Electrode for solar cells and preparation method

Patent metadata

Field	Value
Publication number	US-9799457-B2
Application number	US-201314400921-A
Country	US
Kind code	B2
Filing date	Jun 13, 2013
Priority date	Jun 14, 2012
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

Electrode comprising a conductive substrate on which a uniform layer of aggregates A, having an average diameter ranging from 40 to 100 nm, is deposited, on which a non-homogeneous distribution of aggregates B, having an average diameter ranging from 300 nm to 1,200 nm, is superimposed, both of said aggregates being composed of particles containing one or more metals Me selected from platinum, palladium and gold, having an average diameter ranging from 8 to 10 nm. The use of said electrode, as cathode, for DSSC devices produces a marked improvement in the performances of the cell with respect to the results that can be obtained with known cathodes.

First claim

The invention claimed is:

1. An electrode comprising a conductive substrate on which a uniform layer of aggregates A is deposited, having an average diameter ranging from 40 to 100 nm, on which a non-homogeneous distribution of aggregates B is superimposed, having an average diameter ranging from 300 nm to 1,200 nm, both of said aggregates being composed of particles containing one or more metals selected from platinum, palladium and gold, having an average diameter ranging from 8 to 10 nm.

2. The electrode according to claim 1 , wherein the particles contain only one of said metals.

3. The electrode according to claim 1 , wherein when two or three of said metals are present both monometallic particles, composed of only one of each of said metals, and multimetallic particles, composed of mixtures having a variable composition of said metals, are contemporaneously present.

4. The electrode according to claim 3 , comprising aggregates composed of said monometallic particles that are the same as each other, aggregates composed of said monometallic particles differing from each other with respect to said metals, aggregates composed of said multimetallic particles and aggregates composed of said monometallic particles and said multimetallic particles.

5. The electrode according to claim 1 , wherein platinum, palladium and gold are in elemental form.

6. The electrode according to claim 1 , wherein said uniform layer of aggregates A is less than 300 nm in thickness.

7. The electrode according to claim 1 , wherein the aggregates B have an average diameter ranging from 300 to 600 nm.

8. The electrode according to claim 1 , wherein the conductive substrate is selected from glass with conductive coatings, composites based on plastic polymers or metal laminas.

9. A process for the preparation of an electrode comprising a conductive substrate on which a uniform layer of aggregates A is deposited, having an average diameter ranging from 40 to 100 nm, on which a non-homogeneous distribution of aggregates B is superimposed, having an average diameter ranging from 300 nm to 1,200 nm, both of said aggregates being composed of particles containing one or more metals selected from platinum, palladium and gold, having an average diameter ranging from 8 to 10 nm, comprising the following steps:
(1) dissolving at least one precursor containing platinum, palladium or gold, in a solvent having a boiling point higher than 200° C. to form a solution,
(2) depositing the solution containing the at least one precursor on the conductive substrate,
(3) thermally treating the at least one precursor by heating it to a temperature higher than the boiling point of the solvent used.

10. The process according to claim 9 , wherein in step (1) the solvent used has a boiling point ranging from 220 to 300° C.

11. The process according to claim 9 , wherein the solvent is selected from tetraglyme, glycerine or sulfolane.

12. The process according to claim 9 , wherein in step (2) the solution is deposited on the conductive substrate in a thickness of not less than 15 μm.

13. The process according to claim 9 , wherein, after depositing the solution, the conductive substrate is heated to a temperature ranging from 60 to 130° C. for a time ranging from 0.5 to 20 hours.

14. The process according to claim 9 , wherein in step (3), the thermal treatment is carried out at a temperature at least 100° C. higher than the boiling point of the solvent used in step (1).

15. The process according to claim 14 , wherein in step (3) the thermal treatment is carried out at a temperature at least 150° C. higher than the boiling point of the solvent used in step (1).

16. A Dye Sensitized Solar Cell comprising an electrode according to claim 1 .

17. The Dye Sensitized Solar Cell of claim 16 , wherein said electrode is a cathode.

Assignees

• Eni Spa

Inventors

• Ramello Stefano
• Biagini Paolo

Classifications

• H01G9/2031

  comprising titanium oxide, e.g. TiO2 (H01G9/2036 takes precedence) · CPC title

• Y02E10/542

  Dye sensitized solar cells · CPC title

• H01G9/2059

  comprising an organic dye as the active light absorbing material, e.g. adsorbed on an electrode or dissolved in solution · CPC title

• H01G9/2022 Primary

  characterized by he counter electrode · CPC title

• H01L31/022425

  Electricity · mapped topic