Multiple layer interlayer having improved optical and sound insulation properties

Patent metadata

Field	Value
Publication number	US-9809009-B2
Application number	US-201414563622-A
Country	US
Kind code	B2
Filing date	Dec 8, 2014
Priority date	Dec 8, 2014
Publication date	Nov 7, 2017
Grant date	Nov 7, 2017

Abstract

Multilayered interlayers having good acoustic properties comprising a stiff skin layer(s) and a soft core layer(s) are disclosed. The multilayered interlayers comprise: a first polymer layer (skin layer) comprising plasticized poly(vinyl acetal) resin; a second polymer layer (core layer) comprising plasticized poly(vinyl acetal) resin; wherein at least one plasticizer is a high refractive index plasticizer. The multilayered interlayers have low mottle and resist mottle formation.

First claim

What is claimed is:

1. A polymer interlayer comprising:
at least one soft layer having a first refractive index, the soft layer comprising a first poly(vinyl acetal) resin having a first residual hydroxyl content and a first residual acetate content, and a first plasticizer;
at least one stiffer layer having a second refractive index, the stiffer layer comprising a second poly(vinyl acetal) resin having a second residual hydroxyl content and a second residual acetate content, and a second plasticizer;
wherein at least one of the first and second plasticizers is a high refractive index plasticizer having a refractive index of at least about 1.460;
wherein the absolute value of the difference between the first refractive index and the second refractive index (delta RI) is less than about 0.010;
wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent; and
wherein the polymer interlayer has a damping loss factor (η) (as measured by ISO 16940) of at least about 0.15 at 20° C. and a sound transmission loss (STL) (as measured by ASTM E90 (2009) at 20° C.) of at least 37 decibels.

2. The polymer interlayer of claim 1 , wherein the soft layer of the polymer interlayer has a glass transition temperature (T g ) less than 20° C.

3. The polymer interlayer of claim 1 , wherein the high refractive index plasticizer is selected from adipates, epoxides, phthalates, terephthalates, iso-phthalates, benzoates, substituted phenols, and other specialty plasticizers and mixtures thereof.

4. The polymer interlayer of claim 1 , wherein the high refractive index plasticizer comprises an unsaturated aromatic moiety.

5. The polymer interlayer of claim 1 , wherein the difference between the first residual acetate content and the second residual acetate content is less than 2.0 weight percent.

6. The polymer interlayer of claim 1 , wherein the difference between the first residual acetate content and the second residual acetate content is at least 2.0 weight percent, and wherein at least one of the first poly(vinyl acetal) resin and the second poly(vinyl acetal) resin has a residual acetate content of at least about 4 wt. %.

7. The polymer interlayer of claim 1 , wherein the first plasticizer comprises a high refractive index plasticizer having a refractive index of at least 1.460.

8. The polymer interlayer of claim 1 , wherein the first plasticizer or the second plasticizer further comprises a plasticizer having a refractive index of less than about 1.450.

9. The polymer interlayer of claim 1 , wherein the soft layer further comprises a third poly(vinyl acetal) resin having a third residual hydroxyl content and a third residual acetate content, and wherein the difference between the first residual acetate content and the third residual acetate content is at least 2.0 weight percent or the difference between the first residual hydroxyl content and the third residual hydroxyl content is at least 2.0 weight percent, or the difference between the first residual acetate content and the third residual acetate content is at least 2.0 weight percent and the difference between the first residual hydroxyl content and the third residual hydroxyl content is at least 2.0 weight percent.

10. The polymer interlayer of claim 1 , wherein the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between two different glass transition temperatures (T g ) is at least 3° C.

11. The polymer interlayer of claim 1 , wherein the polymer interlayer has a mottle of less than 1.

12. The polymer interlayer of claim 1 , further comprising a second stiffer layer.

13. A polymer interlayer comprising:
at least one soft layer having a first refractive index, the soft layer comprising a first poly(vinyl acetal) resin having a first residual hydroxyl content and a first residual acetate content, and a first plasticizer;
at least one stiffer layer having a second refractive index, the stiffer layer comprising a second poly(vinyl acetal) resin having a second residual hydroxyl content and a second residual acetate content, and a second plasticizer;
wherein at least one of the first and second plasticizers is a high refractive index plasticizer having a refractive index of at least about 1.460;
wherein the absolute value of the difference between the first refractive index and the second refractive index (delta RI) is less than about 0.010;
wherein the difference between the first residual acetate content and the second residual acetate content is at least 2.0 weight percent; and
wherein the polymer interlayer has a damping loss factor (η) (as measured by ISO 16940) of at least about 0.15 at 20° C. and a sound transmission loss (STL) (as measured by ASTM E90 (2009) at 20° C.) of at least 37 decibels.

14. The polymer interlayer of claim 13 , wherein the soft layer of the polymer interlayer has a glass transition temperature (T g ) less than 20° C., and wherein the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between two different glass transition temperatures (T g ) is at least 3° C.

15. The polymer interlayer of claim 13 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is less than 2.0 weight percent.

16. The polymer interlayer of claim 13 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent.

17. The polymer interlayer of claim 13 , wherein the soft layer further comprises a third poly(vinyl acetal) resin having a third residual hydroxyl content and a third residual acetate content, and wherein the difference between the first residual acetate content and the third residual acetate content is at least 2.0 weight percent or the difference between the first residual hydroxyl content and the third residual hydroxyl content is at least 2.0 weight percent, or the difference between the first residual acetate content and the third residual acetate content is at least 2.0 weight percent and the difference between the first residual hydroxyl content and the third residual hydroxyl content is at least 2.0 weight percent.

18. A polymer interlayer comprising:
at least one soft layer having a first refractive index, the soft layer comprising a first poly(vinyl acetal) resin having a first residual hydroxyl content and a first residual acetate content, and a first plasticizer;
at least one stiffer layer having a second refractive index, the stiffer layer comprising a second poly(vinyl acetal) resin having a second residual hydroxyl content and a second residual acetate content, and a second plasticizer;
wherein at least one of the first and second plasticizers is a high refractive index plasticizer having a refractive index of at least about 1.460;
wherein the absolute value of the difference between the first refractive index and the second refractive index (delta RI) is less than about 0.010;
wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent;
wherein the difference between the first residual acetate content and the second residual acetate content is at least 2.0 weight percent; and

wherein the polymer interlayer has a damping loss factor (η) (as measured by ISO 16940) of at least about 0.15 at 20° C. and a sound transmission loss (STL) (as measured by ASTM E90 (2009) at 20° C.) of at least 37 decibel

Assignees

• Solutia Inc

Inventors

• Lu Jun
• Chen Wenjie
• Schilling Iii Curtis
• D'Errico John
• Cui Weihong
• Li Zhou
• Hurlbut Jeffrey B

Classifications

• B32B27/306

  comprising vinyl acetate or vinyl alcohol (co)polymers · CPC title

• B32B2307/412

  Transparent · CPC title

• B32B2270/00

  Resin or rubber layer containing a blend of at least two different polymers · CPC title

• B32B27/08 Primary

  of synthetic resin · CPC title

• B32B27/22

  using plasticisers · CPC title