PIPA polyol based viscoelastic foams

Patent metadata

Field	Value
Publication number	US-9783633-B2
Application number	US-201414911721-A
Country	US
Kind code	B2
Filing date	Sep 11, 2014
Priority date	Sep 13, 2013
Publication date	Oct 10, 2017
Grant date	Oct 10, 2017

Abstract

Viscoelastic foam is made by reacting an isocyanate compound with water and a polyol mixture. The polyol mixture contains a dispersion of polyurethane or polyurethane-urea particles in a carrier polyol (a PIPA polyol) and at least one other polyol that is a homopolymer of propylene oxide or a copolymer of 20 to 99.9 weight-% propylene oxide and 0.1 to 80 weight-% ethylene oxide, has 2 to 4 hydroxyl groups per molecule and has a hydroxyl equivalent weight of 200 to 400. The VE foams are characterized by high airflows and long recovery times.

First claim

What is claimed is:

1. A method of making a viscoelastic foam, comprising combining at least one organic polyisocyanate with water and a polyol mixture at an isocyanate index of 60 to 150 to form a reaction mixture and curing the reaction mixture to form a polyurethane-urea foam having a foam density of 30 to 120 kg/m 3 , a resiliency of less than 15% and a recovery time of at least 3 seconds as measured according to ASTM D3574 Test M, modified in that an indentation foot is brought into contact with the viscoelastic with a pre-load of 1N to determine the specimen's initial thickness and that time recording stops as soon as the viscoelastic foam recovers to apply a 4.5 N load against the indentation foot or, if the viscoelastic foam is too soft to recover enough to apply a force of 4.5N, then time recording stops when the viscoelastic foam recovers to apply a force of only 1 N against the indentation foot, wherein the polyol mixture includes:
Polyol A: at least one dispersion of polyurethane and/or polyurethane-urea particles in a carrier polyol, wherein said carrier polyol has an average molecular weight of 600 to 5000 and an average of at least two hydroxyl groups per molecule, the polyurethane or polyurethane-urea particles constitute from 5 to 50 weight percent of Polyol A and the Polyol A has a hydroxyl number of at least 40; and
Polyol B: at least one polyol which is a homopolymer of propylene oxide or a copolymer of 20 to 99.9 weight-% propylene oxide and 0.1 to 80 weight-% ethylene oxide, has 2 to 4 hydroxyl groups per molecule and has a hydroxyl equivalent weight of 200 to 400;
and further wherein Polyols A and B together constitute at least 75 weight-percent of all isocyanate-reactive materials other than water in the reaction mixture and the polyol mixture contains at least 1 weight-percent of the polyurethane and/or polyurethane-urea particles.

2. The method of claim 1 wherein Polyol A constitutes 3 to 60 weight percent of the polyol mixture.

3. The method of claim 2 wherein Polyol B constitutes 40 to 85 weight percent of the polyol mixture.

4. The method of claim 1 wherein Polyol B is a mixture of Polyols B1 and B2, wherein Polyol B1 is at least one polyol which is a copolymer of 50 to 80 weight-% ethylene oxide and correspondingly 50 to 20 weight-% propylene oxide, has 2.5 to 3.5 hydroxyl groups per molecule and a hydroxyl equivalent weight of 200 to 400 and polyol B2 is at least one polyol which is a homopolymer of propylene oxide or a copolymer of greater than 80 weight-% propylene oxide and less than 20 weight-% ethylene oxide, has 2-4 hydroxyl groups per molecule and has a hydroxyl equivalent weight of 200 to 400.

5. The method of claim 4 wherein Polyol B1 constitutes 30 to 60 weight-% of the polyol mixture and Polyol B2 constitutes 10 to 25 weight-% of the polyol mixture.

6. The method of claim 1 , wherein Polyol A has a higher hydroxyl number than the carrier polyol.

7. The method of claim 1 , wherein the polyurethane and/or polyurethane-urea particles constitute from 5 to 25 weight percent of Polyol A.

8. The method of claim 1 , wherein Polyol A contains 10 to 25% by weight of said polyurethane and/or polyurethane-urea particles, and said carrier polyol has an average hydroxyl equivalent weight of 200 to 400, nominally contain 2 to 4 hydroxyl groups per molecule and contains at least 75% secondary hydroxyl groups.

9. The method of claim 1 , wherein Polyol A contains 10 to 25% by weight of said polyurethane and/or polyurethane-urea particles and said carrier polyol has an average hydroxyl equivalent weight of 401 to 1200, nominally contains 2 to 4 hydroxyl groups per molecule and contains at least 75% secondary hydroxyl groups.

10. The method of claim 1 , wherein Polyol A contains 10 to 25% by weight of said polyurethane and/or polyurethane-urea particles, and said carrier polyol has an average hydroxyl equivalent weight of 1000 to 2500 and nominally contains 2 to 4 hydroxyl groups per molecule.

11. The method of claim 3 wherein said polyurethane and/or polyurethane-urea particles are a reaction product of triethanolamine, toluene diisocyanate and optionally water.

12. The method of claim 3 wherein the reaction mixture does not contain an SAN-type polymer polyol.

13. The method of claim 12 wherein the polyol mixture contains no more than 2 weight-% of castor oil.

14. The method of claim 1 wherein the viscoelastic foam is made in a free-rise process wherein a curing step is performed by pouring the reaction mixture into an open container such that expansion in at least one direction occurs against the atmosphere or a lightweight surface that provides negligible resistance to the expansion of the foam.

15. The method of claim 14 which is performed by continuously pouring the reaction mixture into the open container.

16. The method of claim 1 wherein the viscoelastic foam is cured in a mold.

17. The method of claim 1 wherein the viscoelastic foam has an airflow prior to crushing of at least 57 L/m.

18. The method of claim 1 wherein the viscoelastic foam has an airflow prior to crushing of at least 57 L/m and said recovery time of at least 10 seconds.

19. The method of claim 1 wherein the viscoelastic foam has an airflow prior to crushing of at least 80 L/m and said recovery time of at least 10 seconds.

Assignees

• Dow Global Technologies Llc

Inventors

• Casati Francois
• Lora Lamia Alberto
• Hunter Dale
• Amici-Kroutilova Irena
• Cookson Paul A
• Delk Van M

Classifications

• C08G18/409

  Dispersions of polymers of C08G in organic compounds having active hydrogen · CPC title

• C08K5/0066

  Flame-proofing or flame-retarding additives · CPC title

• C08G2350/00

  Acoustic or vibration damping material · CPC title

• C08G18/4883

  containing cyclic groups having at least one oxygen atom in the ring · CPC title

• C08G18/7621

  being toluene diisocyanate including isomer mixtures · CPC title