Polypropylene compounds having non-migratory slip properties

Patent metadata

Field	Value
Publication number	US-9796839-B2
Application number	US-201314414576-A
Country	US
Kind code	B2
Filing date	Jul 15, 2013
Priority date	Jul 16, 2012
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

A masterbatch having epoxy-functionalized silicone as a slip additive, the polypropylene compound that the silicone-containing masterbatch has been let down into, and the plastic articles and films from such compounds having improved slip properties are disclosed. The improved slip properties are evidenced by (1) essentially no migration of the slip additive 12 weeks after manufacturing, (2) a dynamic coefficient of friction value of less than 0.4 and a static coefficient of friction 0.6 or less within the first day of manufacturing according to the ASTM D1894-01 method, and (3) less than 15% change in the dynamic and static coefficient of friction values between the first day of manufacturing and 20 days after manufacturing.

First claim

What is claimed is:

1. A masterbatch for polypropylene, comprising in weight percent of the masterbatch:
(a) from 45 to 81 weight percent of polypropylene carrier,
(b) from 5 to 10 weight percent of epoxy functionalized polysiloxane,
(c) from 9 to 45 weight percent of functionalized polyolefin, and
(d) optionally, from 0 to 10 weight percent of other additives;

wherein the functionalized polyolefin contains a maleic anhydride group and is a grafting agent for the epoxy functionalized polysiloxane.

2. The masterbatch of claim 1 , wherein the functionalized polyolefin is selected from the group consisting of maleic anhydride grafted polypropylene, maleic anhydride polypropylene copolymer, ethylene ethyl acrylate maleic anhydride terpolymer, and combinations of them.

3. A polypropylene compound comprising the masterbatch of claim 1 and polypropylene resin.

4. A polypropylene compound comprising:
(a) polypropylene matrix and
(b) a slip additive comprising in weight percent of the slip additive
(i) from 45 to 81 weight percent of polypropylene carrier,
(ii) from 5 to 10 weight percent of epoxy functionalized polysiloxane,
(ii) from 9 to 45 weight percent of functionalized polyolefin, and
(iv) optionally, from 0 to 10 weight percent of other additives;

wherein the functionalized polyolefin contains a maleic anhydride group and is a grafting agent for the epoxy functionalized polysiloxane.

5. The polypropylene compound of claim 4 , wherein the functionalized polyolefin is miscible with the polypropylene matrix.

6. The polypropylene compound of claim 4 , wherein the additive is selected from the group consisting of anti-blocking agents; adhesion promoters; biocides (antibacterials, fungicides, and mildewcides), anti-fogging agents; anti-static agents; bonding, blowing and foaming agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppressants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; plasticizers; processing aids; other slip or release agents; silanes, titanates and zirconates; stabilizers; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them.

7. The polypropylene compound of claim 4 , wherein one or more additives are added in the form of a masterbatch concentrate.

8. The polypropylene compound of claim 4 , in the shape of a molded plastic article, an extruded plastic article, or a calendered plastic article.

9. A film having at least one layer comprised of the polypropylene compound of claim 4 .

10. A laminate of the film of claim 9 , wherein there is more than one film layer, and wherein each layer comprises same or different ingredients.

11. The laminate of claim 10 , wherein there is a skin layer contacting one surface of a core layer also having an opposing surface; and wherein the skin layer has a thickness between about 0.5 microns and about 1 millimeter.

12. The laminate of claim 11 , further comprising a second skin layer contacting the opposing surface of the core layer, wherein the core layer comprises polyolefin resin.

13. The laminate of claim 11 , wherein the skin layer has dynamic coefficient of friction value of 0.4 or less and static coefficient of friction value of 0.6 or less, according to the ASTM D1894-01 method, within 1 day after manufacturing of the laminate.

14. The laminate of claim 11 , wherein the change between static coefficient of friction and dynamic coefficient of friction values of the skin layer within 1 day after manufacturing and 20 days after manufacturing, according to the ASTM D1894-01 method, is 15% or less.

15. The laminate of claim 11 , wherein there is essentially no migration of the slip additive from the skin layer into another film layer measured 12 weeks after manufacturing.

Assignees

• Polyone Corp

Inventors

• Alric Jerome
• Waeler Jerome
• Auvray Fabien

Classifications

• C08L2205/02

  containing two or more polymers of the same C08L -group · CPC title

• C08J2323/26

  modified by chemical after-treatment · CPC title

• B32B27/283

  comprising polysiloxanes · CPC title

• B32B2307/746

  Slipping, anti-blocking, low friction · CPC title

• C08J5/18

  Manufacture of films or sheets · CPC title