Anode for secondary battery, method for producing same, and secondary battery

Patent metadata

Field	Value
Publication number	US-9774029-B2
Application number	US-201314396450-A
Country	US
Kind code	B2
Filing date	Apr 22, 2013
Priority date	Apr 27, 2012
Publication date	Sep 26, 2017
Grant date	Sep 26, 2017

Abstract

In this anode for a secondary battery, method for producing same, and secondary battery, an anode active material is laminated on a surface of a metal foil, the anode active material contains at least titanium dioxide, and the titanium dioxide contains a Brookite crystal phase and contains an amorphous phase in a ratio of 1 vol % to 20 vol %.

First claim

The invention claimed is:

1. An anode for a lithium ion secondary battery obtained by laminating a layer containing at least an anode active material on a metal foil,
wherein the anode active material contains at least titanium dioxide,
the titanium dioxide includes a brookite-type crystal phase, and includes an amorphous phase in a ratio of 4 vol % to 20 vol % with respect to all crystal phases and all amorphous phases.

2. The anode for a lithium ion secondary battery according to claim 1 ,
wherein the titanium dioxide includes the brookite-type crystal phase in a ratio of 1 vol % to 80 vol % with respect to all crystal phases and all amorphous phases of the titanium dioxide.

3. The anode for a lithium ion secondary battery according to claim 1 ,
wherein the titanium dioxide further includes one or more crystal layers selected from the group consisting of anatase-type titanium dioxide, rutile-type titanium dioxide, and bronze-type titanium dioxide.

4. The anode for a lithium ion secondary battery according to claim 1 ,
wherein an average particle diameter of primary particles of the titanium dioxide is in a range of 0.001 μm to 0.1 μm.

5. The anode for a lithium ion secondary battery according to claim 1 , further comprising:
a carbonaceous material.

6. The anode for a lithium ion secondary battery according to claim 5 ,
wherein the carbonaceous material is one or more selected from the group consisting of acetylene black, ketjen black, furnace black, channel black, natural graphite, artificial graphite, carbon nanotubes, carbon nanofibers and carbon fibers.

7. The anode for a lithium ion secondary battery according to claim 1 ,
wherein the metal foil is made of an aluminum foil.

8. A method for producing an anode for a lithium ion secondary battery, comprising in the following order:
a step of synthesizing powder containing at least the titanium dioxide by hydrolyzing a titanium-containing compound in an acidic aqueous solution so as to generate titanium dioxide, and then drying the titanium dioxide;
a step of annealing the powder so as to control the titanium dioxide contained in the powder to have a structure including at least a brookite-type crystal phase and further including an amorphous phase in a range of 4 vol % to 20 vol %, with respect to all crystal phases and all amorphous phases thereby generating a powder-form anode active material; and
a step of dispersing the powder-form anode active material in a dispersion solution so as to adjust a coating fluid, applying and drying the coating fluid on one surface or both surfaces of a metal foil.

9. The method for producing an anode for a lithium ion secondary battery according to claim 8 ,
wherein, in the step of synthesizing the powder, a chloride is used as the titanium-containing compound.

10. The method for producing an anode for a lithium ion secondary battery according to claim 8 ,
wherein, when the powder is annealed, a temperature is set in a range of 300° C. to 800° C., and a time is set in a range of 10 minutes to 300 minutes.

11. The method for producing an anode for a lithium ion secondary battery according to claim 8 ,
wherein, when the powder is annealed, an atmosphere is set to include water vapor in a mass ratio of 0.01 to 1.0 with respect to the powder.

12. A lithium ion secondary battery comprising:
the anode for a secondary battery according to claim 1 .

13. The lithium ion secondary battery according to claim 12 , formed by enclosing the anode for a secondary battery in an external packaging material together with a cathode, a separator, and a non-aqueous electrolytic solution.

14. The lithium ion secondary battery according to claim 13 ,
wherein the external packaging material is obtained by laminating a resin on both surfaces of an aluminum foil.

15. The anode for a lithium ion secondary battery according to claim 1 , wherein the metal foil is made of aluminum or alloy thereof and thickness of the metal foil is in range of 5 μm to 200 μm.

Assignees

• Showa Denko Kk

Inventors

• Yokouchi Hitoshi
• Ohmori Masahiro
• Sotowa Chiaki
• Sanbayashi Masayuki

Classifications

• H01M4/131 Primary

  Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title

• C01G23/0536 Primary

  by hydrolysing chloride-containing salts · CPC title

• H01M4/0416

  involving impregnation with a solution, dispersion, paste or dry powder (H01M4/0438 takes precedence) · CPC title