Water-absorbent resin composition and method for producing thereof, and absorbent material and absorbent product using thereof

Patent metadata

Field	Value
Publication number	US-9796853-B2
Application number	US-56532404-A
Country	US
Kind code	B2
Filing date	Jul 23, 2004
Priority date	Jul 25, 2003
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

A water-absorbent resin composition suffering exfoliation of additives from a water-absorbent resin only insignificantly and excelling in fluidity of powder after absorption of moisture and in deodorizing property and absorbent property as well is provided. The water-absorbent resin composition of this invention comprises a water-absorbent resin obtainable by polymerizing an unsaturated monomer having an acid group and/or a salt thereof; and complex oxide hydrate containing zinc and silicon, or zinc and aluminum, wherein the complex oxide hydrate contains zinc as main metal component, the mass ratio of the content of zinc and the content of silicon or aluminum is in the range of 50/50-99/1, and the absorption capacity at 60 minutes toward 0.90 mass % sodium chloride aqueous solution under the pressure of 1.9 kPa is not less than 20 g/g. Optionally, a plant component (C) can be added to the water absorbent resin composition.

First claim

The invention claimed is:

1. A water-absorbent resin composition having the absorption capacity at 60 minutes toward 0.90 mass % sodium chloride aqueous solution under the pressure of 1.9 kPa not less than 20 g/g, comprising:
a plant component,
a water-absorbent resin obtained by polymerizing an unsaturated monomer having an acid group and/or a salt thereof, and
a complex oxide hydrate containing zinc and silicon, or zinc and aluminum, wherein the complex oxide hydrate constitutes 0.001 to 5 parts by weight per 100 parts by weight the absorbent resin, in which the mass ratio of the content of zinc and the content of silicon or aluminum is in the range of 50/50-99/1; the water-absorbent resin composition is in a granular state and contains particles exceeding 150 μm in diameter in a proportion of not less than 90 mass % of all the particles, exceeding 300 μm in diameter in a proportion of not less than 60 mass % of all the particles, and not exceeding 850 μm in diameter in 100 mass % of all the particles; the complex oxide hydrate is present on the surface of the water-absorbent resin; and the plant component is at least one compound selected from the group consisting of polyphenols, flavones and caffeines.

2. A water-absorbent resin composition having the absorption capacity at 60 minutes toward 0.90 mass % sodium chloride aqueous solution under the pressure of 1.9 kPa not less than 20 g/g, comprising:
a plant component,
a water-absorbent resin obtained by polymerizing an unsaturated monomer having an acid group and/or a salt thereof, and
a complex oxide hydrate containing zinc and silicon, or zinc and aluminum, wherein the complex oxide hydrate constitutes 0.001 to 5 parts by weight per 100 parts by weight the absorbent resin, in which the mass ratio of the content of zinc and the content of silicon or aluminum is in the range of 50/50-99/1; the water-absorbent resin composition is in a granular state and contains particles exceeding 150 μm in diameter in a proportion of not less than 90 mass % of all the particles, exceeding 300 μm in diameter in a proportion of not less than 60 mass % of all the particles, and not exceeding 850 μm in diameter in 100 mass % of all the particles; the complex oxide hydrate is present on the surface of the water-absorbent resin; and the plant component is at least one compound selected from the group consisting of tannins, tannic acid, gall, nutgall, and gallic acid.

3. A water-absorbent resin composition having the absorption capacity at 60 minutes toward 0.90 mass % sodium chloride aqueous solution under the pressure of 1.9 kPa not less than 20 g/g, comprising:
a plant component,
a water-absorbent resin obtained by polymerizing an unsaturated monomer having an acid group and/or a salt thereof, and
a complex oxide hydrate containing zinc and silicon, or zinc and aluminum, wherein the complex oxide hydrate constitutes 0.001 to 5 parts by weight per 100 parts by weight the absorbent resin, in which the mass ratio of the content of zinc and the content of silicon or aluminum is in the range of 50/50-99/1; the water-absorbent resin composition is in a granular state and contains particles exceeding 150 μm in diameter in a proportion of not less than 90 mass % of all the particles, exceeding 300 μm in diameter in a proportion of not less than 60 mass % of all the particles, and not exceeding 850 μm in diameter in 100 mass % of all the particles; the complex oxide hydrate is present on the surface of the water-absorbent resin; and the plant component is contained in a range of 0.001-10 parts by weight based on 100 parts by weight of the water-absorbent resin.

4. A water-absorbent resin composition according to claim 1 , wherein the absorbent resin is surface crosslinked with a surface crosslinking agent at a temperature in the range of 100 to 250° C.

5. A water-absorbent resin composition according to claim 2 , wherein the absorbent resin is surface crosslinked with a surface crosslinking agent at a temperature in the range of 100 to 250° C.

6. A water-absorbent resin composition according to claim 3 , wherein the absorbent resin is surface crosslinked with a surface crosslinking agent at a temperature in the range of 100 to 250° C.

7. An absorbent material for sanitary product comprising: a water-absorbent resin composition of claim 1 and hydrophilic fibers.

8. An absorbent material for sanitary product comprising: a water-absorbent resin composition of claim 2 and hydrophilic fibers.

9. An absorbent material for sanitary product comprising: a water-absorbent resin composition of claim 3 and hydrophilic fibers.

10. An absorbent product comprising: an absorbent material of claim 7 , top-sheet possessing permeability to liquid, and back-sheet possessing impermeability to liquid.

11. An absorbent product comprising: an absorbent material of claim 8 , top-sheet possessing permeability to liquid, and back-sheet possessing impermeability to liquid.

12. An absorbent product comprising: an absorbent material of claim 9 , top-sheet possessing permeability to liquid, and back-sheet possessing impermeability to liquid.

13. A water-absorbent resin composition according to claim 1 , wherein the plant component is at least one of polyphenols and flavones.

14. A water-absorbent resin composition according to claim 2 , wherein the plant component is at least one of gall, nutgall, and gallic acid.

15. A water-absorbent resin composition according to claim 1 , wherein the complex oxide hydrate has a separation ratio of 0 to 20%.

16. A water-absorbent resin composition according to claim 2 , wherein the complex oxide hydrate has a separation ratio of 0 to 20%.

17. A water-absorbent resin composition according to claim 3 , wherein the complex oxide hydrate has a separation ratio of 0 to 20%.

18. A water-absorbent resin composition according to claim 1 , wherein the absorbent resin composition has a hygroscopic blocking ratio of 0 to 30 mass %.

19. A water-absorbent resin composition according to claim 2 , wherein the absorbent resin composition has a hygroscopic blocking ratio of 0 to 30 mass %.

20. A water-absorbent resin composition according to claim 3 , wherein the absorbent resin composition has a hygroscopic blocking ratio of 0 to 30 mass %.

Assignees

• Ueda Hiroko
• Wada Katsuyuki
• Nakashima Yasuhisa
• Nippon Catalytic Chem Ind

Inventors

• Ueda Hiroko
• Wada Katsuyuki
• Nakashima Yasuhisa

Classifications

• C08L101/14 Primary

  the macromolecular compounds being water soluble or water swellable, e.g. aqueous gels · CPC title

• A61L15/18 Primary

  containing inorganic materials · CPC title

• A61L15/60

  Liquid-swellable gel-forming materials, e.g. super-absorbents · CPC title

• A61F13/15

  Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators · CPC title

• C08K7/02

  Fibres or whiskers · CPC title