Methods of preparing a catalyst

Patent metadata

Field	Value
Publication number	US-9796798-B2
Application number	US-201615281514-A
Country	US
Kind code	B2
Filing date	Sep 30, 2016
Priority date	Apr 29, 2015
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

A method comprising a) calcining a silica support at temperature in the range of from about 100° C. to about 500° C. to form a precalcined silica support; b) contacting the precalcined silica support with a titanium alkoxide to form a titanated support; c) subsequent to b), contacting the titanated support with a polyol to form a polyol associated titanated support (PATS); d) contacting at least one of the silica support, pre-calcined silica support, the titanated support, the PATS, or combinations thereof with a chromium-containing compound to form a polymerization catalyst precursor; e) drying the polymerization catalyst precursor to form a dried polymerization catalyst precursor; and f) calcining the dried polymerization catalyst precursor to produce a polymerization catalyst, wherein less than about 0.1 wt. % of a highly reactive volatile organic compound (HRVOC) is emitted during the calcining of the dried polymerization catalyst precursor.

First claim

What is claimed is:

1. A pre-catalyst composition comprising (i) a precalcined silica support, (ii) a tetravalent titanium compound, (iii) a polyol, and (iv) a chromium-containing compound.

2. The composition of claim 1 wherein the precalcined silica support is characterized by a surface area of from about 250 m 2 /g to about 1000 m 2 /g and a pore volume of greater than about 1.0 cm 3 /g.

3. The composition of claim 1 wherein the tetravalent titanium compound comprises a titanium tetra-alkoxide.

4. The composition of claim 3 wherein the titanium tetra-alkoxide comprises titanium ethoxide, titanium n-propoxide, titanium isopropoxide, titanium butoxide or combinations thereof.

5. The composition of claim 1 wherein the tetravalent titanium compound is present in an amount of from about 0.1 wt % to about 10 wt % based on the total weight of the composition.

6. The composition of claim 1 wherein the polyol comprises ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, tripropylene glycol, polyethylene glycols with a molecular weight of from 106 to 1000, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, neopentyl glycol, 1,2-hexanediol, 1,6-hexanediol, 1,2-cyclohexanediol, 1,4-cyclohexanediol, 1,2-octanediol, 1,8-octanediol, 1,2-decanediol, 1,10-decanediol, glycerol, 2,2-dimethylolpropane, trimethylolethane, trimethylolpropane, pentaerythritol, dipentaerythritol, sorbitol, 1,2,4-butanediol, 2,2,4-trimethyl-1,3-pentanediol, 1-phenyl-1,2-ethanediol, 1,2-benzenediol (pyrocatechol), 1,3-benzenediol (resorcinol), 1,4-benzenediol, methyl catechol, methyl resorcinol, 1,2,4-benzenetriol, 2-hydroxybenzylalcohol, 3-hydroxybenzylalcohol, 4-hydroxybenzylalcohol, 3,5-dihydroxybenzylalcohol, 1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 2-(2-hydroxyphenyl)ethanol, 2-(3-hydroxyphenyl)ethanol, 2-(4-hydroxyphenyl)ethanol, 2-phenyl-1,2-propanediol, bisphenol A (2,2-di(4-hydroxyphenyl)propane), bisphenol F (bis(4-hydroxyphenyl)methane), bisphenol S (4,4′-dihydroxydiphenylsulfone), bisphenol Z (4,4′-cyclohexylidenebisphenol), bis(2-hydroxyphenyl)methane, or combinations thereof.

7. The composition of claim 1 wherein the polyol is present in an amount of from about 0.1 to about 10 molar equivalents per mole of tetravalent titanium compound.

8. The composition of claim 1 wherein the chromium-containing compound comprises basic chromium acetate.

9. The composition of claim 1 wherein the chromium-containing compound is present in an amount of from about 0.1 wt. % to about 10 wt. % by total weight of the composition.

10. A pre-catalyst composition prepared by:
a) calcining a silica support at temperature in the range of from about 100° C. to about 500° C. to form a precalcined silica support;
b) contacting the precalcined silica support in a solvent with a titanium alkoxide to form a titanated support;
c) subsequent to b), contacting the titanated support with a polyol to form a polyol associated titanated support (PATS); and
d) contacting at least one of the silica support, the pre-calcined silica support, the titanated support, the PATS, or combinations thereof with a chromium-containing compound to form the pre-catalyst composition.

