Method for preparing microporous polyolefin film by thermally-induced phase separation method

Patent metadata

Field	Value
Publication number	US-9803057-B2
Application number	US-201414444530-A
Country	US
Kind code	B2
Filing date	Jul 28, 2014
Priority date	Jan 26, 2012
Publication date	Oct 31, 2017
Grant date	Oct 31, 2017

Abstract

The present invention discloses a method for preparing a microporous polyolefin film comprising: a step of injecting a composition comprising polyolefin 30 to 60 wt % and a diluent mixture comprising a diluent, which can make liquid-liquid phase separation with the polyolefin thermodynamically 40 to 70 wt %, into an extruding machine, and melting and kneading thereof to prepare a single phase melt; and a step of extruding the melt while conducting liquid-liquid phase separation by passing through a section having the temperature below the liquid-liquid phase separation temperature and forming thereof in the form of a sheet, and a microporous polyolefin film prepared according to the method.

First claim

What is claimed is:

1. A method for preparing a microporous polyolefin film comprising:
(a) a step of injecting a composition comprising polyolefin 30 to 60 wt % and a diluent mixture 40 to 70 wt % together into an extruding machine, and melting and kneading thereof to prepare a single phase melt, wherein the diluent mixture comprises a diluent, which can make liquid-liquid phase separation with the polyolefin thermodynamically and a supplementary diluent forming a thermodynamic single phase with the polyolefin, and weight ratio of the diluent and the supplementary diluent is 3:7 to 7:3; and
(b) a step of extruding the melt while conducting liquid-liquid phase separation by passing through a section having the temperature below the liquid-liquid phase separation temperature and forming thereof in the form of a sheet, wherein Hansen solubility parameter distance (Ra), expressed by the following formula of the diluent mixture to the polyolefin is 4.0 to 6.5 (J/cm 3 ) 1/2 :
Ra (J/cm 3 ) 1/2 =[4*(δ D P −δD D ) 2 +(δ P P −δP D ) 2 +(δ H P −δH D ) 2 ] 1/2

wherein δD P , δP P and δH P represent polyolefin solubility parameter generated by non-polar dispersion energy, polyolefin solubility parameter generated by polar energy by permanent dipole moment and polyolefin solubility parameter generated by energy by hydrogen bonds, respectively; and
δD D , δP D and δH D represent diluent solubility parameter generated by non-polar dispersion energy, diluent solubility parameter generated by polar energy by permanent dipole moment and diluent solubility parameter generated by energy by hydrogen bonds, respectively;
stretching the formed sheet to prepare a film;
extracting the diluent and the supplementary diluent from the stretched film by using an organic solvent;
drying the film; and
heat-setting the dried film to prepare a microporous polyolefin film,
wherein the diluent comprises ester of trimethylolpropane or ester of triethyleneglycol,
wherein the supplementary diluent comprises at least one diluent selected from the group consisting of liquid paraffin, paraffin oil, mineral oil and paraffin wax.

2. The method for preparing a microporous polyolefin film according to claim 1 , wherein the temperature difference (delta T) between a T-die of the extruding machine and a casting roll when extruding is 120 to 160° C.

3. The method for preparing a microporous polyolefin film according to claim 1 , wherein the liquid-liquid phase separation forms uniform pore size by slowly lowering the temperature of the melt (T-die temperature) beyond a filter of the extruding machine to 200° C., and by controlling retention time.

4. The method for preparing a microporous polyolefin film according to claim 2 , wherein crystallinity is increased and uniform pore size is formed by lowering the temperature difference (delta T) between the T-die and the casting roll of the extruding machine when extruding.

5. The method for preparing a microporous polyolefin film according to claim 1 , which further comprises a step of aging the prepared microporous polyolefin film.

Assignees

• Lg Chemical Ltd

Inventors

• Kim Bong-Tae
• Song Heon-Sik
• Lee Seung-Yup
• Kim Kyoung-Min

Classifications

• C08J2201/03

  Extrusion of the foamable blend · CPC title

• C08J2323/06

  Polyethene · CPC title