Hot-rolled steel sheet for high-strength galvanized steel sheet or high-strength galvannealed steel sheet and method for manufacturing the same (as amended)

Patent metadata

Field	Value
Publication number	US-9758847-B2
Application number	US-201214354810-A
Country	US
Kind code	B2
Filing date	Nov 2, 2012
Priority date	Nov 17, 2011
Publication date	Sep 12, 2017
Grant date	Sep 12, 2017

Abstract

Provided is a hot-rolled steel sheet having a composition containing 0.04 mass percent to 0.20 mass percent C, 0.7 mass percent to 2.3 mass percent Si, 0.8 mass percent to 2.8 mass percent Mn, 0.1 mass percent or less P, 0.01 mass percent or less S, 0.1 mass percent or less Al, and 0.008 mass percent or less N, the remainder being Fe and inevitable impurities. Internal oxides containing one or more selected from the group consisting of Si, Mn, and Fe are present at grain boundaries and in grains in a base metal. The internal oxides present at the grain boundaries in the base metal are located within 5 μm from the surface of the base metal. The difference between the depths at which the internal oxides are formed in the cross direction of the steel sheet is 2 μm or less.

First claim

The invention claimed is:

1. A hot-rolled steel sheet for a high-strength galvanized steel sheet or a high-strength galvannealed steel sheet, having a composition containing 0.04 mass percent to 0.20 mass percent C, 0.7 mass percent to 2.3 mass percent Si, 0.8 mass percent to 2.8 mass percent Mn, 0.1 mass percent or less P, 0.01 mass percent or less S, 0.1 mass percent or less Al, and 0.008 mass percent or less N, the remainder being Fe and inevitable impurities, wherein internal oxides containing one or more selected from the group consisting of Si, Mn, and Fe are present at grain boundaries and in grains in a base metal, the internal oxides present at the grain boundaries in the base metal are located at a depth of 2.4 μm or more and 5 μm or less from the surface of the base metal, and the difference between the depths at which the internal oxides are formed across an entirety of the steel sheet in a direction perpendicular to a thickness direction and perpendicular to a rolling direction of the steel sheet is 2 μm or less.

2. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 1 , wherein the mass ratio (Si/Mn) of Si to Mn in the composition is less than 1.

3. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 2 , wherein the composition further contains one or more selected from the group consisting of 0.05 mass percent to 1.0 mass percent Cr, 0.005 mass percent to 0.5 mass percent V, 0.005 mass percent to 0.5 mass percent Mo, 0.05 mass percent to 1.0 mass percent Ni, and 0.05 mass percent to 1.0 mass percent Cu.

4. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 3 , wherein the composition further contains one or more selected from the group consisting of 0.01 mass percent to 0.1 mass percent Ti, 0.01 mass percent to 0.1 mass percent Nb, and 0.0003 mass percent to 0.0050 mass percent B.

5. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 4 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

6. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 3 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

7. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 2 , wherein the composition further contains one or more selected from the group consisting of 0.01 mass percent to 0.1 mass percent Ti, 0.01 mass percent to 0.1 mass percent Nb, and 0.0003 mass percent to 0.0050 mass percent B.

8. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 7 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

9. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 2 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

10. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 1 , wherein the composition further contains one or more selected from the group consisting of 0.05 mass percent to 1.0 mass percent Cr, 0.005 mass percent to 0.5 mass percent V, 0.005 mass percent to 0.5 mass percent Mo, 0.05 mass percent to 1.0 mass percent Ni, and 0.05 mass percent to 1.0 mass percent Cu.

11. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 10 , wherein the composition further contains one or more selected from the group consisting of 0.01 mass percent to 0.1 mass percent Ti, 0.01 mass percent to 0.1 mass percent Nb, and 0.0003 mass percent to 0.0050 mass percent B.

12. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 11 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

13. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 10 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

14. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 1 , wherein the composition further contains one or more selected from the group consisting of 0.01 mass percent to 0.1 mass percent Ti, 0.01 mass percent to 0.1 mass percent Nb, and 0.0003 mass percent to 0.0050 mass percent B.

15. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 14 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

16. The hot-rolled steel sheet for the high-strength galvanized steel sheet or the high-strength galvannealed steel sheet according to claim 1 , wherein the composition further contains one or more selected from 0.001 mass percent to 0.005 mass percent Ca and 0.001 mass percent to 0.005 mass percent of a REM.

Assignees

• Jfe Steel Corp

Inventors

• Miyata Mai
• Suzuki Yoshitsugu
• Nagataki Yasunobu
• Kawasaki Yoshiyasu
• Sugihara Hirokazu

Classifications

• C22C38/18 Primary

  containing chromium · CPC title

• C22C38/002

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• C23C2/28

  Thermal after-treatment, e.g. treatment in oil bath · CPC title

• C21D8/0236

  Cold rolling · CPC title

• B21B3/02

  Rolling special iron alloys {, e.g. stainless steel} · CPC title