Aqueous cross-linking compositions and methods

Patent metadata

Field	Value
Publication number	US-9790374-B2
Application number	US-201113152856-A
Country	US
Kind code	B2
Filing date	Jun 3, 2011
Priority date	Jun 4, 2010
Publication date	Oct 17, 2017
Grant date	Oct 17, 2017

Abstract

Water-borne cross-linking polymeric compositions and related embodiments, such as methods of making and using the compositions, as well as products formed with said compositions are described. For example, the water-borne composition may comprise polymers incorporating cross-linking functionality such as, but not limited to, carbonyl or epoxy functionality, and a blocked cross-linking agent, for example, a hydrazone. The cross-linking functionality does not react with the blocked cross-linking agent; however, the blocked cross-linking agent is capable of reacting with the alternative form cross-linking agent such as, but not limited to, a hydrazide, to yield a cross-linked polymer. The alternative form cross-linking agent may be formed in an equilibrium reaction including the blocked cross-linking agent.

First claim

What is claimed is:

1. A water-borne polymeric composition suitable for application to surface, which consists essentially of:
water;
one or more polymers for coalescence or drying into polymer solids, each polymer comprising one or more carbon groups, one or more epoxy groups, or both one or more carbonyl groups and one or more epoxy groups; and
a cross-linking agent which reacts with said carbonyl or epoxy groups or with both said carbonyl and epoxy groups, a blocked cross-linking agent having at least one hydrazone group incorporated therein, and a ketone or aldehyde, the blocked cross-linking agent being the reaction product of the ketone or aldehyde with the cross-linking agent;
in which composition, before its application to the surface, a reversible reaction of said blocked cross-linking agent produces said ketone or aldehyde and said cross-linking agent, with the reaction being at equilibrium such that the amount of the cross-linking agent is greater than 0% and less than or equal to 3% in said water-borne composition;
said reversible reaction being such that after said composition's application to the surface a reduction of the amount of ketone or aldehyde causes a shift toward the production of the cross-linking agent, and a resultant completion of its reaction with said carbonyl or epoxy groups or with both said carbonyl and epoxy groups, to yield a cross-linked water-resistant scrubable polymeric material.

2. The water-borne polymeric composition of claim 1 , which comprises different chain polymers for coalescence or drying into polymer solids, each polymer comprising one or more reactive carbonyl groups, one or more reactive epoxy groups, or both one or more reactive carbonyl groups and one or more reactive epoxy groups.

3. The water-borne polymeric composition of claim 2 , wherein the polymers are present in the composition in a range of 3% to 60% by weight.

4. The water-borne polymeric composition of claim 3 , wherein a ratio of the moles of blocked cross-linking agent to the number of said reactive groups is from 0.1:1 to 2:1.

5. The water-borne polymeric composition of claim 1 , wherein the blocked cross-linking agent comprises at least two hydrazone groups.

6. The water-borne polymeric composition of claim 1 , wherein the blocked cross-linking agent further comprises a hydrazine group.

7. The water-borne polymeric composition of claim 1 , wherein the pH of the composition is from 6.5 to 10.3.

8. The water-borne polymeric composition of claim 7 , wherein the pH of the composition is from 8.0 to 9.8.

9. The water-borne polymeric composition of claim 8 , wherein the pH of the composition is from 8.5 to 9.5.

10. The water-borne polymeric composition of claim 1 , wherein the blocked cross-linking agent is of formula:

is at least one blocked cross-linking agent of each of said formulae;
wherein R is a divalent organic group or a covalent bond, and each of R1, R2, R3, and R4 is selected to be independently of the others hydrogen or an organic group.

11. The water-borne polymeric composition of claim 10 , wherein each of R1, R2, R3, and R4 is selected, to be, independently of the others: C1 to C12 linear alkyl, alkenyl, or alkynyl; or a branched alkyl, alkenyl, or alkynyl having a C1 to C12 primary chain; or R1 and R2 or R3 and R4 are joined together to form a cyclic organic group or said linear or branched alkyl, alkenyl, or alkynyl being substituted with an hydroxyl, amino, phenyl, benzyl, or halogen.