11. The composition of claim 10 wherein the solvent is anhydrous.

12. The composition of claim 11 wherein the solvent comprises alcohols, ketones, aliphatic hydrocarbons, aromatic hydrocarbons, halocarbons, ethers, acetonitrile, esters, or combinations thereof.

13. A pre-catalyst composition comprising (i) a titania-coated silica support, (ii) a polyol, (iii) and (iv) a chromium-containing compound, wherein the titania-coated silica support comprises a tetravalent titanium-containing compound selected from the group consisting of titanium ethoxide, titanium n-propoxide, titanium isopropoxide, titanium butoxide or combinations thereof.

14. The composition of claim 13 wherein the titania-coated silica support is characterized by a surface area of from about 250 m 2 /g to about 1000 m 2 /g and a pore volume of greater than about 1.0 cm 3 /g.

15. The composition of claim 13 wherein the polyol comprises ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, tripropylene glycol, polyethylene glycols with a molecular weight of from 106 to 1000, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, neopentyl glycol, 1,2-hexanediol, 1,6-hexanediol, 1,2-cyclohexanediol, 1,4-cyclohexanediol, 1,2-octanediol, 1,8-octanediol, 1,2-decanediol, 1,10-decanediol, glycerol, 2,2-dimethylolpropane, trimethylolethane, trimethylolpropane, pentaerythritol, dipentaerythritol, sorbitol, 1,2,4-butanediol, 2,2,4-trimethyl-1,3-pentanediol, 1-phenyl-1,2-ethanediol, 1,2-benzenediol (pyrocatechol), 1,3-benzenediol (resorcinol), 1,4-benzenediol, methyl catechol, methyl resorcinol, 1,2,4-benzenetriol, 2-hydroxybenzylalcohol, 3-hydroxybenzylalcohol, 4-hydroxybenzylalcohol, 3,5-dihydroxybenzylalcohol, 1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 2-(2-hydroxyphenyl)ethanol, 2-(3-hydroxyphenyl)ethanol, 2-(4-hydroxyphenyl)ethanol, 2-phenyl-1,2-propanediol, bisphenol A (2,2-di(4-hydroxyphenyl)propane), bisphenol F (bis(4-hydroxyphenyl)methane), bisphenol S (4,4′-dihydroxydiphenylsulfone), bisphenol Z (4,4′-cyclohexylidenebisphenol), bis(2-hydroxyphenyl)methane, or combinations thereof.

16. The composition of claim 15 wherein the polyol is present in an amount of from about 0.1 to about 10 molar equivalents per mole of the tetravalent titanium-containing compound.

17. The composition of claim 13 wherein the chromium-containing compound comprises basic chromium acetate present in an amount of from about 0.1 wt. % to about 10 wt. % by total weight of the composition.

18. A pre-catalyst composition comprising (i) a titania-coated silica support, (ii) a polyol, and (iii) a chromium-containing compound, wherein thermal treatment of the pre-catalyst composition produces less than about 1 wt. % of highly reactive volatile chemicals based on the total weight of the composition.

19. The composition of claim 18 , wherein the titania-coated silica support comprises a tetravalent titanium-containing compound selected from the group consisting of titanium ethoxide, titanium n-propoxide, titanium isopropoxide, titanium butoxide or combinations thereof.

20. The composition of claim 18 wherein the highly reactive volatile organic compound comprises propylene.

Assignees

• Chevron Phillips Chemical Co Lp
• Chevron Phillips Chemical Co Lp

Inventors

• Praetorius Jeremy M
• Schwerdtfeger Eric D
• Mcdaniel Max P
• Cymbaluk Ted H
• Boxell Connor D
• Collins Kathy S
• Solenberger Alan L

Classifications

• C08F4/24

  Oxides · CPC title

• C08F10/02 Primary

  Ethene · CPC title

• C08F4/02

  Carriers therefor · CPC title

• B01J31/38

  of titanium, zirconium or hafnium · CPC title

• B01J37/08

  Heat treatment {(B01J37/0009, B01J37/0018 take precedence)} · CPC title