Hybrid fiber cord and method for manufacturing the same

Patent metadata

Field	Value
Publication number	US-9789731-B2
Application number	US-201314438294-A
Country	US
Kind code	B2
Filing date	Dec 23, 2013
Priority date	Dec 27, 2012
Publication date	Oct 17, 2017
Grant date	Oct 17, 2017

Abstract

Disclosed are a hybrid fiber cord comprising a nylon filament and an aramid filament, the cord having more uniform physical properties and better strength and fatigue properties and being able to be made more easily than the conventional hybrid fiber cords such that it can be used to make an ultra high performance tire, and a method for manufacturing the same. The hybrid fiber cord comprises a nylon primarily-twisted yarn having a first twist number, and an aramid primarily-twisted yarn having a second twist number. The first twist number is identical with the second twist number. The nylon and aramid primarily-twisted yarns are secondarily-twisted together to have identical structures with each other.

First claim

The invention claimed is:

1. A hybrid fiber cord comprising:
a nylon primarily-twisted yarn having a first twist number of 300 to 500 TPM;
an aramid primarily-twisted yarn having a second twist number of 300 to 500 TPM; and
an adhesive,
wherein the first twist number is identical with the second number,
wherein the nylon primarily-twisted yarn and the aramid primarily-twisted yarn are secondarily-twisted together at a third twist number which is identical with the first and second twist numbers and have identical structures with each other in the hybrid fiber,
wherein the nylon primarily-twisted yarn and aramid primarily-twisted yarn which are secondarily-twisted together with the identical twist number form a 2-ply secondarily-twisted yarn consisting of 1-ply nylon primarily-twisted yarn and 1-ply aramid primarily-twisted yarn, and
wherein the secondarily-twisted yarn is coated with the adhesive, and the secondarily-twisted yarn coated with the adhesive has a strength retention rate of 80% or more after a disc fatigue test is performed according to JIS-L 1017 method of Japanese Standard Association, and has a dry heat shrinkage of 1.5 to 2.5%.

2. The hybrid fiber cord of claim 1 , wherein weight ratio of the nylon primarily-twisted yarn to the aramid primarily-twisted yarn is 20:80 to 80:20.

3. The hybrid fiber cord of claim 1 , wherein the hybrid fiber cord has breaking tenacity of 8.0 to 15.0 g/d and elongation at break of 7 to 15%, the breaking tenacity and elongation at break being measured according to ASTM D885 (2004).

4. A method for manufacturing a hybrid fiber cord, the method comprising:
a first step for primarily-twisting a nylon filament at a first twist number of 300 to 500 TPM to produce a nylon primarily-twisted yarn;
a second step for primarily-twisting an aramid filament at a second twist number of 300 to 500 TPM to produce an aramid primarily-twisted yarn;
a third step for secondarily-twisting the nylon and aramid primarily-twisted yarns together at a third twist number to produce a ply yarn in such a way that the nylon and aramid primarily-twisted yarns have identical structures with each other; and
coating the ply yarn with an adhesive, and the ply yarn coated with the adhesive has a strength retention rate of 80% or more after a disc fatigue test is performed according to JIS-L 1017 method of Japanese Standard Association, and has a dry heat shrinkage of 1.5 to 2.5%,
wherein the first, second and third twist numbers are identical with each other, and
wherein the third step produces a 2-ply secondarily-twisted yarn consisting of 1-ply of nylon primarily-twisted yarn and 1-ply of aramid primarily-twisted yarn.

5. The method of claim 4 , wherein the first, second and third steps are performed simultaneously and continuously.

6. The method of claim 4 , wherein the step of coating the ply yarn with an adhesive comprises:
submerging the ply yarn into an adhesive solution;
drying the ply yarn having the adhesive solution impregnated therein; and
heat-treating the dried ply yarn.

7. The method of claim 6 , wherein the adhesive solution comprises Resorcinol-Formaldehyde-Latex adhesive.

Assignees

• Kolon Inc

Inventors

• Lee Min Ho
• Jeon Ok Wha
• Chung Il

Classifications

• D10B2331/02

  polyamides (D10B2331/08 takes precedence) · CPC title

• D02G3/04

  Blended or other yarns or threads containing components made from different materials · CPC title

• D10B2331/021

  aromatic polyamides, e.g. aramides · CPC title

• D02G3/48 Primary

  Tyre cords {(tyre reinforcements B60C9/00; metal cords for reinforcing rubber or plastic articles D07B1/0606)} · CPC title

• D02G3/40

  Yarns in which fibres are united by adhesives; Impregnated yarns or threads · CPC title