Process for producing wet masterbatch, and wet masterbatch produced by said process

Patent metadata

Field	Value
Publication number	US-9796819-B2
Application number	US-201515309027-A
Country	US
Kind code	B2
Filing date	Apr 3, 2015
Priority date	May 8, 2014
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

Provided is a process for producing a wet masterbatch which, without deteriorating a reinforcing property of a rubber composition and rubber physical properties, micronizes a filler slurry by controlling an amount of functional groups on a filler surface, and improves filler dispersibility in the rubber wet masterbatch and the rubber composition. The process for producing a wet masterbatch comprises: a step of producing a slurry solution having a pH of 8 or more by dispersing carbon black having an average amount of surface acidic functional groups (μeq/m 2 ) of 0.15 or more and less than 3.00; a step of producing a mixture by mixing the slurry solution and a rubber latex solution in a liquid phase; and a step of drying the mixture.

First claim

The invention claimed is:

1. A process for producing a wet masterbatch comprising: a step of introducing acidic functional groups on a surface of carbon black by a gas phase ozone treatment performed under an ozone atmosphere of 0.1% or more and 16% or less to produce carbon black having an average amount of surface acidic functional groups (μeq/m 2 ) of 0.15 or more and less than 3.00; a step of producing a slurry solution having a pH of 8 or more by dispersing the carbon black; a step of producing a mixture by mixing the slurry solution and a rubber latex solution in a liquid phase; and a step of drying the mixture.

2. The process for producing a wet masterbatch according to claim 1 , wherein the carbon black has a DBP oil absorption amount (ml/100 g) of 100 or less.

3. The process for producing a wet masterbatch according to claim 1 , wherein the pH of the slurry solution is 9 or more.

4. The process for producing a wet masterbatch according to claim 1 , wherein the carbon black has an average amount of surface acidic functional groups (μeq/m 2 ) of 0.20 or more and 2.00 or less.

5. The process for producing a wet masterbatch according to claim 1 , wherein, when an STSA (m 2 /g) of the carbon black is 120 or more, the step of producing a slurry solution comprises dispersing the carbon black in a basic aqueous solution prepared by mixing water and a base.

6. The process for producing a wet masterbatch according to claim 5 , wherein an amount of the base is, relative to a total amount of the slurry solution, 0.06% by mass or more and 0.1% by mass or less.

7. The process for producing a wet masterbatch according to claim 5 , wherein a frequency of micronized slurry having a particle size of 1 μm or less in the slurry solution is 65% or more.

8. A wet masterbatch produced by the process for producing a wet masterbatch according to claim 1 .

9. A process for producing a wet masterbatch comprising: a step of producing a slurry solution having a pH of 8 or more by dispersing carbon black having an STSA (m 2 /g) of 120 or more and an average amount of surface acidic functional groups (μeq/m 2 ) of 0.15 or more and less than 3.00 in a basic aqueous solution prepared by mixing water and a base, wherein a frequency of micronized slurry having a particle size of 1 μm or less in the slurry solution is 65% or more; a step of producing a mixture by mixing the slurry solution and a rubber latex solution in a liquid phase; and a step of drying the mixture.

10. The process for producing a wet masterbatch according to claim 9 , wherein the carbon black has a DBP oil absorption amount (ml/100 g) of 100 or less.

11. The process for producing a wet masterbatch according to claim 9 , wherein the pH of the slurry solution is 9 or more.

12. The process for producing a wet masterbatch according to claim 9 , wherein the carbon black has an average amount of surface acidic functional groups (μeq/m 2 ) of 0.20 or more and 2.00 or less.

13. The process for producing a wet masterbatch according to claim 9 , comprising a step of introducing acidic functional groups on a surface of the carbon black by a gas phase ozone treatment.

14. The process for producing a wet masterbatch according to claim 13 , wherein the gas phase ozone treatment is performed under an ozone atmosphere of 0.1% or more and 16% or less.

15. The process for producing a wet masterbatch according to claim 9 , wherein an amount of the base is, relative to a total amount of the slurry solution, 0.06% by mass or more and 0.1% by mass or less.

16. A wet masterbatch produced by the process for producing a wet masterbatch according to claim 9 .

Assignees

• Bridgestone Corp

Inventors

• Nishiura Fumiteru
• Kanda Yukari
• Someno Kazuaki

Classifications

• C08K3/04

  Carbon · CPC title

• C08J2307/02

  Latex · CPC title

• C08J3/22 Primary

  using masterbatch techniques · CPC title

• C08L21/02

  Latex · CPC title

• C08K2201/006

  Additives being defined by their surface area · CPC title