12. The water-borne polymeric composition of claim 11 , wherein each of R1, R2, R3, and R4 is selected to be independently of the others methyl, ethyl, n-propyl, n-butyl, iso-butyl, tert-butyl, n-amyl, iso-amyl, n-hexyl, n-heptyl, n-octyl, iso-octyl, n-nonyl, n-decyl, n-undecyl or n-dodecyl.

13. The water-borne polymeric composition of claim 11 , wherein the cyclic group is cyclopentyl or cyclohexy.

14. The water-borne polymeric composition of claim 1 , wherein the carbonyl is incorporated within a ketone, aldehyde, or anhydride group.

15. The water-borne polymeric composition of claim 1 , wherein the polymeric composition functions as a paint, primer, coating, ink, or adhesive.

16. The water-borne polymetric composition of claim 1 , wherein the blocked cross-linking agent has the following formula:

wherein R is a divalent organic group or a covalent bond and each of R1, R2, R3, and R4 is selected to be independently of the others hydrogen or an organic group.

17. The water-borne polymeric composition of claim 16 , wherein R, in combination with the carbonyl groups adjacent to it, forms an oxalic, malonic, succinic, glutaric, adipic or sebacic moiety.

18. The water-borne polymeric composition of claim 1 , wherein the blocked cross-linking agent has the following formula:

wherein each of R′ and R″ is selected to be independently of the other a cyclic organic group and wherein R is a divalent organic group or a covalent bond.

19. The water-borne polymeric composition of claim 1 , wherein the blocked cross-linking agent is adipic acid di(2-butylidene hydrazide).

20. A method of preparing a water-borne composition suitable for application to a surface, which consists essentially of:
providing an aqueous dispersion including water, one or more cross-linkable polymers for coalescence or drying into polymer solids, a cross-linking agent, a blocked cross-linking agent comprising at least one hydrazone group, and ketone or aldehyde, the blocked cross-linking agent being the reaction product of the ketone or aldehyde with the cross-linking agent;
subjecting said dispersion to conditions inducing said cross-linking agent, blocked cross-linking agent and ketone or aldehyde to come to equilibrium with one another before said composition's application to the surface such that the amount of the cross-linking agent is greater than 0% and less than or equal to 3% in the water-borne composition;
wherein at least one polymer in the dispersion comprises one or more carbonyl groups, one or more epoxy groups, or both one or more carbonyl groups and one or more epoxy groups, and wherein said cross-linking agent reacts with said carbonyl or epoxy groups or with both said carbonyl and epoxy groups.

21. A method of coating a surface, which consists essentially of:
applying a water-borne polymeric composition to a surface, the composition comprising an aqueous polymeric dispersion including water, one or more polymers for coalescence or drying into polymer solids when applied to a surface, a cross-linking agent, a blocked cross-linking agent comprising at least one hydrazone group, and ketone or aldehyde, the blocked cross-linking agent being the reaction product of the ketone or aldehyde with the cross-linking agent;
in which composition, prior to being applied to the surface, an equilibrium is established such that the amount of the cross-linking agent is greater than 0% and less than or equal to 3% in said water-borne composition;
wherein at least one of the polymers comprises one or more carbonyl groups, one or more epoxy groups both one or more carbonyl groups and one or more epoxy groups, and said cross-linking agent is reactive with said carbonyl or epoxy groups or w

Assignees

• Chen Yue
• Yang Yong
• Sheerin Robert J
• Mauck Jean Fredrick
• Tilara Navin
• Garcia De Visicaro Johanna
• Columbia Insurance Co

Inventors

• Chen Yue
• Yang Yong
• Sheerin Robert J
• Mauck Jean Fredrick
• Tilara Navin
• Garcia De Visicaro Johanna

Classifications

• C09D5/024 Primary

  characterised by the additives · CPC title

• C09D133/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C08G59/4014

  Nitrogen containing compounds · CPC title

• C09D133/068

  containing glycidyl groups · CPC title

• C08L2201/56

  Non-aqueous solutions or dispersions · CPC title