Resin beads, method for manufacting resin beads and product including resin beads

Patent metadata

Field	Value
Publication number	US-9809705-B2
Application number	US-201515305571-A
Country	US
Kind code	B2
Filing date	Jul 3, 2015
Priority date	Jul 9, 2014
Publication date	Nov 7, 2017
Grant date	Nov 7, 2017

Abstract

The present invention provides resin beads that are capable of imparting stable water repellency and oil absorbency at a high level to products, and realizing good spreadability and excellent persistence of makeup without giving sticky feeling when added to, for example, cosmetic materials, the process for producing the resin beads, and various kinds of products using the resin beads and having excellent properties. Resin beads being resin particles obtained by subjecting a monomer mixture containing a plurality of monomers each having a copolymerizable functional group to suspension polymerization in a state where at least a non-polymerizable silicone compound is present, the resin particles each having a roughened surface, and a process for producing the resin beads, and various kinds of products each using the resin beads and each having excellent properties.

First claim

The invention claimed is:

1. Resin beads being resin particles, each having a roughened surface,
wherein the resin particles are a product of suspension polymerization of a monomer mixture comprising a plurality of monomers each having a copolymerizable functional group, in the presence of at least a non-polymerizable silicone compound, and
the non-polymerizable silicone compound is at least one material selected from the group consisting of silicone-acrylic copolymers, polyether-modified silicones, polyether-alkyl-modified silicones, and silicone elastomers.

2. The resin beads according to claim 1 ,
wherein an amount of the non-polymerizable silicone compound present in the suspension polymerization is at a ratio from 1.0 to 30 parts by mass relative to 100 parts by mass of the monomer mixture that is a component of forming resin of the resin particles.

3. The resin beads according to claim 1 ,
wherein the non-polymerizable silicone compound is a silicone-acrylic copolymer.

4. The resin beads according to claim 1 ,
wherein the monomer having a copolymerizable functional group is a (meth)acrylate-based monomer.

5. The resin beads according to claim 1 ,
wherein the plurality of monomers each having a copolymerizable functional group comprises a monomer having a plurality of copolymerizable functional groups, and
the monomer mixture comprises the monomer having a plurality of copolymerizable functional groups in a content of 10% by mass or more relative to the plurality of monomers each having a copolymerizable functional group in the monomer mixture.

6. The resin beads according to claim 5 , wherein the monomer having a plurality of copolymerizable functional groups is a di(meth)acrylate.

7. The resin beads according to claim 1 ,
wherein the resin particles have a volume average particle diameter of 20 μm or less.

8. A resin beads production process for producing the resin beads according to claim 1 , comprising:
subjecting a polymerizable solution comprising: the monomer mixture comprising:
the plurality of monomers each having a copolymerizable functional group;
the non-polymerizable silicone compound;
a polymerization initiator; and
optionally a pigment

to the suspension polymerization in an aqueous phase,
the aqueous phase comprises a dispersion stabilizer dissolved therein, thereby obtaining resin beads each having at least water repellency and the roughened surface.

9. A water repellent and oil absorbent product comprising: the resin beads according to claim 1 in at least one product selected from the group consisting of cosmetics, dermal agents, paints, shaped articles, films, coating agents, and resin compositions.

10. Resin beads, each having a roughened surface,
wherein the resin particles are a product of suspension polymerization of a monomer mixture comprising a plurality of monomers each having a copolymerizable functional group, in the presence of at least a non-polymerizable silicone compound, and
the suspension polymerization is conducted in a state where a pigment is further present.

Assignees

• Dainichiseika Color Chem

Inventors

• Abe Takashi

Classifications

• C08L33/04

  Homopolymers or copolymers of esters {(C08L43/04 takes precedence)} · CPC title

• C08F220/1812

  C12-(meth)acrylate, e.g. lauryl (meth)acrylate · CPC title

• C08F220/1804

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• A61K8/0279

  Porous; Hollow · CPC title

• A61K8/025

  Explicitly spheroidal or spherical shape · CPC title