Silver powder

Patent metadata

Field	Value
Publication number	US-9796018-B2
Application number	US-201314650348-A
Country	US
Kind code	B2
Filing date	Oct 2, 2013
Priority date	Dec 7, 2012
Publication date	Oct 24, 2017
Grant date	Oct 24, 2017

Abstract

Provided is a silver powder which has an appropriate viscosity range at the time of paste production, can be easily kneaded, and prevents the occurrence of flakes. The silver powder to be used has a specific surface area ratio SA B /SA S of 0.5 to 0.9, wherein SA B is a specific surface area measured by the BET method, and SA S is a specific surface area calculated from a mean primary-particle diameter D S measured with a scanning electron microscope. Furthermore, the silver powder preferably has a degree of aggregation of 1.5 to 5.0, the degree being obtained in such a manner that a volume median diameter D 50 measured by laser diffraction scattering is divided by the foregoing Ds.

First claim

The invention claimed is:

1. A silver powder, having a specific surface area ratio SA B /SA S of 0.5 to 0.9, wherein SA B is a specific surface area measured by a BET method and SA S is a specific surface area calculated from a mean primary-particle diameter D S measured with a scanning electron microscope, and having a degree of aggregation of 1.5 to 3.5, the degree being obtained in such a manner that a volume median diameter D 50 measured by laser diffraction scattering after application of a load of 100 N/cm 2 is divided by the foregoing Ds.

2. The silver powder according to claim 1 , having a degree of aggregation of 1.5 to 5.0, the degree being obtained in such a manner that a volume median diameter D 50 measured by laser diffraction scattering before application of the load is divided by the foregoing Ds.

3. The silver powder according to claim 1 , having a compressibility of not less than 20% caused by application of a load of 34 N/cm 2 in a measurement of a shear stress of a powder bed and having a compressibility of not more than 40% caused by application of a load of 113 N/cm 2 .

4. The silver powder according to clam 1 , having a ratio D 2 /D 1 of from 0.5 to 1.5, wherein D 1 is a volume median diameter obtained in such a manner that the silver powder in a paste obtained by kneading of said silver powder with an epoxy resin at a centrifugal force of 420 G is measured by laser diffraction scattering; and D 2 is a volume median diameter obtained in such a manner that the paste is subsequently further kneaded using a three-roll mill, and the silver powder in said paste is measured by laser diffraction scattering.

5. The silver powder according to claim 1 , having a ratio η 2 /η 1 of from 0.5 to 1.5 , wherein η 1 is a viscosity at a shear rate of 4 sec −1 , obtained in such a manner that a paste obtained by kneading of the silver powder with an epoxy resin at a centrifugal force of 420 G is measured using a viscoelastometer, and η 2 is a viscosity at a shear rate of 4 sec −1 , obtained in such a manner that the paste is subsequently further kneaded using a three-roll mill and measured.

6. The silver powder according to claim 1 , wherein SA B /SA S is 0.6 to 0.9.

Assignees

• Sumitomo Metal Mining Co

Inventors

• Terao Toshiaki
• Kawakami Yuji

Classifications

• B22F1/05

  Metallic powder characterised by the size or surface area of the particles · CPC title

• H05K1/092

  Dispersed materials, e.g. conductive pastes or inks · CPC title

• C22C5/06

  Alloys based on silver · CPC title

• H01B1/22

  the conductive material comprising metals or alloys · CPC title

• H01B1/02 Primary

  mainly consisting of metals or alloys · CPC title