Method for low temperature bonding of elastomers

Patent metadata

Field	Value
Publication number	US-9757898-B2
Application number	US-201514829244-A
Country	US
Kind code	B2
Filing date	Aug 18, 2015
Priority date	Aug 18, 2014
Publication date	Sep 12, 2017
Grant date	Sep 12, 2017

Abstract

A method of bonding a vulcanized elastomer is provided comprising the steps of; providing an adhesive comprising a primary acrylate monomer, a reactive flexibilizing monomer, and further optionally comprising a toughener, an adhesion promoter and a free radical initiator, then depositing the adhesive on at least one surface of an elastomer or a second substrate, wherein the elastomer is a vulcanized elastomer, then bringing the elastomer substrate and second substrate together with the adhesive disposed therebetween, and allowing the adhesive to cure and bond the elastomer and second substrate together at a temperature of less than about 100° C. to produce a bonded structure.

First claim

The invention claimed is:

1. A method of bonding a vulcanized elastomer comprising the steps of:
a) providing an adhesive comprising two parts, wherein the first part comprises:
30 to 60 weight percent primary acrylate monomer comprising at least one of methyl methacrylate or tetrahydrofurfuryl methacrylate,
5 to 15 weight percent reactive flexibilizing monomer comprising at least one of 2-ethylhexyl methacrylate, hexyl methacrylate, or octyl methacrylate,
5 to 15 weight percent of a substrate dependent reactive monomer comprising iso-butyl methacrylate,
10 to 30 weight percent of a toughener,
0.5 to 5 weight percent of a reducing agent,
and the second part comprises:
30 to 60 weight percent of an epoxy resin, and
20 to 40 weight percent of an organic peroxide;
b) depositing the adhesive on at least one surface of an elastomer or a second substrate, wherein the elastomer is a vulcanized elastomer;
c) bringing the elastomer and second substrate together with the adhesive disposed therebetween; and,
d) allowing the adhesive to cure and bond the elastomer and second substrate together at a temperature of less than about 100° C. to produce a bonded structure.

2. The method of claim 1 , wherein step d) is performed at a temperature of less than about 50° C.

3. The method of claim 1 , wherein the second substrate comprises at least one of an elastomer substrate, a thermoplastic substrate, or a metallic substrate.

4. The method of claim 1 , wherein the toughener comprises at least one of poly(styrene:butadiene:styrene), poly(styrene:acrylonitrile:butadiene), or styrene:isoprene:styrene.

5. The method of claim 1 , wherein the adhesive is free of halogenated compounds, isocyanate compounds, or solvents.

6. The method of claim 1 , wherein the 2-part adhesive is mixed immediately prior to the step of depositing the adhesive.

7. The method of claim 1 , wherein there is no elastomer chlorination step.

8. The method of claim 1 , wherein there is no metal degreasing step.

9. The method of claim 1 , where the adhesive comprises the sole chemical composition applied to either the elastomer or second substrate prior to bonding, and the elastomer and second substrate are absent any metal primer, tack coating, or elastomer pre-treatment.

10. The method of claim 1 , wherein the cured adhesive has an adhesion as measured by pull value of greater than 25pli as measured by ASTM D429 Method D at a peel rate of 2.0in/min.

11. The method of claim 1 , wherein the adhesive is deposited by providing the first part on one of the elastomer or second substrate and providing the second part on the other of the elastomer or second substrate, and wherein when the elastomer and second substrate are brought together an initiator cures the acrylate monomer.

Assignees

• Lord Corp

Inventors

• Huang Jian-Piang
• Troughton Jr Ernest B
• Bate Norah

Classifications

• B32B7/12

  using interposed adhesives or interposed materials with bonding properties · CPC title

• B29C65/485

  Multi-component adhesives, i.e. chemically curing as a result of the mixing of said multi-components · CPC title

• B29C66/71

  characterised by the composition of the plastics material of the parts to be joined (welding bar compositions B29C65/125) · CPC title

• B32B2439/40

  Closed containers · CPC title

• B29L2031/712

  Containers; Packaging elements or accessories, Packages (closures therefor B29L2031/56; ink or toner cartridges B29L2031/7678; squeeze tubes B29L2023/20; suitcases B29L2031/7418) · CPC title