Li—Ni composite oxide particles and process for producing the same, and non-aqueous electrolyte secondary battery

Patent metadata

Field	Value
Publication number	US-9764962-B2
Application number	US-201214111590-A
Country	US
Kind code	B2
Filing date	Apr 12, 2012
Priority date	Apr 14, 2011
Publication date	Sep 19, 2017
Grant date	Sep 19, 2017

Abstract

The present invention provides lithium composite compound particles having good high-temperature storage property and excellent cycle characteristics as an active substance for a non-aqueous electrolyte secondary battery, and a secondary battery using the lithium composite compound particles. The Li—Ni composite oxide particles for a non-aqueous electrolyte secondary battery according to the present invention have a BET specific surface area of 0.05 to 0.8 m 2 /g; an atomic ratio (Ma/Ni) of a concentration of an amphoteric metal to a concentration of Ni on an outermost surface of the respective Li—Ni composite oxide particles is 2 to 6; and the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is higher than a concentration of the amphoteric metal at a position spaced by 50 nm from the outermost surface toward a center of the respective Li—Ni composite oxide particles.

First claim

The invention claimed is:

1. A process for producing Li—Ni composite oxide particles having a composition represented by the formula:
Li x (Ni 1-y-w-z-v Co y Mn w Ma z Mb v )O 2
wherein 0.9≦x≦1.1; 0.05≦y≦0.25; 0≦w≦0.25; 0<z≦0.15; 0≦v≦0.03; Ma is at least one amphoteric metal selected from the group consisting of Al, Zn and Sn; and Mb is at least one metal selected from the group consisting of Bi, Sb, Zr, B and Mg,
wherein the Li—Ni composite oxide particles have a BET specific surface area of 0.05 to 0.8 m 2 /g; an atomic ratio (Ma/Ni) of a concentration of the amphoteric metal to a concentration of Ni on an outermost surface of the respective Li—Ni composite oxide particles is 2 to 6; and the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is higher than a concentration of the amphoteric metal at a position spaced by 50 nm from the outermost surface toward a center of the respective Li—Ni composite oxide particles, and
wherein the Li—Ni composite oxide particles have a content of lithium hydroxide of not more than 0.25% by weight, and a content of lithium carbonate of not more than 0.20% by weight,
the process comprising:
a water-washing step of adjusting a pH value of a slurry prepared by dispersing Li—Ni composite oxide particles in water to 5.0 to 11.0 while stirring; and
a heat-treating step of annealing the Li—Ni composite oxide particles obtained by successively subjecting the particles obtained after the water-washing step to filtration, rinsing and drying, in a temperature range of 450 to 850° C. in an oxygen-containing atmosphere having a carbon dioxide gas concentration of not more than 100 ppm such that after the heat treating step the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is higher than the concentration of the amphoteric metal at the position spaced by 50 nm from the outermost surface toward the center of the respective Li—Ni composite oxide particles.

2. The process for producing Li—Ni composite oxide particles according to claim 1 , wherein the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is 5 to 60 atom % based on a total concentration of Ni, Co, Mn, the amphoteric metal (Ma), Mb and oxygen.

3. The process for producing Li—Ni composite oxide particles according to claim 1 , wherein the Li—Ni composite oxide particles have an average secondary particle diameter of 1 to 30 μm.

4. The process for producing Li—Ni composite oxide particles according to claim 1 , wherein the Li—Ni composite oxide particles have a sulfur content of not more than 100 ppm, and a sodium content of not more than 100 ppm.

5. A process for producing Li—Ni composite oxide particles having a composition represented by the formula:
Li x (Ni 1-y-w-z-v Co y Mn w Ma z Mb v )O 2
wherein 0.9≦x≦1.1; 0.05≦y≦0.25; 0≦w≦0.25; 0<z≦0.15; 0≦v≦0.03; Ma is at least one amphoteric metal selected from the group consisting of Al, Zn and Sn; and Mb is at least one metal selected from the group consisting of Bi, Sb, Zr, B and Mg,
wherein the Li—Ni composite oxide particles have a BET specific surface area of 0.05 to 0.8 m 2 /g; an atomic ratio (Ma/Ni) of a concentration of the amphoteric metal to a concentration of Ni on an outermost surface of the respective Li—Ni composite oxide particles is 2 to 6; and the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is higher than a concentration of the amphoteric metal at a position spaced by 50 nm from the outermost surface toward a center of the respective Li—Ni composite oxide particles, and
wherein there is a concentration gradient region such that the concentration of the amphoteric metal is gradually decreased into an inner side of particles from the outermost surface having a maximum concentration of the amphoteric metal,
the process comprising:
a water-washing step of adjusting a pH value of a slurry prepared by dispersing Li—Ni composite oxide particles in water to 5.0 to 11.0 while stirring; and
a heat-treating step of annealing the Li—Ni composite oxide particles obtained by successively subjecting the particles obtained after the water-washing step to filtration, rinsing and drying, in a temperature range of 450 to 850° C. in an oxygen-containing atmosphere having a carbon dioxide gas concentration of not more than 100 ppm such that after the heat treating step the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is higher than the concentration of the amphoteric metal at the position spaced by 50 nm from the outermost surface toward the center of the respective Li—Ni composite oxide particles.

6. The process for producing Li—Ni composite oxide particles according to claim 5 , wherein the concentration of the amphoteric metal on the outermost surface of the respective Li—Ni composite oxide particles is 5 to 60 atom % based on a total concentration of Ni, Co, Mn, the amphoteric metal (Ma), Mb and oxygen.

7. The process for producing Li—Ni composite oxide particles according to claim 5 , wherein the Li—Ni composite oxide particles have an average secondary particle diameter of 1 to 30 μm.

8. The process for producing Li—Ni composite oxide particles according to claim 5 , wherein the Li—Ni composite oxide particles have a sulfur content of not more than 100 ppm, and a sodium content of not more than 100 ppm.

Assignees

• Imahashi Taiki
• Watanabe Hiroyasu
• Kikuya Kazuhiko
• Sadamura Hideaki
• Toda Kogyo Corp

Inventors

• Imahashi Taiki
• Watanabe Hiroyasu
• Kikuya Kazuhiko
• Sadamura Hideaki

Classifications

• H01M4/525

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/505 Primary

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• C01P2006/80

  Compositional purity · CPC title

• C01P2006/12

  Surface area · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title