Method and apparatus for fabrication of metal-coated optical fiber, and the resulting optical fiber

Patent metadata

Field	Value
Publication number	US-9798080-B2
Application number	US-201414775361-A
Country	US
Kind code	B2
Filing date	Mar 14, 2014
Priority date	Mar 14, 2013
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

Method and apparatus for producing metal-coated optical fiber involves providing a length of optical fiber having a glass fiber with or without a carbon layer surrounded by a liquid-soluble polymeric coating. The optical fiber is passed through a series of solution baths such that the fiber will contact the solution in each bath for a predetermined dwell time, the series of solution baths effecting removal of the polymer coating and subsequent electroless plating of metal on the glass fiber. The optical fiber is collected after metal plating so that a selected quantity of the metal-coated optical fiber is gathered, Preferably, the glass fiber passes through the series of solution baths without contacting anything except for the respective solution in each.

First claim

What is claimed is:

1. A method for producing metal-coated optical fiber, said method comprising:
(a) providing a length of optical fiber having a glass fiber surrounded by a liquid soluble polymeric coating;
(b) passing said optical fiber through a series of solution baths such that the glass fiber will contact the solution in each bath for a predetermined dwell time, the series of solution baths effecting removal of said polymer coating and subsequent plating of metal on the glass fiber, wherein the glass fiber passes through the series of solution baths without contacting anything except for the respective solution in each of said solutions baths and wherein each of said solutions baths comprises a vessel having inlet and outlet holes through which said optical fiber passes horizontally without contacting said vessel; and
(c) collecting the optical fiber after metal plating so that a selected quantity of said metal-coated optical fiber is gathered.

2. A method as set forth in claim 1 , wherein said glass fiber has a carbon layer.

3. A method as set forth in claim 1 , wherein said liquid soluble polymeric coating comprises a polymeric material that is removed by a chemical solvent.

4. A method as set forth in claim 3 , wherein said polymeric material that is removed by a chemical solvent comprises acrylate.

5. A method as set forth in claim 1 , wherein said liquid soluble polymeric coating, comprises a water soluble polymer.

6. A method as set forth in claim 5 , wherein said water soluble polymer is selected from the group consisting of sodium polyacrylater, plyacrylamide, polyvinyl alcohol, polyethyleneimine, polyethylene glycol, and polyvinylpyrrolidone.

7. A method as set forth in claim 5 , wherein said water soluble polymer of said polymeric coating is removed by water at substantially room temperature.

8. A method as set forth in claim 7 , wherein said water soluble polymer of said polymeric coating is removed by said water in no more than approximately one minute dwell time.

9. A method as set forth in claim 1 , wherein liquid in said vessel flows out of said inlet and outlet holes for recirculation.

10. A method as set forth in claim 1 , wherein liquid is inhibited from flowing out of said inlet outlet holes due to ambient pressure.

11. A method as set forth in claim 1 , wherein said liquid soluble polymeric coating is applied to said glass fiber by passing said glass fiber through at least one die containing a polymer solution.

12. A method as set forth in claim 11 , wherein said glass fiber is passed vertically through said at least one die.

13. A method as set forth in claim 11 , wherein said polymer has a viscosity of 1-5000 mPa-s.

14. A method as set forth in claim 1 , wherein the metal is plated on said glass fiber via an electroless plating process.

15. A method as set forth in claim 14 , wherein the metal is selected from a group consisting of nickel, copper, gold, silver, and suitable alloys.

16. A method as set forth in claim 1 , wherein said length of optical fiber is between one and ten kilometers in length.

17. A method for producing metal-coated optical fiber, said method comprising:
(a) providing a length of optical fiber having a glass fiber surrounded by a water soluble polymeric coating;
(b) passing said optical fiber through a water bath to remove said polymeric coating;
(c) passing said glass fiber through at least one solution bath after removal of said polymeric coating such that the glass fiber will contact solution therein for a predetermined dwell time in order to achieve electroless plating of metal on the glass fiber, wherein the glass fiber passes through the at least one solution bath without contacting anything except for the in the at least one solution bath and wherein the at least one solution bath comprises a vessel having inlet and outlet holes through which said optical fiber passes horizontally without contacting said vessel; and
(d) collecting the optical fiber after metal plating so that a selected quantity of said metal-coated optical fiber is gathered.

18. A method as set forth in claim 17 , wherein said glass fiber has a carbon layer.

19. A. method as set forth in claim 17 , wherein said water soluble polymer is selected from the group consisting of sodium polyacrylater, plyacrylamide, polyvinyl alcohol, polyethyleneimine, polyethylene glycol, and polyvinylpyrrolidone.

20. A method as set forth in claim 17 , wherein said water soluble polymer of said polymeric coating is removed by water at substantially room temperature.

21. A method as set forth in claim 20 , wherein said water soluble polymer of said polymeric coating is removed by said water in no more than approximately one minute dwell time.

22. A method as set forth in claim 17 , wherein said water soluble polymeric coating is applied to said glass fiber by passing said glass fiber through at least one die containing a polymer solution.

23. A method as set forth in claim 22 , wherein said polymer has a viscosity of 1-5000 mPa-s.

24. A method as set forth in claim 17 , wherein the metal is selected from a group consisting of nickel, copper, gold, silver, and suitable alloys.

Assignees

• Afl Telecommunications Llc
• Fujikura Ltd

Inventors

• Miyamoto Matsuhiro
• Miyachi Masami

Classifications

• C23C18/1632

  Features specific for the apparatus, e.g. layout of cells and of its equipment, multiple cells · CPC title

• C03C25/70

  Cleaning, e.g. for reuse (C03C25/62 -C03C25/66 take precedence) · CPC title

• G02B6/03622

  having 2 layers only · CPC title

• G02B6/03694 Primary

  Multiple layers differing in properties other than the refractive index, e.g. attenuation, diffusion, stress properties · CPC title

• C23C18/1664

  with additional means during the plating process · CPC title