Process for producing composite profiles

Patent metadata

Field	Value
Publication number	US-9757885-B2
Application number	US-201314034775-A
Country	US
Kind code	B2
Filing date	Sep 24, 2013
Priority date	Sep 28, 2012
Publication date	Sep 12, 2017
Grant date	Sep 12, 2017

Abstract

The present invention relates to a process for producing composite profiles comprising at least two metal shells which are joined by struts comprising a thermoplastic material and a core comprising rigid polyurethane foam, which comprises introduction of the starting components of the rigid polyurethane foam into a hollow space formed by the metal shells, with the rigid polyurethane foam being formed, and subsequent application of a surface coating to the outer surface of the composite profile by means of a powder coating or baking enamel, where the rigid polyurethane foam is obtained by reaction of the following components:
A) at least one polyisocyanate, B) at least one polyfunctional compound which is reactive toward isocyanates, C) one or more blowing agents comprising at least formic acid, D) optionally one or more flame retardants, E) optionally one or more catalysts and F) optionally further auxiliaries or additives,

wherein the starting components of the rigid polyurethane foam do not comprise any inorganic fillers.

First claim

The invention claimed is:

1. A process for producing a composite profile, comprising:
introducing starting components of rigid polyurethane foam into a hollow space formed by at least two metal shells to obtain the rigid polyurethane foam, and
subsequently applying a surface coating to an outer surface of the composite profile by powder coating or baking enamel,
wherein:
the composite profile comprises the at least two metal shells joined by struts,
the struts comprise a thermoplastic material and a core comprising the rigid polyurethane foam, and
the starting components of the rigid polyurethane foam comprise:
A) a polyisocyanate,
B) a polyfunctional compound which is reactive toward isocyanates,
C) a blowing agent comprising at least formic acid,
D) optionally a flame retardant,
E) optionally a catalyst,
F) optionally further auxiliaries or additives, and
no inorganic fillers.

2. The process according to claim 1 , wherein component C) is an aqueous solution of formic acid.

3. The process according to claim 2 , wherein component C) is a solution of from 70 to 95% by weight of formic acid in water.

4. The process according to claim 1 , wherein an amount of formic acid based on a total weight of components B) to F) is from 2 to 6% by weight.

5. The process according to claim 1 , wherein component B) comprises exclusively compounds which are obtained by alkoxylation of a starter by exclusively propylene oxide.

6. The process according to claim 1 , wherein component B) comprises a polyether polyol having a hydroxyl number of from 200 to 400 mg KOH/g and a functionality of from 2 to 3.

7. The process according to claim 1 , wherein component B) comprises a polyether polyol having a hydroxyl number of from 300 to 600 mg KOH/g and a functionality of from 4 to 8.

8. The process according to claim 1 , wherein a weight average functionality of component B) is from 2.4 to 5.

9. The process according to claim 1 , wherein the surface coating is applied at a temperature of from 100 to 250° C.

10. The process according to claim 1 , wherein the starting components of the rigid polyurethane foam comprise:
A) a polyisocyanate,
B) a polyfunctional compound which is reactive toward isocyanates,
C) a blowing agent comprising at least formic acid,
D) a flame retardant,
E) a catalyst,
F) optionally further auxiliaries or additives, and
no inorganic fillers.

Assignees

• Basf Se

Inventors

• Koesters Michael
• Tomasi Gianpaolo
• Schoen Lars
• Windeler Ludwig

Classifications

• E06B1/325

  comprising insulation between two metal section members · CPC title

• E06B3/267

  with insulating elements formed in situ · CPC title

• E06B3/26303

  with thin strips, e.g. defining a hollow space between the metal section members · CPC title

• B29C44/1276 Primary

  the preformed parts being three dimensional structures which are wholly or partially penetrated by the foam · CPC title

• Y10T428/233

  Foamed or expanded material encased · CPC title