Method for preparing self-supporting flexible electrodes

Patent metadata

Field	Value
Publication number	US-9780355-B2
Application number	US-201214347871-A
Country	US
Kind code	B2
Filing date	Oct 4, 2012
Priority date	Oct 6, 2011
Publication date	Oct 3, 2017
Grant date	Oct 3, 2017

Abstract

A method for preparing self-supporting flexible electrodes is provided using refined cellulose fibers as binder. The negative or positive self-supporting flexible electrode is obtained by such method. A Li-ion battery is also provided in which at least one electrode is a self-supporting flexible electrode.

First claim

The invention claimed is:

1. Method for preparing a self-supporting flexible electrode g having at least one active electrode material, and at least one binder, said method comprising at least the following steps:
i) a step of preparation of an aqueous paste by the dispersion of a mixture of solid particles in an aqueous phase, said mixture of solid particles having:
at least one active electrode material, in a quantity varying from 50 to 98% by weight relative to the total weight of the mixture of solid particles,
at least one binder comprising refined cellulose fibres, in a quantity varying from 2 to 50% by weight relative to the total weight of the mixture of solid particles;

said mixture of solid particles representing at least 0.02% by weight of the total weight of the aqueous paste;
ii) a step of filtration of the aqueous paste obtained above in the step i) on a filtration cloth;
iii) optionally, a step of pressing, in the wet state, of the aqueous paste followed by its transfer onto a drying felt;
iv) a drying step to obtain a sheet of dry flexible electrode supported by the filtration cloth or by the drying felt when the step iii) has been carried out; and
v) a step of separation between the sheet of electrode and the filtration cloth or the drying felt when the step iii) has been carried out, to obtain the self-supporting flexible electrode.

2. Method according to claim 1 , wherein the refined cellulose fibres (FBr) are obtained by a refining method comprising the following steps:
a) a step of dispersion, in an aqueous medium, of previously dried cellulose fibres, to obtain a cellulose fibre paste in which the cellulose fibre content varies from 1 to 15% by weight relative to the total weight of said cellulose fibre paste; and
b) a step of shearing of said cellulose fibre paste, so as to obtain refined cellulose fibres, that is to say cellulose fibres exhibiting a Schopper-Riegler degree varying from 30 to 95° SR.

3. Method according to claim 1 , wherein an anti-flocculation agent for the fibres is incorporated in the aqueous suspension of the step i).

4. Method according to claim 3 , wherein the anti-flocculation agent is chosen from carboxymethylcellulose (CMC), starch and one of their mixtures.

5. Method according to claim 3 , wherein the anti-flocculation agent for the fibres represents 0.01 to 10% by weight relative to the total weight of the aqueous paste of the step i).

6. Method according to claim 1 , wherein the concentration by weight of the mixture of solid particles in the aqueous suspension on completion of the step i) varies from 0.02 to 5%.

7. Method according to claim 1 , wherein the filtration threshold of the step ii) is of the order of 1 to 100 μm.

8. Method according to claim 1 , wherein the degree of refining of the refined cellulose fibres (FBr) is at least 30° SR.

9. Method according to claim 1 , wherein the aqueous suspension of the step i) also contains at least one agent generating an electronic conductivity.

10. Method according to claim 9 , wherein the agent generating an electronic conductivity is selected from the group consisting of carbon black, carbon SP, acetylene black, carbon fibres and nanofibres, carbon nanotubes, metal particles, and one of their mixtures.

11. Self-supporting flexible electrode obtained by the implementation of the method as defined in claim 1 , wherein said self-supporting flexible electrode comprises at least one active electrode material, possibly at least one agent generating an electrical conductivity, possibly an anti-flocculation agent for the fibres and at least one binder comprising refined cellulose fibres (FBr) imprisoning said active electrode material.

12. Electrode according to claim 11 , wherein said electrode is a positive electrode and that the active material is selected from the group consisting of LixMn y O 4 (0<x<2, 0<y<2 and x+y=3), LiCoO 2 , LiMPO 4 , (M=Fe, Mn, Co, Ni), LiAl x Co y Ni z O 2 (0<x<1, 0<y<1, 0<z<1 and x+y+z=1) and LiNi (1-y) Co y O 2 (0≦y≦1).

13. Electrode according to claim 11 , wherein said electrode is a negative electrode and in that the active material is selected from the group consisting of: graphite, hard carbon, soft carbon and the metal alloys Li Y M (1<y<5 and M=Mn, Sn, Pb, Si, In, Ti).

14. Electrode according to claim 11 , wherein said electrode has a thickness varying from 50 to 300 μm.

15. Flexible lithium-ion battery comprising at least one negative electrode and/or at least one positive electrode between which is placed a solid electrolyte or a separator impregnated with a liquid electrolyte, wherein the positive electrode and/or the negative electrode is an electrode as defined in claim 11 .

16. Battery according to claim 15 , wherein each of the electrodes is a self-supporting flexible electrode as defined in claim 11 , said electrodes being separated from one another by a sheet of paper impregnated with liquid electrolyte.

Assignees

• Centre Nat Rech Scient
• Inst Polytechnique Grenoble

Inventors

• Jabbour Lara
• Chaussy Didier
• Beneventi Davide
• Destro Matteo
• Bodoardo Silvia
• Gerbaldi Claudio
• Penazzi Nerino

Classifications

• H01M4/485

  of mixed oxides or hydroxides for inserting or intercalating light metals, e.g. LiTi2O4 or LiTi2OxFy (H01M4/505, H01M4/525 take precedence) · CPC title

• H01M2220/30

  Batteries in portable systems, e.g. mobile phone, laptop · CPC title

• H01M4/1391

  of electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title

• Y02T10/7011

  Cross-Sectional Technologies · mapped topic

• H01M4/131

  Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title