Method for manufacturing fluoropolymers

Patent metadata

Field	Value
Publication number	US-9803036-B2
Application number	US-201013515973-A
Country	US
Kind code	B2
Filing date	Dec 16, 2010
Priority date	Dec 18, 2009
Publication date	Oct 31, 2017
Grant date	Oct 31, 2017

Abstract

The invention pertains to a process for manufacturing a (per)fluoropolymer, said process comprising polymerizing one or more fluorinated monomers in the presence of a multi-phase medium, said medium comprising:
(A) a water phase [phase (W)]; (B) at least one fluorinated surfactant [surfactant (FS)] having formula (I) here below:

R f —(OCF 2 CF 2 ) k-1 —O—CF 2 —COOX a   (I)
wherein R f is a C 1 -C 3 perfluoroalkyl group comprising, optionally, one or more ether oxygen atoms, k is 2 or 3 and X a is a selected from a monovalent metal and an ammonium group of formula NR N 4 , wherein R N , equal or different at each occurrence, is a hydrogen atom or a C 1 -C 3 alkyl group; (C) an oil phase [phase (O)] comprising:
at least one non-functional (per)fluoropolyether (non-functional PFPE) comprising at least one (per)fluoropolyoxyalkylene chain [chain (R F )] and at least one functional (per)fluoropolyether (functional PFPE) comprising at least one (per)fluoropolyoxyalkylene chain [chain (R′ F )] and having a number average molecular weight of at least 1000 and a solubility of less than 1% by weight in water at 25° C.

First claim

The invention claimed is:

1. A process for manufacturing a (per)fluoropolymer, said process comprising polymerizing one or more fluorinated monomers in the presence of a multi-phase medium, said medium comprising:
(A) a water phase (W);
(B) at least one fluorinated surfactant (FS) having formula (I) here below:
R f —(OCF 2 CF 2 ) k-1 —O—CF 2 —COOX a   (I)

wherein R f is a C 1 -C 3 perfluoroalkyl group comprising, optionally, one or more ether oxygen atoms, k is 2 or 3 and X a is selected from the group consisting of a monovalent metal and an ammonium group of formula NR N 4 , wherein R N , equal or different at each occurrence, is a hydrogen atom or a C 1 -C 3 alkyl group;
(C) an oil phase (O) comprising:
at least one non-functional (per)fluoropolyether (non-functional PFPE) comprising at least one (per)fluoropolyoxyalkylene chain (R F ) and free from functional end-groups, and
at least one functional (per)fluoropolyether (functional PFPE) comprising at least one (per)fluoropolyoxyalkylene chain (R′ F )] and having a number average molecular weight of at least 1000 and a solubility of less than 1% by weight in water at 25° C.;

wherein the at least one non-functional (per)fluoropolyether is present in an amount ranging from 0.01% to less than 30% by weight of the total weight of the multi-phase medium.

2. The process of claim 1 , wherein the surfactant (FS) complies with formula (II) here below:
R f ′O—CF 2 CF 2 —O—CF 2 —COOX a ′  (II)

wherein:
R f ′ is a C 1 -C 3 perfluoroalkyl group;
X a ′ is selected from the group consisting of Li, Na, K, NH 4 and NR N′ 4 , wherein R N′ is a C 1 -C 3 alkyl group.

3. The process of claim 1 , wherein the surfactant (FS) complies with formula (III) here below:
CF 3 CF 2 O—CF 2 CF 2 —O—CF 2 —COOX a ′  (III)

wherein X a ′ is selected from the group consisting of Li, Na, K, NH 4 and NR N′ 4 , wherein R N′ is a C 1 -C 3 alkyl group.

4. The process of claim 1 , wherein the non-functional PFPE is selected from the group consisting of:
T 1 -O—[CF(CF 3 )CF 2 O] b1′ (CFYO) b2′ -T 1′   (1)

wherein:
T 1 and T 1′ , equal to or different from each other, are independently selected from the group consisting of —CF 3 , —C 2 F 5 and —C 3 F 7 groups;
Y, equal or different at each occurrence, is selected from the group consisting of a fluorine atom and a —CF 3 group;
b 1′ and b 2 ′, equal to or different from each other, are independently integers ≧0 such that the b1′/2′ ratio is comprised between 20 and 1000 and the (b1′+b2′) sum is comprised between 5 and 250; should b1′ and b2′ be both different from zero, the different recurring units are generally statistically distributed along the perfluoropolyoxyalkylene chain;
T 1 -O—[CF(CF 3 )CF 2 O] c1′ (C 2 F 4 O) c2′ (CFYO) c3′ -T 1 ′  (2)

wherein:
T 1 and T 1 ′ equal to or different from each other, have the same meaning as defined above;
Y, equal or different at each occurrence, has the same meaning as defined above;
c 1 ′, c 2 ′ and c 3′ , equal to or different from each other, are independently integers ≧0 such that the (c1′+c2′+c3′) sum is comprised between 5 and 250; should at least two of c 1 ′, c2′ and c3′ be different from zero, the different recurring units are generally statistically distributed along the perfluoropolyoxyalkylene chain;
T 1 -O—(C 2 F 4 O) d1′ (CF 2 O) d2′ -T 1 ′  (3)

