High-strength galvanized steel sheet with high yield ratio having excellent ductility and stretch flange formability and method for manufacturing the same

Patent metadata

Field	Value
Publication number	US-9765413-B2
Application number	US-201113809953-A
Country	US
Kind code	B2
Filing date	Jul 12, 2011
Priority date	Jul 15, 2010
Publication date	Sep 19, 2017
Grant date	Sep 19, 2017

Abstract

A high-strength galvanized steel sheet with high yield ratio having excellent ductility and stretch flange formability, the steel sheet having a chemical composition containing, by mass %, C: 0.04% or more and 0.13% or less, Si: 0.9% or more and 2.3% or less, Mn: 0.8% or more and 2.4% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.01% or more and 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities and a microstructure including, in terms of area ratio, 94% or more of a ferrite phase and 2% or less of a martensite ferrite phase, wherein mean grain size of ferrite is 10 μm or less, Vickers hardness of ferrite is 140 or more, mean grain size of carbide particles existing at grain boundaries of ferrite is 0.5 μm or less, and aspect ratio of carbide particles existing at the grain boundaries of ferrite is 2.0 or less.

First claim

The invention claimed is:

1. A galvanized steel sheet comprising a chemical composition containing, by mass %, C: 0.04% or more and 0.13% or less, Si: 0.9% or more and 2.3% or less, Mn: 0.8% or more and 2.4% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.01% or more and 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities and a microstructure including, in terms of area ratio, 94% or more of a ferrite phase and 2% or less of a martensite phase, wherein mean grain size of ferrite is 10μm or less, Vickers hardness of ferrite is 140 or more, mean grain size of carbide particles existing at grain boundaries of ferrite is 0.5 μm or less, and aspect ratio of carbide particles existing at the grain boundaries of ferrite is 2.0 or less.

2. The galvanized steel sheet according to claim 1 , wherein the microstructure has a number of crystal grains of ferrite containing 5 or more carbide particles in the crystal grains of 0.005 grain/μm 2 or more when the microstructure is observed by using a scanning electron microscope at a magnification of 3000 times.

3. The galvanized steel sheet according to claim 2 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less and Cu: 0.05% or more and 1.0% or less.

4. The galvanized steel sheet according to claim 2 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less and B: 0.0003% or more and 0.005% or less.

5. The galvanized steel sheet according to claim 2 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

6. The galvanized steel sheet according to claim 2 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ta: 0.001% or more and 0.010% or less and Sn: 0.002% or more and 0.2% or less.

7. The galvanized steel sheet according to claim 1 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less and Cu: 0.05% or more and 1.0% or less.

8. The galvanized steel sheet according to claim 7 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less and B: 0.0003% or more and 0.005% or less.

9. The galvanized steel sheet according to claim 7 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

10. The galvanized steel sheet according to claim 7 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ta: 0.001% or more and 0.010% or less and Sn: 0.002% or more and 0.2% or less.

11. The galvanized steel sheet according to claim 1 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ti: 0.01% or more and 0.1% or less, Nb: 0,01% or more and 0.1% or less and B: 0.0003% or more and 0.005% or less.

12. The galvanized steel sheet according to claim 11 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

13. The galvanized steel sheet according to claim 11 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ta: 0.001% or more and 0.010% or less and Sn: 0.002% or more and 0.2% or less.

14. The galvanized steel sheet according to claim 1 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

15. The galvanized steel sheet according to claim 14 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ta: 0.001% or more and 0.010% or less and Sn: 0.002% or more and 0.2% or less.

16. The galvanized steel sheet according to claim 1 , wherein the chemical composition further comprises one or more chemical elements selected from the group consisting of, by mass %, Ta: 0.001% or more and 0.010% or less and Sn: 0.002% or more and 0.2% or less.

17. The galvanized steel sheet according to claim 1 , wherein the chemical composition further comprises, by mass %, Sb: 0.002% or more and 0.2% or less.

18. A method for manufacturing the galvanized steel Sheet according to claim 1 , consisting of:
hot-rolling a steel slab comprising the chemical composition with a finishing delivery temperature of 850° C. or higher,
coiling the resulting hot-rolled steel sheet at a temperature of 450° C. or higher and 600° C. or lower,
pickling the steel sheet,
annealing the steel sheet by holding the steel sheet at a temperature of 600° C. or higher and 750° C. or lower for a holding time of 50 seconds or more and 550 seconds or less,
cooling the steel sheet,
galvanizing the steel sheet, and
performing alloyina on the steel sheet at a temperature of 470° C. or higher and 600° C. or lower after galvanizing has been performed.

Assignees

• Kawasaki Yoshiyasu
• Nakagaito Tatsuya
• Kaneko Shinjiro
• Nagataki Yasunobu
• Fukushi Keisuke
• Jfe Steel Corp

Inventors

• Kawasaki Yoshiyasu
• Nakagaito Tatsuya
• Kaneko Shinjiro
• Nagataki Yasunobu
• Fukushi Keisuke

Classifications

• C21D6/005 Primary

  containing Mn · CPC title

• C21D9/46

  for sheet metals · CPC title

• C21D2211/005

  Ferrite · CPC title

• B05D3/0218

  Pretreatment, e.g. heating the substrate · CPC title

• B05D3/12

  by mechanical means · CPC title