obtained by using the polysiloxane composition according to claim 1 .

14. The cured article according to claim 13 ,
wherein the cured article has at least one loss tangent peak measured at a frequency of 10 Hz in a temperature range of −40° C. to 50° C.

15. An optical device, obtained by using the polysiloxane composition according to claim 1 .

16. The optical device according to claim 15 , comprising an encapsulant for optical elements which is obtained by using the polysiloxane composition.

17. The polysiloxane composition according to claim 1 , wherein the aryl group in the organopolysiloxane (B) is in an amount of 0.1 to 10 mmol/g.

Assignees

• Nishiyama Yoshitaka
• Tanaka Hiroyuki
• Sugiyama Satoshi
• Manabe Takao
• Kaneka Corp

Inventors

• Nishiyama Yoshitaka
• Tanaka Hiroyuki
• Sugiyama Satoshi
• Manabe Takao

Classifications

• C08G77/38

  Polysiloxanes modified by chemical after-treatment · CPC title

• C08L2201/14

  Gas barrier composition · CPC title

• C08G77/20

  containing silicon bound to unsaturated aliphatic groups · CPC title

• C08L2201/02

  Flame or fire retardant/resistant · CPC title

• C08L2205/025

  containing two or more polymers of the same hierarchy C08L, and differing only in parameters such as density, comonomer content, molecular weight, structure · CPC title