wherein:
T 1 and T 1 ′, equal to or different from each other, have the same meaning as defined above;
d 1 ′ and d 2 ′, equal to or different from each other, are independently integers ≧0 such that the d1′/d2′ ratio is comprised between 0.1 and 5 and the (d1′+(d2′) sum is comprised between 5 and 250; should d1′ and d2′ be both different from zero, the different recurring units are generally statistically distributed along the perfluoropolyoxyalkylene chain;
T 2 -O—[CF(CF 3 )CF 2 O] e′ -T 2′   (4)

wherein:
T 2 and T 2′ , equal to or different from each other, are independently selected from the group consisting of —C 2 F 5 and —C 3 F 7 groups;
e′ is an integer comprised between 5 and 250
T 2 -O—(CF 2 CF 2 O) f′ -T 2′   (5)

wherein:
T 2 and T 2 ′, equal to or different from each other, have the same meaning as defined above;
f′ is an integer comprised between 5 and 250;
T1-O—(CF 2 CF 2 C(Hal′) 2 O) g1′ —(CF 2 CF 2 CH 2 O) g2′ —(CF 2 CF 2 CH(Hal′) g3′ -T 1′   (6)

wherein:
T 1 and T 1′ , equal to or different from each other, have the same meaning as defined above;
Hal′ is fluorine;
g1′, g2′, and g3′, equal to or different from each other, are independently integers ≧0 such that the (g1′+g2′+g3′) sum is comprised between 5 and 250; should at least two of g1′, g2′ and g3′ be different from zero, the different recurring units are generally statistically distributed along the (p)fluoropolyoxyalkylene chain; and
R 1 f —{C(CF 3 ) 2 —O—[C(R 2 f ) 2 ] j1′ C(R 2 f ) 2 —O} j2′ —R 1 f   (7)

wherein:
R 1 f , equal or different at each occurrence, is a C 1 -C 6 perfluoroalkyl group;
R 2 f , equal or different at each occurrence, is selected from the group consisting of a fluorine atom and a C 1 -C 6 perfluoroalkyl group;
j1′ is equal to 1 or 2;
j2′ is an integer comprised between 5 and 250.

5. The process of claim 1 , wherein the functional PFPE comprises at least one functional end-group selected from the group consisting of carboxylic acid, phosphonic acid and sulphonic acid groups.

6. The process of claim 5 , wherein the functional PFPE complies with formula (IV) here below:
T 1 -(CFW 1 ) p1 —O—R F —(CFW 2 ) p2 -T 2   (IV)

wherein;
R F is a (per)fluoropolyoxyalkylene chain (chain R′ F ) such that the number average molecular weight of the functional PFPE is at least 1000;
T 1 and T 2 , equal to or different from each other, are selected from the group consisting of:
i) functional end-groups selected from the group consisting of carboxylic acid, phosphoric acid and sulphonic acid groups, and
ii) non-functional end-groups selected from the group consisting of a fluorine atom and a C 1 -C 3 (per)fluoroalkyl group,
with the proviso that at least one of T 1 and T 2 is a functional end-group;

W 1 and W 2 , equal to or different from each other, independently represent a fluorine atom or a —CF 3 group;
p 1 and p 2 , equal to or different from each other, are independently integers comprised between 1 and 3.

7. The process of claim 1 , wherein the functional PFPE is a bifunctional PFPE complying with formula (VI) here below;
HOOC—CF 2 —O—(CF 2 ) n′ (CF 2 CF 2 O) m′ —CF 2 —COOH  (VI)

wherein n′ and m′ are independently integers 0 such that the number average molecular weight of the bifunctional PFPE is at least 1000, the recurring units being generally statistically distributed along the perfluoropolyoxyalkylene chain.

8. The process of claim 1 , wherein the weight ratio of said at least one surfactant (FS) having said formula (I) to said at least one functional PFPE ranges between 1:0.3 and 1:0.9.

9. The process of claim 1 , wherein R f is a (per)fluoropolyoxyalkylene chain (R′ F ) such that the number average molecular weight of the functional PFPE is at least 1500.

10. The process of claim 7 , wherein n′ and m′ are independently integers >0 such that the number average molecular weight of the bifunctional PFPE is at least 1500.

11. The process of claim 1 , wherein the fluorinated surfactant (FS) and the functional PFPE are present in a weight ratio of between 1:0.1 and 1:1.

12. The process of claim 1 , wherein the fluorinated surfactant (FS) and the functional PFPE are present in a weight ratio of between 1:0.3 and 1:0.9.

Assignees

• Pieri Riccardo
• Kapeliouchko Valeri
• Chernysheva Liubov
• Solvay Specialty Polymers It

Inventors

• Pieri Riccardo
• Kapeliouchko Valeri
• Chernysheva Liubov

Classifications

• C08F2/24

  with the aid of emulsifying agents · CPC title

• C08F2/32

  Polymerisation in water-in-oil emulsions · CPC title

• C08F14/18

  Monomers containing fluorine · CPC title

• C08L27/12

  containing fluorine atoms · CPC title

• C08F6/14 Primary

  Treatment of polymer emulsions {(C08F6/001, C08F6/006, C08F6/008, C08F6/02, C08F6/04 take precedence)} · CPC title